All-Solid-State Li Batteries with NCM–Garnet-Based Composite Cathodes: The Impact of NCM Composition on Material Compatibility

Christoph Roitzheim, Yoo Jung Sohn, Liang-Yin Kuo, Grit Häuschen, Markus Mann, Doris Sebold, Martin Finsterbusch, Payam Kaghazchi, Olivier Guillon, Dina Fattakhova-Rohlfing

ACS Applied Energy Materials· Volume 5· Issue 6
Publisher page

Abstract

Garnet-based all-solid-state batteries (ASBs) with high energy density require composite cathodes with high areal loading and high-capacity cathode active materials. While all ceramic cathodes can typically be manufactured via cosintering, the elevated temperatures necessary for this process pose challenges with respect to material compatibility. High-capacity cathode active materials like Ni-rich LiNixCoyMn1–x–yO2 (NCM) show insufficient material compatibility toward the solid electrolyte Li6.45Al0.05La3Zr1.6Ta0.4O12 (LLZO:Ta) during cosintering, leading to the formation of highly resistive interphases. We investigated this secondary phase formation both experimentally and via density functional theory calculation to get a mechanistic understanding of the cosintering behavior of LLZO:Ta with NCM111 and Ni-rich NCM811. Furthermore, we employed B doping of both NCM materials in order to assess its impact on the cation interchange and subsequent secondary phase formation. While secondary phases were formed for all four NCM materials, their onset temperature, nature, and amount strongly depend on the NCM composition and doping. Surprisingly, Ni-rich NCM811 turned out to be the most promising cathode active material for the combination with garnet-type LLZO:Ta. As proof of concept, fully inorganic, ceramic all-solid-state lithium batteries featuring only a Li-metal anode, an LLZO:Ta separator, and a composite cathode, consisting of LLZO:Ta, Li3BO3, and NCM811, were prepared by conventional sintering. The purely inorganic full cells delivered a high specific areal discharge capacity of 0.7 mA h cm–2 in the initial cycle.
Source: openalex_inverted_index · Quality: baseline

Research context

OpenAlex topics: Advanced Battery Materials and Technologies · Advancements in Battery Materials · Electromagnetic wave absorption materials

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Institute of Energy and Climate Research−Materials Synthesis and Processing (IEK-1), Forschungszentrum Jülich GmbH, Wilhelm-Johnen-Str., Jülich 52425, Germany

Faculty of Engineering and Center for Nanointegration Duisburg-Essen (CENIDE), Universität Duisburg-Essen, Lotharstraße 1, Duisburg 47057, Germany

Department of Chemical Engineering, Ming Chi University of Technology, 84 Gungjuan Rd., Taishan Dist., New Taipei City 24301, Taiwan

Helmholtz Institute Münster: Ionics in Energy Storage (IEK-12), Corrensstr. 46, Münster 48149, Germany

Jülich-Aachen Research Alliance: JARA-Energy, Jülich 52425, Germany

Funding

Bundesministerium f?r Bildung und Forschung

References (48)

