Zone-melted unidirectional solidification of particulate dispersed composites

In order to solve the problem of particles settling and agglomeration in front of solidifying interface in unidirectional solidification (UDS) experiments, a zone-melted process has been utilized in this study. The experimental results show that, the melting zone could be kept in 30–40 mm width and the zone melted UDS experiments are realized with Al2O3 particle reinforced aluminum-matrix composites. But particle settling still occurs in the liquid, and becomes severe as the particle volume fraction decreases. However, when the volume fraction of the particles is more than 20–22 vol.%, no further settling occurs under a solidification rate of 8–16 mm/h. Investigation on the interaction of particles and solid/liquid interface reveals that the Al2O3 particles are rejected into liquid and pushed by the growing solid phase in Al2O3(P)/Al and Al2O3(P)/Al-0.23wt.%Ce composites. Some particles are mechanically entrapped between cells, and distributed along the crystal grain boundaries.