Photoluminescence investigations on alumina ceramic bearing couples tested under different angles of inclination in a Hip joint simulator

Aseptic loosening due to wear and dislocation of the implant represents the main complication after total hip arthroplasty. To gain more insight into the influence of the implant position on wear, commercial alumina couplings have been tested in a hip joint simulator under three different angles of cup inclination (23°, 45°, 63°) with respect to a horizontal plane. The planned length of the test was ten million cycles. However, the test was stopped at 5.5 million cycles due to the fracture of one of the femoral heads, tested with at angle of 63°. The residual stress state in the worn acetabular cups and in the fractured femoral head were evaluated by the frequency shift and broadening of the R1 and R2 fluorescence bands due to the Cr3+ ions naturally present in alumina ceramics as trace impurities.