The Dynamic Interaction of Surfactants with Colloidal Molybdenum Disulfide Nanosheets Calls for Thermodynamic Stabilization by Solvents

Top-down liquid-phase exfoliation (LPE) and bottom-up hot-injection synthesis are scalable methods to produce colloids of two-dimensional (2D) van der Waals (vdW) solids. Generally thought off as two entirely different fields, we show that similar stabilization mechanisms apply to colloids of molybdenum disulfide (MoS 2 ) produced by both methods. By screening the colloidal stability of MoS 2 produced in a hot-injection synthesis in a wide range of solvents, we observe that colloidal stability can be understood based on solution thermodynamics, wherein matching the solubility parameter of solvent and nanomaterial maximizes colloidal stability. Identical to MoS 2 produced through LPE, optimal solvents to disperse MoS 2 produced from the bottom-up have similar solubility parameters of ≈22 MPa 1/2 and include aromatic solvents with polar functionalities, such as o -dichlorobenzene, and polar aprotic solvents, such as N, N -dimethylformamide. We further complemented our findings by nuclear magnetic resonance (NMR) spectrscopy, highlighting that organic surfactants, such as oleylamine and oleic acid, have a minimal affinity toward the nanocrystal surface and engage in a highly dynamic adsorption/desorption equilibrium. We thus conclude that hot injection yields MoS 2 colloids with comparable surfaces as those produced by LPE. These similarities might offer the prospect of using established procedures developed for LPE nanomaterials to postprocess colloidally synthesized dispersions of 2D colloids as processable inks.