Formation of n-Hexane-in-DMF Nonaqueous Pickering Emulsions: ABC Triblock Worms versus AB Diblock Worms

Nonaqueous Pickering emulsions exhibit promising applications in many industrial areas but have been relatively less studied in the past. In this study, n-hexane-in-DMF nonaqueous Pickering emulsions stabilized by core cross-linked copolymer worms with mixed shells are demonstrated for the first time. Core cross-linked copolymer worms with mixed shells were prepared by seeded reversible addition–fragmentation chain transfer (RAFT) quasi-solution polymerization. Specifically, polystyrene-poly(4-vinylpyridine) (PS-P4VP) diblock copolymer worms were first prepared via RAFT-mediated dispersion polymerization in toluene under the given conditions using PS as both the macro-CTA and the stabilizer block. After the chemical cross-linking of P4VP cores, PS-P4VP diblock copolymer worms were chain-extended with LMA in DMF/toluene (1:9, weight ratio) mixed solvents, producing core cross-linked PS-P4VP-PLMA worms with PS/PLMA mixed shells. The as-prepared core cross-linked PS-P4VP-PLMA worms with mixed PS/PLMA shells were further utilized as Pickering emulsifiers for the generation of nonaqueous n-hexane-in-DMF Pickering emulsions. The emulsifying performances of mixed-shell copolymer worms were compared with those of their spherical and linear analogues with entirely identical chemical compositions as well as PS-P4VP diblock copolymer worm precursors, respectively.