Formation and retention of local melted films in AZ91 friction stir spot welds
Source abstract
Abstract
The formation of local melted films during friction stir spot welding of as-cast AZ91D and thixomolded AZ91 material is investigated. The average temperatures close to the tip of the rotating pin vary from 438 to 454 °C during the dwell period in friction stir spot welding. These measured temperature values are higher than the melting temperature of α-Mg + Mg17Al12 eutectic (437 °C). It is suggested that the temperature in the stir zone during the dwell period is determined by the relative proportions of α-Mg and (α-Mg + Mg17Al12) eutectic material, which are incorporated during friction stir spot welding. Based on the stir zone temperature measurements and a detailed examination of material located at the root of the pin thread it is suggested that material is moved downwards via the pin thread and into the stir zone during the dwell period in friction stir spot welding. Evidence of local melted film formation is observed in the stir zone of AZ91 spot welds. It is suggested that melted films are retained since their dissolution rate is much slower in the high temperature stir zone than it is when melted films is formed in the stir zone during Al 7075-T6 friction stir spot welding. The spontaneous melting temperature, solute diffusion rate and the thermodynamic driving force for droplet dissolution are much higher during Al 7075-T6 friction stir spot welding.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Advanced Welding Techniques Analysis · Aluminum Alloys Composites Properties · Aluminum Alloy Microstructure Properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (23)
Show source-provided references
1. Su P, Gerlich A, North TH, Bendzsak GJ (2006) Sci Tech Weld Joining 11(2):16310.1179/174329306X84373 ↗
2. Su P, Gerlich A, North TH (2006) SAE Technical Series, 2006-01-0971
3. Gerlich A, Avramovic-Cingara G, North TH (2006) Metall Trans A 37A:277310.1007/BF02586110 ↗
4. Gerlich A, Su P, North TH (2005) J Mat Sci 40:647310.1007/s10853-005-1568-9 ↗
5. Gerlich A, Su P, North TH (2005) Sci Tech Weld Joining 10(6):64710.1179/174329305X48383 ↗
6. Gerlich A, Su P, North TH, Bendzsak GJ (2005) In: Nie JF et al (eds) Materials forum 29:290
7. Gerlich A, Su P, North TH (2005) In: Neelameggham NR, Kaplan HI, Powell BR (eds) Magnesium technology 2005. TMS, p 383
8. Lin P-C, Lin S-H, Pan J, Pan T, Nicholson JM, Garman MA (2004) SAE Technical Series, 2004-01-1330
9. Gerlich A, Su P, North TH, Bendzsak GJ (2006) Proc Friction Stir Welding Colloquium, Graz, Austria, May 23rd 2006
10. Su P, Gerlich A, North TH, Bendzsak GJ (2007) Metall Trans A 38A:58410.1007/s11661-006-9067-4 ↗
11. Droenen P-E, Ryum N (1994) Metall Trans A 25A:52110.1007/BF02651593 ↗
12. Reiso O, Øverlie H-G, Ryum N (1990) Metall Trans A 21A:168910.1007/BF02672585 ↗
13. Lohne O, Ryum N (1988) Proc. 4th Int. Aluminum extrusion technology seminar, Aluminum Association, vol II. 303
14. Lyman T (1961) ASM metals handbook, 8th edn. American Society for Metals, Metals Park, Ohio
15. Bendzsak GJ, North TH, Smith CB (2000) Proc. 2nd Int. Conf. Friction Stir Welding, Gothenburg, Sweden, TWI
16. North TH, Bendzsak GJ, Smith CB, Luan GH (2001) Proc. of the 7th Int. Symp. of JWS. p 621
17. Bowden FP, Ridler KEW (1936) Proc Roy Soc 154(883):640
18. Bowden P, Thomas PH (1954) Proc Roy Soc 223(1152):29
19. Song M, Kovacevic R (2002) Trans SME 621
20. Colegrove P, Shercliff H (2003) Sci Tech Weld Joining 8(5):36010.1179/136217103225005534 ↗
21. Whelan MJ (1969) Met Sci J 3:9510.1179/msc.1969.3.1.95 ↗
22. Su J-Q, Nelson TW, Mishra M, Mahoney M (2003) Acta Mat 51:71310.1016/S1359-6454(02)00449-4 ↗
23. Su P, Gerlich A, North TH, Bendzsak GJ, (2006) Sci Tech Weld Joining 11(1):6110.1179/174329306X77056 ↗