Preparation and characterisation of ceramic-faced metal–ceramic interpenetrating composites for impact applications

This article accesses the impact performance of ceramic-faced, metal–ceramic interpenetrating composites (IPCs) produced in situ from infiltrating ceramic foams with a molten aluminium–magnesium alloy. The approach had two variations, viz., the production of a metal bond between a ceramic front face and backing IPC and the creation of a ceramic bond. The impact performance of metal-bonded IPCs was evaluated using both split Hopkinson’s pressure bar (SHPB) and depth of penetration (DoP) techniques. With a 4-mm thick Al2O3 front face and an 8-mm thick IPC backing, the DoP was zero. In one case, a sample survived fundamentally intact with only spall damage to the dense Al2O3 front face. The resulting damage was thoroughly assessed using a range of techniques, including polarized light microscopy, scanning electron microscopy (SEM), 3D MicroCT and transmission electron microscopy (TEM). The metal phase deformed as a result of the formation of large numbers of dislocations, whilst the ceramic phase accommodated the deformation via localised cracking. Metal bridges across the cracks formed, increasing the damage tolerance of the IPCs. The metal bond between the ceramic front face and the IPC was also observed to withstand the impact of the armour piercing rounds without any sign of debonding occurring.