Mechanical and antibacterial behavior of multilayered geopolymer coatings on Ti6Al4V alloys
Source abstract
Abstract
Abstract Geopolymers are commonly used in a wide range of applications including binders into the building industry, production of refractory elements, filtration systems, low CO2 emission applications, etc. Their production can be performed either by acidic or alkaline formulation. In the last 15 years, however, they have been proposed also in biomedical applications for bone tissue regeneration. The aim of this work is the preparation of a thin and homogeneous geopolymer coating on a Ti6Al4V alloy in order to test their futuristic application as coating of prosthetic devices made with this metal alloy. Multilayered coatings were therefore produced by mean of dip coating with the aim of verifying which formulation, acidic or alkaline maximize adhesion. The morphological and chemical characteristics of the coatings were analyzed and adhesion of geopolymers to the substrate was investigated by scratch tests. Finally, a bacterial growth test was performed to verify antibacterial properties of the coatings. Graphical abstract
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Bone Tissue Engineering Materials · Orthopaedic implants and arthroplasty · Concrete and Cement Materials Research
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (33)
Show source-provided references
1. Lazorenko G, Kasprzhitskii A, Mischinenko V, Kruglikov A (2021) Fabrication and characterization of metakaolin-based geopolymer composites reinforced with cellulose nanofibrils. Mater Lett 308:13114610.1016/j.matlet.2021.131146 ↗
2. Shehata N, Sayed ET, Abdelkareem MA (2021) Recent progress in environmentally friendly geopolymers: a review. Sci Total Environ 762:14316610.1016/j.scitotenv.2020.143166 ↗
3. Jiang C, Wang A, Bao X, Ni T, Ling J (2020) A review on geopolymer in potential coating application: materials, preparation and basic properties. J Build Eng 32:10173410.1016/j.jobe.2020.101734 ↗
4. Celerier H, Jouin J, Mathivet V, Tessier-Doyen N, Rossignol S (2018) Composition and properties of phosphoric acid-based geopolymers. J Non-Cryst Solids 493:94–9810.1016/j.jnoncrysol.2018.04.044 ↗
5. Davidovits J (2011) Geopolymer chemistry and application, 3rd edn. Institute Geopolymer, Saint-Quentin
6. Wang Y-S, Alrefaei Y, Dai J-G (2019) Silico-aluminophosphate and alkali-aluminosilicate geopolymers: a comparative review. Front Mater 6:10610.3389/fmats.2019.00106 ↗
7. Al Bakria AM, Kamarudin H, BinHussain M, Nizar IK, Zarina Y, Rafiza A (2011) The effect of curing temperature on physical and chemical properties of geopolymers. Phys Procedia 22:286–29110.1016/j.phpro.2011.11.045 ↗
8. Mo B, Zhu H, Cui X, He Y, Gong S (2014) Effect of curing temperature on geopolymerization of metakaolin-based geopolymers. Appl Clay Sci 99:144–14810.1016/j.clay.2014.06.024 ↗
9. Zhang S, Gong K, Lu J (2004) Novel modification method for inorganic geopolymer by using water soluble organic polymers. Mater Lett 58:1292–129610.1016/j.matlet.2003.07.051 ↗
10. Salwa M, Al Bakri A, Kamarudin H, Ruzaidi C, Binhussain M, Zaliha S (2013) Review on current geopolymer as a coating material. Aust J Basic Appl Sci 7:246–257
11. Janaki P, Selvaraj R (2017) Experimental study on mechanical properties of geopolymer coatings for corrosion protection of steel. Adv Nat Appl Sci 11:13–20
12. Ma Y, Ye G (2015) The shrinkage of alkali activated fly ash. Cem Concr Res 68:75–8210.1016/j.cemconres.2014.10.024 ↗
13. Ma Y, Hu J, Ye G (2012) The effect of activating solution on the mechanical strength, reaction rate, mineralogy, and microstructure of alkali-activated fly ash. J Mater Sci 47:4568–4578. https://doi.org/10.1007/s10853-012-6316-310.1007/s10853-012-6316-3 ↗
14. Davidovits J et al (1994) Geopolymers: man-made rock geosynthesis and the resulting development of very early high strength cement. J Mater Educ 16:91–91
15. Delucchi M, Barbucci A, Cerisola G (1997) Study of the physico-chemical properties oforganic coatings for concrete degradation control. Constr Build Mater 11:365–37110.1016/S0950-0618(97)00060-3 ↗
