Effect of austenitizing temperature and cooling rate on the structure and properties of a ultrahigh strength low alloy steel

N. Kishore Babu, M. R. Suresh, P. P. Sinha, D. S. Sarma

Journal of Materials Science· Volume 41· Issue 10
Publisher page

Abstract

A 0.3C-CrMoV(ESR) steel is being developed primarily for making pressure vessels used for aerospace applications. Since it is important to understand the range of microstructures and mechanical properties that will be obtained in the heat affected zone of welds, the steel has been subjected to different austenitizing treatments (temperatures ranging from 925°C to 1250°C) followed by cooling at various rates to room temperature. It has been shown that the austenite grain size increased from about 10 to 250 μm as the austenitizing temperature is increased from 925°C to 1250°C (1 hr) and that the hardness, YS, UTS,% elongation and% reduction in area as well as CVN energy for 450°C tempered condition decrease as the austenitizing temperature is increased for all cooling rates (furnace cooling, air cooling, oil quenching, quenching and tempering at 450°C). This is attributed mainly to the increase in austenitic grain size. The ranges of microstructures that can be obtained in the heat-affected zone are massive ferrite, fine pearlite, upper as well as lower bainite and martensite. The Charpy impact energy for the oil-quenched steel tempered at 200°C, however, did not vary significantly with austenitizing temperature.
Source: openaire · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Microstructure and Mechanical Properties of Steels · Metal Alloys Wear and Properties · Welding Techniques and Residual Stresses

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (16)

Show source-provided references
1. French Norms for Steel Products (AFNOR-BNS), Spec. no. A35-55A, Paris, France 1 (1978) 299.
2. K. SREEKUMAR, M. S. P. MURTY, A. NATARAJAN and P. P. SINHA, Trans. Indian Inst. Met. 35 (1982) 349.
3. J. M. HOLT, H. MINDLIN and C. Y. HO, Structural Alloys HandBook CINDAS/Purdue University, West Lafayette, Indiana, USA, 1996 vol. 1.
4. M. R. SURESH, I. SAMAJDAR, A. INGLE, N. B. BALLAL, P. K. RAO and P. P. SINHA, Iron. Steel. 30 (2003) 379.10.1179/030192303225004097 ↗
5. M. CHATTERJEE, M. S. N. BALASUBRAMANIAN, K. M. GUPT and P. K. RAO, Ironmaking and Steelmaking 17 (1990) 38.
6. G. M. PADKI, M. S. N. BALASUBRAMANIAN, K. M. GUPT and P. K. RAO, ibid. 10 (1983) 180.
7. G. HOYLE, Electroslag Processes: Principles and Practice (Applied Science Publishers, London & New York, 1983).
8. M. R. SURESH, Development of a New Ultrahigh Strength Steel and Studies of its Microstructure and Properties, Ph.D. Thesis, IIT, Bombay, 2002.
9. L. A. NORSTORM, Scand. J. Metall. 5 (1976) 159.
10. R. VISHWANATHAN and A. JOSHI, Met. Trans. A. 6A (1975) 2289.10.1007/BF02818656 ↗
11. G. J. P. BUCHI, J. H. R. PAGE and M. P. SIDEY, J. Iron. Steel. Inst. 203 (1965) 291.
12. H. R. TIPLER, L. H. TAYLOR and G. B. THOMAS, Metal. Tech. 2 (1975) 206.10.1179/030716975803277609 ↗
13. R. M. HORN and R. O. RITCHIE, Met. Trans. A. 9A (1978) 1039.10.1007/BF02652208 ↗
14. G. THOMAS, Met. Trans. A. 9 (1978) 439.10.1007/BF02646396 ↗
15. G. R. SPEICH, D. S. DABKOWSKI and L. F. PORTER, Met. Trans. 4 (1973) 303.10.1007/BF02649630 ↗
16. P. M. MACMEIER, C. D. LITTLE. M. H. HOROWITZ and R. P. OATES, Metal. Tech. (1979) 291.10.1179/030716979803276138 ↗