Show source-provided references
1. 10.1021/acsami.8b0670510.1021/acsami.8b06705 ↗
2. 10.1038/nenergy.2016.14110.1038/nenergy.2016.141 ↗
3. 10.1002/anie.20070114410.1002/anie.200701144 ↗
4. 10.1007/s10832-015-9988-710.1007/s10832-015-9988-7 ↗
5. 10.1039/c1cp22108f10.1039/c1cp22108f ↗
6. 10.1021/acsami.6b0083110.1021/acsami.6b00831 ↗
7. 10.1016/j.jpowsour.2017.01.00910.1016/j.jpowsour.2017.01.009 ↗
8. 10.1016/j.jmat.2016.04.00310.1016/j.jmat.2016.04.003 ↗
9. 10.1007/s10832-016-0062-x10.1007/s10832-016-0062-x ↗
10. 10.1080/10667857.2020.174653910.1080/10667857.2020.1746539 ↗
11. 10.1039/C8SE00436F10.1039/C8SE00436F ↗
12. 10.1021/acsami.6b0905910.1021/acsami.6b09059 ↗
13. 10.1021/acs.chemmater.5b0102310.1021/acs.chemmater.5b01023 ↗
14. 10.1021/acsaem.8b0103510.1021/acsaem.8b01035 ↗
15. 10.1002/aenm.20200268910.1002/aenm.202002689 ↗
16. 10.1016/j.jpowsour.2020.22890510.1016/j.jpowsour.2020.228905 ↗
17. 10.1016/j.jpowsour.2018.02.08010.1016/j.jpowsour.2018.02.080 ↗
18. 10.1016/j.jpowsour.2013.01.06310.1016/j.jpowsour.2013.01.063 ↗
19. 10.1016/j.jpowsour.2013.02.07310.1016/j.jpowsour.2013.02.073 ↗
20. 10.1016/j.jpowsour.2014.04.06510.1016/j.jpowsour.2014.04.065 ↗
21. 10.1016/j.elecom.2013.04.00410.1016/j.elecom.2013.04.004 ↗
22. 10.1016/j.ssi.2015.06.01510.1016/j.ssi.2015.06.015 ↗
23. 10.1021/acsami.8b1788110.1021/acsami.8b17881 ↗
24. 10.1021/acsenergylett.7b0061310.1021/acsenergylett.7b00613 ↗
25. 10.1016/j.jpowsour.2019.22724210.1016/j.jpowsour.2019.227242 ↗
26. 10.1002/adfm.20201009510.1002/adfm.202010095 ↗
27. 10.1021/acsaem.1c0300010.1021/acsaem.1c03000 ↗
28. Park K.-J. · Adv. Energy Mater. · 2018 · 8 · 180120210.1002/aenm.201801202 ↗
29. 10.1016/j.jpowsour.2016.07.06410.1016/j.jpowsour.2016.07.064 ↗
30. 10.1038/s41598-019-54115-z10.1038/s41598-019-54115-z ↗
31. 10.1149/2.1011605jes10.1149/2.1011605jes ↗
32. 10.1007/s11581-021-04300-w10.1007/s11581-021-04300-w ↗
33. 10.3390/ma1422680910.3390/ma14226809 ↗
34. Shizuka, K.; Okahara, K., Layered lithium nickel manganese cobalt composite oxide powder for material of positive electrode of lithium secondary battery, process for producing the same, positive electrode of lithium secondary battery therefrom, and lithium secondary battery. US 8,354,191 B2, In Google Patents: 2013.
35. 10.1017/S088571561400084010.1017/S0885715614000840 ↗
36. Bruker · 2008
37. 10.1103/PhysRevB.50.1795310.1103/PhysRevB.50.17953 ↗
38. 10.1103/PhysRevB.54.1116910.1103/PhysRevB.54.11169 ↗
39. 10.1103/PhysRevLett.77.386510.1103/PhysRevLett.77.3865 ↗
40. 10.1021/acssuschemeng.0c0767510.1021/acssuschemeng.0c07675 ↗
41. 10.1016/j.mtla.2020.10060710.1016/j.mtla.2020.100607 ↗
42. 10.1016/j.jpowsour.2014.11.06210.1016/j.jpowsour.2014.11.062 ↗
43. 10.1039/c3ta11996c10.1039/c3ta11996c ↗
44. 10.1149/2.0011912jes10.1149/2.0011912jes ↗
45. 10.1016/j.ssi.2013.09.02710.1016/j.ssi.2013.09.027 ↗
46. 10.1039/D0TA10215F10.1039/D0TA10215F ↗
47. 10.1107/S056773947600155110.1107/S0567739476001551 ↗
48. 10.1016/j.joule.2018.02.00710.1016/j.joule.2018.02.007 ↗