Effect of Tb substitution on the magnetic properties of exchange-biased Nd2Fe14B/Fe3B
Source abstract
Abstract
Tb-substituted (Nd,Tb)2Fe14B/Fe3B nanocomposite ribbons have been synthesized by melt spinning of Nd3Tb1Fe76Cu0.5Nb1B18.5 alloys. Tb substitution has significantly enhanced the value of coercivity and Curie temperature. Highest value of coercivity has been obtained as 4.76 kOe for the sample annealed at 953 K for 10 min. Curie temperature of Tb substituted sample, Nd3Tb1Fe76Cu0.5Nb1B18.5 is 549 K while Curie temperature of the sample without Tb, Nd4Fe76Cu0.5Nb1B18.5 is 535 K. Recoil hysteresis loops measured along the major demagnetization curve are steep having small recoil loop area. Temperature dependence of coercivity, remanent ratio and maximum energy product have been measured for the sample annealed at 893 K and 923 K for 10 min. At 5 K, coercivity and maximum energy product of the sample annealed at 893 K for 10 min are 5.2 kOe and 11.5 MGOe respectively and the sample annealed at 923 K for 10 min are 6 kOe and 13.1 MGOe respectively.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Magnetic Properties of Alloys · Magnetic properties of thin films · Magnetic Properties and Applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (10)
Show source-provided references
1. Kneller EF, Hawig R (1991) IEEE Trans Magn 27:358810.1109/20.102931 ↗
2. Sagawa M, Fujimura S, Yamamoto H, Matsuura Y (1984) IEEE Trans Magn Mag-20:158410.1109/TMAG.1984.1063214 ↗
3. Jin ZQ, Okumura H, Hadjipanayis GC (2001) IEEE Trans Magn 37:256410.1109/20.951236 ↗
4. Harland CL, Lewis L-H, Chen Z, Ma B-M (2004) J Magn Mag Mater 271:5310.1016/j.jmmm.2003.09.014 ↗
5. Kang K, Lewis LH, Jiang JS, Bader SD (2005) J Appl Phys 98:11390610.1063/1.2138785 ↗
6. Withanawasam L, Hadjipanayis GC, Krause RF (1994) J Appl Phys 75:664610.1063/1.356882 ↗
7. Givord D, Tenaud P, Viadieu T (1986) J Appl Phys 60:326310.1063/1.337715 ↗
8. Givord D, Li HS, Perrier R (1984) Solid State Commun 51:85710.1016/0038-1098(84)91087-1 ↗
9. Hadjipanayis GC, Hall C, Kim A (1987) IEEE Trans Magn 23:253310.1109/TMAG.1987.1065347 ↗
10. Hadjipanayis GC, Withanawasam L, Krause RF (1995) IEEE Trans Magn 31:359610.1109/20.489581 ↗