Microstructure and tensile properties of metal injection molding Co–29Cr–6Mo–0.23C alloy
Source abstract
Abstract
The microstructure and tensile properties of a metal injection molding 0.23%C Co–Cr–Mo alloy (F75 alloy) were investigated. The as-sintered microstructure contains a significant amount of carbides, and is modified by solution annealing, the main effect being to reduce the amount of carbides. Ductility and ultimate tensile strength increase significantly, but yield strength decreases with solution annealing. Aging causes both intragranular and intergranular precipitation, which increases hardness and yield strength but decreases ductility excessively. In both as-sintered and solution-annealed conditions, the material displays noticeable work hardenability. By sintering at 1300 °C and solution annealing at 1220 °C, 440 MPa yield strength and 25% elongation at fracture are obtained.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Advanced materials and composites · Injection Molding Process and Properties · Powder Metallurgy Techniques and Materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (23)
Show source-provided references
1. Kilner T, Pilliar RM, Weatherly GC, Allibert C (1982) J Biomed Mater Res 16:6310.1002/jbm.820160109 ↗
2. Weeton JW, Signorelli RA (1955) Trans Am Soc Met 47:815
3. Caudillo M, Herrera-Trejo M, Castro MR, Ramirez E, Gonzalez CR, Juarez JI (2002) J Biomed Mater Res 59(2):37810.1002/jbm.10001 ↗
4. Mancha H, Gomez M, Castro M, Mendez M, Mendes J, Juarez J (1996) J Mater Synth Process 4(4):217
5. Saldivar Garcia AJ, Lopez HF (2005) J Biomed Mater Res 74A:26910.1002/jbm.a.30392 ↗
6. Dobbs HS, Robertson JLM (1983) J Mater Sci 18:391. doi: https://doi.org/10.1007/BF0056062710.1007/BF00560627 ↗
7. Taylor RNJ, Waterhouse RB (1983) J Mater Sci 18:3265. doi: https://doi.org/10.1007/BF0054415110.1007/BF00544151 ↗
8. Vander Sande JB, Coke JR, Wulff J (1976) Metall Trans 7A:38910.1007/BF02642835 ↗
9. Billiet RT, Billiet TH (2006) A practical guide to metal and ceramic injection moulding. Elsevier, Oxford
10. Johnson JL, Heaney DF. Advanced Powder Products, Inc. https://doi.org/www.advancedpowderproducts.com/publications.asp . Accessed 15 March 2009
11. Tandon R (1999) In: Disegi JA, Kennedy RL, Pilliar R (eds) Cobalt-base alloys for biomedical applications, ASTM STP 1365. ASTM, West Conshohocken, p 310.1520/STP14259S ↗
12. Sago JA, Chen H, Broadley MW, Eckert JK (2009) Adv Powder Metall Part Mater 4:111
13. Muterlle PV, D’Incau M, Perina M, Bardini R, Molinari A (2008) Adv Powder Metall Part Mater 4:183
14. Lutterotti L, Matthies S, Wenk HR, Shultz AS, Richardson JW (1997) J Appl Phys 81:59410.1063/1.364220 ↗
15. Lonardelli I, Wenk HR, Lutterotti L, Goodwin M (2005) J Synchrotron Radiat 12:35410.1107/S090904950500138X ↗
16. Clemow AJT, Daniell BL (1979) J Biomed Mater Res 13:26510.1002/jbm.820130208 ↗
17. Shortsleeve FJ, Nicholson ME (1951) Trans Am Soc Met 43:142
18. Rajan K (1982) Metall Trans 13A:116110.1007/BF02645497 ↗
19. Rajan K (1984) Metall Trans 15A:133510.1007/BF02648562 ↗
20. Betteridge W (1982) Cobalt and its alloys. Ellis Horwood, Chichester
21. Dieter GE (1988) Mechanical metallurgy (adapted by D. Bacon), SI Metric edn. Materials Science & Metallurgy, Singapore
22. Salinas-Rodriguez A, Rodriguez-Galicia JL (1996) J Biomed Mater Res 31:40910.1002/(SICI)1097-4636(199607)31:3<409::AID-JBM16>3.0.CO;2-D ↗
23. Kim YG, Lim CY (1988) Metall Trans 19A:162510.1007/BF02674039 ↗