Synthesis of New Thermoresponsive Polymers Possessing the Dense 1,2,3-Triazole Backbone

Thermoresponsive water-soluble polymers, aqueous solutions of which undergo lower critical solution temperature (LCST)-type phase separation, have been investigated in detail for several decades. To develop LCST-type thermoresponsive polymers with new polymer backbone, 4-azido-5-hexynamide (AHA) derivatives were designed as monomers for copper(I)-catalyzed azide–alkyne cycloaddition (CuAAC) polymerization. AHA derivatives carrying secondary amide side chains, that is, 4-azido-N-methyl-5-hexynamide (M), 4-azido-N-ethyl-5-hexynamide (E), and 4-azido-N-isopropyl-5-hexynamide (iP), were first synthesized and polymerized by CuAAC to obtain polymers (poly(M), poly(E), and poly(iP)). Contrary to our expectation, poly(M), poly(E), and poly(iP) were insoluble in water and many organic solvents presumably because of the formation of hydrogen bonding between the amide side chains or between the amide side chains and triazole residues in the backbone. Thus, AHA derivatives carrying tertiary amide side chains, that is, 4-azido-N,N-dimethyl-5-hexynamide (MM), 4-azido-N-ethyl-N-methyl-5-hexynamide (ME), 4-azido-N-isopropyl-N-methyl-5-hexynamide (MiP), and 4-azido-N,N-diethyl-5-hexynamide (EE), were also synthesized and polymerized to yield polymers (poly(MM), poly(ME), poly(MiP), and poly(EE)). These polymers were soluble in a number of common organic solvents. It is noteworthy that poly(MM) and poly(ME) were also soluble in water. The phase separation behavior of 1.0 wt % aqueous solutions of poly(MM) and poly(ME) was then investigated by transmittance measurements. These data indicated that poly(ME) was an LCST-type thermoresponsive polymer, whereas poly(MM) was not. A large hysteresis was observed in the transmittance measurements for the poly(ME) aqueous solution because of slow rehydration after phase separation. The phase separation behavior was investigated preliminarily by differential scanning calorimetry and 1H NMR.