Rich defects near the percolation threshold of dilute solid solutions are of fundamental interest to thermoelectric research. Sn-substituted Pb 0.98 Na 0.02 Se (1 mol %) is a typical example that demonstrates how various defects induce intriguing transport phenomena. Unfortunately, the presence of Pb vacancies severely degrades the carrier mobility of samples, and the thermoelectric figure of merit ZT is only marginally improved. In this study, we show that Pb vacancies are effectively inhibited by a facile defect reconfiguration strategy. This is achieved by doping a dilute amount of Te at Se sites of Pb 0.97 Sn 0.01 Na 0.02 Se, where the interstitial Sn ions are pulled back to Pb sites as revealed by the X-ray photoelectron spectroscopy analysis and the positron annihilation test. Consequently, Pb vacancies get occupied, and the room temperature carrier mobility is remarkably recovered from 2.8 to 70 cm 2 V –1 s –1 upon 3 mol % Te doping. Moreover, Te doping reinforces phonon scattering by strain and mass field fluctuations. The lattice thermal conductivity at 300 K goes down to ∼1.7 W m –1 K –1 for Pb 0.97 Sn 0.01 Na 0.02 Se 0.94 Te 0.06, which is ∼32% lower than that of the Pb 0.97 Sn 0.01 Na 0.02 Se control sample. Altogether, the average ZT value of Pb 0.97 Sn 0.01 Na 0.02 Se between 300 and 773 K is doubled upon 6 mol % Te doping.
Source: openalex_inverted_index · Quality: baseline
Affiliations
State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan 430070, China
International School of Materials Science and Engineering, Wuhan University of Technology, Wuhan 430070, China
Hubei Nuclear Solid Physics Key Laboratory, Department of Physics, Wuhan University, Wuhan 430072, China
Funding
Ministry of Science and Technology of the People's Republic of China · Youth Innovation Promotion Association of the Chinese Academy of Sciences · National Natural Science Foundation of China