The influence of artificial aging on the microstructure and hardness of an Al–Zn–Mg–Zr alloy processed by equal-channel angular pressing
Source abstract
Abstract
The effect of artificial aging on the microstructure and hardness of an ultrafine-grained (UFG) Al–4.8%Zn–1.2%Mg–0.14%Zr (wt%) alloy was studied. The UFG microstructure with an average grain size of about 260 nm was obtained by severe plastic deformation applying four passes of equal-channel angular pressing (ECAP) at room temperature. Then, artificial aging was performed on the ECAP-processed samples at 120 °C and 170 °C for 2 h. In the ECAP-processed sample Guinier–Preston (GP) zones, MgZn2 precipitates and a high dislocation density were observed. After aging at 120 °C, coarse MgZn2 precipitates were formed in the grain boundaries, leading to softening, while the dislocation density did not decrease. Annealing at 170 °C yielded a growth of the matrix grains to ~ 530 nm with a significant decrease in the dislocation density. In addition, GP zones disappeared and MgZn2 precipitates were formed in both the grain interiors and the boundaries. This overaging of the precipitate structure and the decrease in the dislocation density resulted in a lower hardness than after annealing at 120 °C. It was found that the hardness reduction due to the change of the precipitate structure at 170 °C was higher than that caused by the decrease in the dislocation density.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Microstructure and mechanical properties · Aluminum Alloy Microstructure Properties · Advanced materials and composites
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (29)
Show source-provided references
1. Mondolfo LF (1971) Structure of the aluminium: magnesium: zinc alloys. Int Metall Rev 153:95–12410.1179/095066071790137865 ↗
2. Polmear IJ (1995) Light alloys-metallurgy of the light metals, 3rd edn. Arnold, London
3. Lendvai J (1996) Precipitation and strengthening in aluminium alloys. Mater Sci Forum 217–222:43–5610.4028/www.scientific.net/MSF.217-222.43 ↗
4. Löffler H, Kovács I, Lendvai J (1983) Decomposition processes in Al–Zn–Mg alloys. J Mater Sci 18:2215–2240. https://doi.org/10.1007/BF0054182510.1007/BF00541825 ↗
5. Liddicoat PV, Liao XZ, Zhao Y, Zhu Y, Murashkin MY, Lavernia EJ, Valiev RZ, Ringer SP (2010) Nanostructural hierarchy increases the strength of aluminium alloys. Nat Commun 1:63. https://doi.org/10.1038/ncomms106210.1038/ncomms1062 ↗
6. Watanabe K, Matsuda K, Ikeno S, Yoshida T, Murakami S (2015) TEM observation of precipitate structures in Al–Zn–Mg alloys with addition of Cu/Ag. Metall Mater 60:977–97910.1515/amm-2015-0244 ↗
7. Wu C, Ma K, Zhang D, Wu J, Luo G, Zhang J, Chen F, Shen Q, Zhang L, Lavernia EJ (2017) Precipitation phenomena in Al–Zn–Mg alloy matrix composites reinforced with B4C particles. Sci Rep 7:9589. https://doi.org/10.1038/s41598-017-10291-410.1038/s41598-017-10291-4 ↗
8. Bobruk E, Murashkin MY, Kazykhanov VU, Valiev RZ (2018) Superplastic behavior at lower temperatures of high strength ultrafine-grained Al alloy 7475. Adv Eng Mater 21:1800094. https://doi.org/10.1002/adem.20180009410.1002/adem.201800094 ↗
9. Wang D, Ma ZY (2009) Effect of pre-strain on microstructure and stress corrosion cracking of over-agaed 7050 aluminum alloy. J Alloys Compd 469:445–45010.1016/j.jallcom.2008.01.137 ↗
10. Zhao YH, Liao XZ, Jin Z, Valiev RZ, Zhu YT (2004) Microstructures and mechanical properties of ultrafine grained 7075 Al alloy processed by ECAP and their evolutions during annealing. Acta Mater 52:4589–459910.1016/j.actamat.2004.06.017 ↗
11. Xu C, Furukawa M, Horita Z, Langdon TG (2005) Influence of ECAP on precipitate distributions in a spray-cast aluminum alloy. Acta Mater 53:749–75810.1016/j.actamat.2004.10.026 ↗
