SnO2 Films Elaborated by Radio Frequency Magnetron Sputtering as Potential Transparent Conducting Oxides Alternative for Organic Solar Cells
Source abstract
Abstract
Transparent conducting oxides (TCOs) are a crucial component of solar cells. Tin-doped indium oxide (ITO) is the most employed TCO, but the scarcity and high price of indium induce a search for lower-cost TCOs with equivalent properties as substitutes. Tin dioxide (SnO2) films have many advantages, such as rich sources of material, low prices, and nontoxicity. SnO2 films present a high visible-light transmittance, near-infrared light reflectivity, and excellent electrical properties. They also have a higher chemical and mechanical stability compared to ITO. The aim of this work is to elaborate SnO2 films by radio frequency (RF)-magnetron sputtering in order to use them as electrodes for organic solar cells (OSCs). The SnO2 films were deposited on glass, SiO2, and quartz substrates in a mixed environment of Ar and O2. X-ray diffraction (XRD) measurements show that the as-deposited SnO2 films are polycrystalline with a cassiterite tetragonal structure. Scanning electron microscopy (SEM) analysis showed that the films are homogeneous, continuous, and nanostructured. The electrical resistivity and average optical transmittance of the samples are about 10–3 Ω.cm and over 80%, respectively. The estimated optical band gap (Eg) is around 4.0 eV, while the work function (WF) of the films is around 5.0 eV. The SnO2 films are used as electrodes for inverted OSCs, using poly(3-hexylthiophene-2,5-diyl): [6,6]-phenyl-C60-butryric acid methyl ester (P3HT:PC60BM) as the active layer. The device’s open-circuit voltage (VOC) and short-circuit current density (JSC) are similar to those obtained for the inverted OSCs employing ITO as the same electrode. Even if the achieved power conversion efficiency (PCE) is lower compared to the value for the reference OSC with an ITO electrode, these results are promising and place SnO2 TCO as a potential candidate to replace ITO.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: ZnO doping and properties · Gas Sensing Nanomaterials and Sensors · Transition Metal Oxide Nanomaterials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Université de Strasbourg CNRS, Institut de Physique et Chimie des Matériaux de Strasbourg, UMR 7504, 23 rue du Loess, F-67000 Strasbourg, France
Mohammed V University in Rabat, Faculty of Sciences, MANAPSE, B.P. 1014, 10000 Rabat, Morocco
ICube Laboratory (Université de Strasbourg and CNRS), UMR 7357, 23 rue du Loess, BP 20 CR, F-67037 Cedex 2 Strasbourg, France
Funding
European Commission · H2020 Marie Sk??odowska-Curie Actions
References (46)
Show source-provided references
1. 10.1016/j.solmat.2007.04.03110.1016/j.solmat.2007.04.031 ↗
2. 10.1088/0268-1242/20/4/00410.1088/0268-1242/20/4/004 ↗
3. 10.1016/j.orgel.2020.10570410.1016/j.orgel.2020.105704 ↗
4. 10.1002/adfm.20090071410.1002/adfm.200900714 ↗
5. 10.1021/cr400733510.1021/cr4007335 ↗
6. 10.1557/mrs2007.2910.1557/mrs2007.29 ↗
7. Ihokura K. · 2020
8. 10.1016/0925-4005(91)80003-310.1016/0925-4005(91)80003-3 ↗
9. 10.1016/j.progsurf.2005.09.00210.1016/j.progsurf.2005.09.002 ↗
10. 10.1016/j.tsf.2013.06.07710.1016/j.tsf.2013.06.077 ↗
11. 10.1016/j.tsf.2012.09.06210.1016/j.tsf.2012.09.062 ↗
12. 10.1016/j.jlumin.2004.12.00310.1016/j.jlumin.2004.12.003 ↗
13. 10.1016/j.surfcoat.2011.07.06810.1016/j.surfcoat.2011.07.068 ↗
14. 10.1016/j.matpr.2015.05.09010.1016/j.matpr.2015.05.090 ↗
15. 10.1016/j.snb.2016.11.05410.1016/j.snb.2016.11.054 ↗
16. 10.1016/S0038-1098(02)00009-110.1016/S0038-1098(02)00009-1 ↗
17. 10.1016/j.apsusc.2011.10.07210.1016/j.apsusc.2011.10.072 ↗
18. 10.1016/j.spmi.2015.10.04310.1016/j.spmi.2015.10.043 ↗
19. 10.1016/j.jeurceramsoc.2017.04.01410.1016/j.jeurceramsoc.2017.04.014 ↗
20. 10.1016/j.tsf.2015.04.06510.1016/j.tsf.2015.04.065 ↗
21. 10.1016/j.mssp.2020.10548310.1016/j.mssp.2020.105483 ↗
22. 10.1016/j.proeng.2013.01.06710.1016/j.proeng.2013.01.067 ↗
23. 10.1016/j.optlastec.2020.10657510.1016/j.optlastec.2020.106575 ↗
24. 10.1016/S0379-6779(01)00624-510.1016/S0379-6779(01)00624-5 ↗
25. 10.1016/j.ceramint.2005.11.01310.1016/j.ceramint.2005.11.013 ↗
26. 10.1016/j.phpro.2012.03.66410.1016/j.phpro.2012.03.664 ↗
27. 10.1016/j.matchemphys.2019.05.07210.1016/j.matchemphys.2019.05.072 ↗
28. 10.1016/S0040-6090(03)00506-610.1016/S0040-6090(03)00506-6 ↗
29. 10.1016/j.mseb.2008.10.03710.1016/j.mseb.2008.10.037 ↗
30. 10.1016/j.matpr.2020.02.77410.1016/j.matpr.2020.02.774 ↗
31. 10.1016/j.jallcom.2012.09.03510.1016/j.jallcom.2012.09.035 ↗
32. 10.1016/S1003-6326(13)62521-210.1016/S1003-6326(13)62521-2 ↗
33. 10.1007/s12540-010-0614-610.1007/s12540-010-0614-6 ↗
34. Scherrer P. · 1918
35. 10.1016/j.matchar.2013.09.00210.1016/j.matchar.2013.09.002 ↗
36. 10.1080/1478643560823807410.1080/14786435608238074 ↗
37. 10.1016/j.mseb.2004.12.02610.1016/j.mseb.2004.12.026 ↗
38. 10.1016/j.jlumin.2014.09.04410.1016/j.jlumin.2014.09.044 ↗
39. 10.1143/JJAP.27.L28710.1143/JJAP.27.L287 ↗
40. Tauc J. · 197410.1007/978-1-4615-8705-7 ↗
41. 10.1016/j.tsf.2006.07.02010.1016/j.tsf.2006.07.020 ↗
42. 10.1155/1987/4972010.1155/1987/49720 ↗
43. 10.1063/1.32324010.1063/1.323240 ↗
44. 10.1166/jnn.2016.1217310.1166/jnn.2016.12173 ↗
45. 10.1063/1.8878710.1063/1.88787 ↗
46. investigation of enhanced conductivity in dye-coated tin oxide thin films using hall voltage measurements https://www.degruyter.com/database/IBZ/entry/ibz.ID677615503/html (accessed 2021-11-09).