High-temperature pyrolysis of ceramic fibers derived from polycarbosilane–polymethylhydrosiloxane polymer blends with porous structures

The polymer blends of PCS (polycarbosilane) and PMHS-h (polymethylohydrosiloxane with high molecular weight) were prepared by freeze-drying process of mixed benzene solution. Melt viscosity, mass loss, and gas evolution from prepared polymer blends were analyzed. A polymer blend of HSah15 (15 mass% PMHS-h to PCS) was melt-spun to fiber form, curing by thermal oxidation and pyrolyzed at various temperatures up to 1773 K. The obtained fibers were investigated by tensile tests, FE-SEM (field emission scanning electron microscope) observation, and XRD (X-ray diffraction) analysis. After pyrolysis at 1273 K, there were no pores in the cross section of the fiber derived from pure PCS; however, there were amounts of pores in the cross sections of the fiber derived from HSah15. After pyrolysis at 1773 K, the coarse β-SiC (silicon carbide) crystals were formed on the outside surface of the fiber derived from pure PCS; however, no remarkable β-SiC crystal were formed on the outside surface of the fiber derived from HSah15.