16. Hansson C, Mammoliti L, Hope B (1998) Corrosion inhibitors in concrete-part i: the principles. Cem Concr Res 28:1775–178110.1016/S0008-8846(98)00142-2 ↗
17. Sayed M, Gado R, Naga S, Colombo P, Elsayed H (2020) Influence of the thermal treatment on the characteristics of porous geopolymers as potential biomaterials. Mater Sci Eng C 116:11117110.1016/j.msec.2020.111171 ↗
18. Catauro M, Bollino F, Lancellotti I, Kamseu E, Leonelli C (2010) Chemical and biological characterization of geopolymers for potential application as hard tissue prostheses. In: Advances in science and technology, vol 69. Trans Tech Publ, pp 192–19710.4028/www.scientific.net/AST.69.192 ↗
19. Oudadesse H, Derrien AC, Lefloch M, Davidovits J (2007) MAS-NMR studies of geopolymers heat-treated for applications in biomaterials field. J Mater Sci 42:3092–3098. https://doi.org/10.1007/s10853-006-0524-710.1007/s10853-006-0524-7 ↗
20. Dal Poggetto G, D’Angelo A, Blanco I, Piccolella S, Leonelli C, Catauro M (2021) FT-IR study, thermal analysis, and evaluation of the antibacterial activity of a MK-geopolymer mortar using glass waste as fine aggregate. Polymers 13:297010.3390/polym13172970 ↗
21. Vuong C, Otto M (2002) Staphylococcus epidermidis infections. Microbes Infect 4:481–48910.1016/S1286-4579(02)01563-0 ↗
22. Furlani E, Rondinella A, Aneggi E, Maschio S (2021) Possible recycling of end-of-life dolomite refractories by the production of geopolymer-based composites: experimental investigation. J Sustain Metall 7(3):908–91910.1007/s40831-021-00383-x ↗
23. Furlani E, Aneggi E, Rondinella A, Zanocco M, Fedrizzi L, Maschio S (2021) The effect of the P/Si ratio on the preparation and properties of phosphoric acid-metakaolin geopolymers. J Ceram Sci Technol 12(1):19–28
24. Duxson P, Provis JL, Lukey GC, Mallicoat SW, Kriven WM, Van Deventer JS (2005) Understanding the relationship between geopolymer composition, microstructure and mechanical properties. Colloids Surf A 269(1–3):47–5810.1016/j.colsurfa.2005.06.060 ↗
25. A. S. for Testing M (2010) ASTM, Standard test method for adhesion strength and mechanical failure modes of ceramic coatings by quantitative single point scratch testing (ASTM c1624/22). American Society for Testing and Materials
26. Kuenzel C, Vandeperre LJ, Donatello S, Boccaccini AR, Cheeseman C (2012) Ambient temperature drying shrinkage and cracking in metakaolin-based geopolymers. J Am Ceram Soc 95:3270–327710.1111/j.1551-2916.2012.05380.x ↗
27. Zuhua Z, Xiao Y, Huajun Z, Yue C (2009) Role of water in the synthesis of calcined kaolin-based geopolymer. Appl Clay Sci 43:218–22310.1016/j.clay.2008.09.003 ↗
28. Fu S, He P, Wang M, Cui J, Wang M, Duan X, Yang Z, Jia D, Zhou Y (2020) Hydrothermal synthesis of pollucite from metakaolin-based geopolymer for hazardous wastes storage. J Clean Prod 248:11924010.1016/j.jclepro.2019.119240 ↗
29. Ducloué L, Pitois O, Tocquer L, Goyon J, Ovarlez G (2017) Yielding and flow of foamed metakaolin pastes. Colloids Surf A Phys Chem Eng Asp 513:87–9410.1016/j.colsurfa.2016.11.015 ↗
30. Temuujin J, Rickard W, Lee M, van Riessen A (2011) Preparation and thermal properties of fire resistant metakaolin-based geopolymer-type coatings. J Non-Cryst Solids 357(5):1399–140410.1016/j.jnoncrysol.2010.09.063 ↗
31. Zanocco M, Boschetto F, Zhu W, Marin E, McEntire BJ, Bal BS, Adachi T, Yamamoto T, Kanamura N, Ohgitani E, Yamamoto K, Mazda O, Pezzotti G (2020) 3D-additive deposition of an antibacterial and osteogenic silicon nitride coating on orthopaedic titanium substrate. J Mech Behav Biomed Mater 103:10355710.1016/j.jmbbm.2019.103557 ↗
32. Li K, Jin S, Zhou Y, Zhang F, Zeng G, Li J, Shi SQ, Li J (2022) Bioinspired dual-crosslinking strategy for fabricating soy protein-based adhesives with excellent mechanical strength and antibacterial activity. Compos Part B Eng 240:10998710.1016/j.compositesb.2022.109987 ↗
33. Li K, Jin S, Jiang S, Li X, Li J, Shi SQ, Li J (2022) Bioinspired mineral–organic strategy for fabricating a high-strength, antibacterial, flame-retardant soy protein bioplastic via internal boron–nitrogen coordination. Chem Eng J 428:13261610.1016/j.cej.2021.132616 ↗