Structure Regulated P(VDF-TrFE)/PVDF-HFP/ZnO Ternary Films for Flexible Piezoelectric and Thermal Dual Mode Sensing

By blending P(VDF-TrFE) with PVDF-HFP and introducing a small amount of ZnO, a composite film system with both mechanical flexibility and electrical responsiveness was constructed. The effects of the TrFE/HFP ratio and hot rolling temperature on the mechanical behavior and strain-induced electrical response of the films were systematically studied. The results show that the introduction of HFP improves film ductility, while a higher TrFE content enhances load bearing capability and electrical response. Among the investigated compositions, the TrFE80/HFP20 composite containing 1.08 wt % surface-modified ZnO showed a good balance between electrical response and mechanical compliance. After hot rolling, the films processed at 65 °C showed stable mechanical behavior at low to moderate strain and produced clear open circuit voltage signals under stretching. Clear electrical signals were also observed under thermal perturbation. Based on these results, the selected composite film was used to fabricate flexible strain sensors, demonstrating promising potential for practical applications.