Graphene Oxide-Based Mesoporous Calcium Silicate Hydrate Sandwich-like Structure: Synthesis and Application for Thermal Energy Storage
Source abstract
Abstract
In this study, we designed a mesoporous composite with high latent heat capacity, stable structure, and efficient thermal response for thermal energy storage in green building constructions. Graphene oxide (GO) nanosheets were sandwiched by a vertically interconnected network of two-dimensional (2D) calcium silicate hydrate (CSH) nanoplates via an in situ dissolution–coprecipitation strategy to obtain CSH/GO/CSH (CGC). The CGC mesoporous sandwich-like structures with a high specific surface area (677 m2 g–1) and a large pore volume (∼2.5 cm3 g–1) were infiltrated with lauric acid (LA) as phase change materials (PCMs) to produce LA@CGC composites. Our results demonstrated that LA@CGC had a high latent heat value of 118.0–127.6 J g–1 and 92–99% efficiency after 50 heating–cooling cycles, which, together with the reinforcing properties of GO and the compatibility of CSH in cement-based matrixes, makes the composite a sustainable PCM for thermal energy storage in building constructions.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Phase Change Materials Research · Adsorption and Cooling Systems · Solar Thermal and Photovoltaic Systems
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Civil Engineering, Monash University, Clayton, VIC 3800, Australia
Funding
Australian Research Council
References (60)
Show source-provided references
1. 10.1016/j.enconman.2003.09.01510.1016/j.enconman.2003.09.015 ↗
2. 10.1081/GE-20005129910.1081/GE-200051299 ↗
3. 10.1016/j.enconman.2015.01.08410.1016/j.enconman.2015.01.084 ↗
4. 10.1002/htj.2193810.1002/htj.21938 ↗
5. 10.1021/acsaem.1c0126810.1021/acsaem.1c01268 ↗
6. 10.1016/j.enbuild.2017.03.06310.1016/j.enbuild.2017.03.063 ↗
7. 10.1016/j.apenergy.2020.11508810.1016/j.apenergy.2020.115088 ↗
8. 10.1021/acsaem.0c0097110.1021/acsaem.0c00971 ↗
9. 10.1021/acsaem.0c0286410.1021/acsaem.0c02864 ↗
10. 10.1016/j.solmat.2021.11114010.1016/j.solmat.2021.111140 ↗
11. 10.1016/j.carbon.2020.12.03510.1016/j.carbon.2020.12.035 ↗
12. 10.1016/j.jcis.2021.03.11110.1016/j.jcis.2021.03.111 ↗
13. 10.1021/acsaem.8b0144410.1021/acsaem.8b01444 ↗
14. 10.1016/j.rser.2016.10.01410.1016/j.rser.2016.10.014 ↗
15. 10.1016/j.apenergy.2015.09.03110.1016/j.apenergy.2015.09.031 ↗
16. 10.1016/j.solener.2016.08.01210.1016/j.solener.2016.08.012 ↗
17. 10.1016/j.applthermaleng.2015.08.04010.1016/j.applthermaleng.2015.08.040 ↗
18. 10.1016/j.conbuildmat.2020.11847910.1016/j.conbuildmat.2020.118479 ↗
19. 10.1016/j.solmat.2019.11023310.1016/j.solmat.2019.110233 ↗
20. 10.1016/j.renene.2020.11.03010.1016/j.renene.2020.11.030 ↗
21. 10.1016/j.enconman.2014.01.01610.1016/j.enconman.2014.01.016 ↗
22. 10.1016/j.solmat.2018.12.01510.1016/j.solmat.2018.12.015 ↗
23. 10.1016/j.solmat.2019.11009010.1016/j.solmat.2019.110090 ↗
24. 10.1016/j.solmat.2017.09.03410.1016/j.solmat.2017.09.034 ↗
25. 10.1016/j.solmat.2017.08.02510.1016/j.solmat.2017.08.025 ↗
26. 10.1016/j.conbuildmat.2018.06.20110.1016/j.conbuildmat.2018.06.201 ↗
27. 10.1038/s43246-021-00191-610.1038/s43246-021-00191-6 ↗
28. 10.1016/j.cemconcomp.2019.10348810.1016/j.cemconcomp.2019.103488 ↗
29. 10.1016/j.conbuildmat.2020.12101610.1016/j.conbuildmat.2020.121016 ↗
30. 10.1007/s10853-012-7128-110.1007/s10853-012-7128-1 ↗
31. 10.1016/j.diamond.2015.06.00510.1016/j.diamond.2015.06.005 ↗
32. 10.1038/srep0390910.1038/srep03909 ↗
33. 10.1002/smll.20130009710.1002/smll.201300097 ↗
34. 10.1016/j.cplett.2004.05.07110.1016/j.cplett.2004.05.071 ↗
35. 10.7763/IJAPM.2013.V3.24010.7763/IJAPM.2013.V3.240 ↗
36. 10.1016/j.conbuildmat.2013.10.00210.1016/j.conbuildmat.2013.10.002 ↗
37. 10.1016/j.cemconres.2021.10652510.1016/j.cemconres.2021.106525 ↗
38. Basquiroto de Souza F. · 2021
39. 10.1016/j.enbuild.2021.11108710.1016/j.enbuild.2021.111087 ↗
40. 10.1016/j.solmat.2012.03.01310.1016/j.solmat.2012.03.013 ↗
41. 10.1016/j.enbuild.2015.06.05910.1016/j.enbuild.2015.06.059 ↗
42. 10.1081/MB-10010780110.1081/MB-100107801 ↗
43. 10.1016/j.apenergy.2018.03.13410.1016/j.apenergy.2018.03.134 ↗
44. 10.1016/j.cej.2018.09.01310.1016/j.cej.2018.09.013 ↗
45. 10.1021/jp408478h10.1021/jp408478h ↗
46. Ma F. · J. Mater. Eng. · 2010 · 4 · 15
47. 10.1016/j.energy.2014.08.04210.1016/j.energy.2014.08.042 ↗
48. 10.1007/s11595-010-0068-110.1007/s11595-010-0068-1 ↗
49. 10.1016/j.cej.2009.09.00510.1016/j.cej.2009.09.005 ↗
50. 10.1016/j.enbuild.2016.01.02310.1016/j.enbuild.2016.01.023 ↗
51. 10.1016/j.solmat.2018.03.00510.1016/j.solmat.2018.03.005 ↗
52. 10.1016/j.cej.2019.12283110.1016/j.cej.2019.122831 ↗
53. 10.1103/PhysRevApplied.3.06401010.1103/PhysRevApplied.3.064010 ↗
54. 10.1016/j.applthermaleng.2015.01.05610.1016/j.applthermaleng.2015.01.056 ↗
55. 10.1016/j.cemconcomp.2019.02.01010.1016/j.cemconcomp.2019.02.010 ↗
56. 10.1016/j.conbuildmat.2020.12211910.1016/j.conbuildmat.2020.122119 ↗
57. 10.1016/j.ijheatmasstransfer.2021.12116510.1016/j.ijheatmasstransfer.2021.121165 ↗
58. 10.1016/j.scs.2019.10188410.1016/j.scs.2019.101884 ↗
59. 10.1016/j.cemconcomp.2017.12.00610.1016/j.cemconcomp.2017.12.006 ↗
60. 10.1016/j.jclepro.2020.12492410.1016/j.jclepro.2020.124924 ↗