12. Xu C, Furukawa M, Horita Z, Langdon TG (2003) Using ECAP to achieve grain refinement, precipitate fragmentation and high strain rate superplasticity in a spray-cast aluminum alloy. Acta Mater 51:6139–614910.1016/S1359-6454(03)00433-6 ↗
13. Gubicza J, Schiller I, Chinh NQ, Illy J, Horita Z, Langdon TG (2007) The effect of severe plastic deformation on precipitation in supersaturated Al–Zn–Mg alloys. Mater Sci Eng A 460–461:77–8510.1016/j.msea.2007.01.001 ↗
14. Samaee M, Najafi S, Eivani AR, Jafarian HR, Zhou J (2016) Simultaneous improvements of the strength and ductility of fine-grained AA6063 alloy with increasing number of ECAP passes. Mater Sci Eng A 669:350–35710.1016/j.msea.2016.05.070 ↗
15. Ashrafizadeh SM, Eivani AR, Jafarian HR, Zhou J (2017) Improvement of mechanical properties of AA6063 aluminum alloy after equal channel angular pressing by applying a two-stage solution treatment. Mater Sci Eng A 687:54–6210.1016/j.msea.2017.01.024 ↗
16. Duan ZC, Chinh NQ, Xu Ch, Langdon TG (2010) Developing processing routes for the equal-channel angular pressing of age-hardenable aluminum alloys. Metall Mater Trans 41A:802–80910.1007/s11661-009-0020-1 ↗
17. Chinh NQ, Lendvai J, Ping DH, Hono K (2004) The effect of Cu on mechanical and precipitation properties of Al–Zn–Mg alloys. J Alloys Compd 378:52–6010.1016/j.jallcom.2003.11.175 ↗
18. Dorward RC, Beerntsen DJ (1995) Grain structure and quench-rate effects on strength and toughness of AA7050 Al–Zn–Mg–Cu–Zr alloy plate. Metall Trans A 26:2481–248410.1007/BF02671263 ↗
19. Chinh NQ, Juhász A, Tasnádi P, Lendvai J, Kovács I (1993) Effect of copper and zirconium upon the high temperature mechanical properties of AlMgZn alloys. Phys Stat Sol (a) 138:175–18410.1002/pssa.2211380115 ↗
20. Eivani AR, Zhou J, Duszczyk J (2012) A new approach to incorporating the effect of nano-sized dispersoids on recrystallization inhibition into Monte carlo simulation. Comput Mater Sci 54:370–37710.1016/j.commatsci.2011.10.016 ↗
21. Buranova Y, Kulitskiy Peterlechner M, Mogucheva A, Kaibyshev R, Divinski SV, Wilde G (2017) Al3(Sc, Zr)-based precipitates in Al–Mg alloy: effect of severe deformation. Acta Mater 124:210–22410.1016/j.actamat.2016.10.064 ↗
22. Iwahashi Y, Wang J, Horita Z, Nemoto M, Langdon TG (1996) Principle of equal-channel angular pressing for the processing of ultra-fine grained materials. Scr Mater 35:143–14610.1016/1359-6462(96)00107-8 ↗
23. Furukawa M, Iwahashi Y, Horita Z, Nemoto M, Langdon TG (1998) The shearing characteristics associated with equal-channel angular pressing. Mater Sci Eng A 257:328–33210.1016/S0921-5093(98)00750-3 ↗
24. Ribárik G, Gubicza J, Ungár T (2004) Correlation between strength and microstructure of ball-milled Al–Mg alloys determined by X-ray diffraction. Mater Sci Eng A 387–389:343–34710.1016/j.msea.2004.01.089 ↗
25. Ungár T, Tichy G, Gubicza J, Hellmig RJ (2005) Correlation between subgrains and coherently scattering domains. Powder Diffr 20:366–37510.1154/1.2135313 ↗
26. Priya P, Krane MJM, Johnson DR (2016) Precipitation of Al3Zr dispersoids during homogenization of Al–Zn–Cu–Mg–Zr alloys. In: Williams E (ed) Light metals 2016. Springer, Cham, pp 213–21810.1007/978-3-319-48251-4_36 ↗
27. Gubicza J, Schiller I, Chinh NQ, Illy J, Horita Z, Langdon TG (2007) The effect of severe plastic deformation on precipitation in supersaturated Al–Zn–Mg alloys. Mater Sci Eng A 460–461:77–8510.1016/j.msea.2007.01.001 ↗
28. Gubicza J, Chinh NQ, Lábár JL, Hegedűs Z, Xu C, Langdon TG (2008) Microstructure and yield strength of severely deformed silver. Scr Mater 58:775–77810.1016/j.scriptamat.2007.12.028 ↗
29. Tabor D (1951) Hardness of metals. Clarendon Press, Oxford