Effect of high temperature exposure on the microstructure of Udimet-500 super alloy

Noveed Ejaz, Muhammad Mansoor, Iftikhar Salam

Journal of Materials Science· Volume 45· Issue 16
Publisher page

Abstract

Udimet-500 alloy is a high-strength nickel-bases super alloy used for turbine blades applications. It is primarily strengthened by very fine precipitates called gamma prime (γ′) which coarsened with time when exposed to high temperature. In this study, Udimet-500 alloy in the standard aged condition was exposed at 850–1100 °C for 25–100 h in air. The change in the size of γ′ with respect to the high temperature exposure was characterized using scanning electron microscope. A systematic coarsening of the γ′ was observed with the change in the exposure temperature/time. The γ′ size in the virgin sample was 0.1 μm while after high temperature exposures it coarsened to 1 μm. The Larson-Miller parameter (LMP) of the high temperature exposure was also measured. It was found that the LMP had power relation with the γ′ size. In addition, degradation of the primary as well as secondary carbides was also observed which can be used as add-on microstructural information in high temperature exposure. Elevated temperature exposure (≥1000 °C) also lead to (a) near surface de-alloying, (b) precipitation of needle-like Ti-rich phase and (c) depletion of γ′. It may contribute in the accelerated corrosion and loss of strength of alloy.
Source: openaire · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: High Temperature Alloys and Creep · High-Temperature Coating Behaviors · Advanced Materials Characterization Techniques

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (20)

Show source-provided references
1. Naga M, Kanaya A, Imano S, Doi H, Ichikawa K (2004) In: 16th world conference on NDT, Montreal, Canada, www.ndt.net
2. Lvova E, Norsworthy D (2001) J Mater Eng Perform 10(3):29910.1361/105994901770345015 ↗
3. Cheruvu NS (2000) In: Proceeding of 2000 international joint power generation conference, Miami Beach, Florida, 23–26 July 2000, Paper IJPGC2000-15068
4. Huff H, Pillhofer H (1988) In: Superalloys 1988, The Metallurgical Society, pp 835–84310.7449/1988/Superalloys_1988_835_843 ↗
5. Ejaz N, Tauqire A (2006) Eng Fail Anal 13:45210.1016/j.engfailanal.2004.12.041 ↗
6. Koul AK et al (1988) In: Reichman S (ed) Superalloys-1988. The Metallurgical Society, Inc., Warrendale, PA, p 75510.7449/1988/Superalloys_1988_755_764 ↗
7. James A (2001) Mater Sci Technol 17:48110.1179/026708301101510168 ↗
8. Hunt MW (ed) (1999) ASM J Adv Mater Proc 156:7910.2307/4011591 ↗
9. Stolof CT, Norman S, Hagel WC (1987) Superalloys-II. Wiley, New York, pp 124–125
10. Hertzberg RW (1996) Deformation and fracture mechanics of engineering materials, 4th edn. Wiley, Hoboken, NJ
11. Wlodek ST, Field RD (1994) In: Loria EA (ed) Superalloy 718, 625, 706 and various derivatives. The Minerals Metals and Materials Research Society, pp 659–67110.7449/1994/Superalloys_1994_659_670 ↗
12. Smith WF (1993) Structure and properties of engineering alloys, 2nd edn. McGraw Hill, New York, p 47
13. Chester CS (1966) J Met 10:1119
14. Vander Voort GF (1986) In: Kathleen M, Davis JR (eds) Metallography and microstructure. Metal handbook, vol 9, 9th edn. ASM, Materials Park, OH, pp 305–329
15. Stolof CT, Norman S, Hagel WC (1987) Superalloys II. Wiley, New York, pp 124–125
16. Murphy HJ, Sims CT (1967) Trans AIME 239:1961
17. Loomis WT et al (1972) Met Trans 3:98910.1007/BF02647677 ↗
18. Sims CC (1966) J Met 18:111910.1007/BF03378505 ↗
19. Lindblom Y (1978) In: Courtsouradis D et al (eds) Creep and structural stability of high temperature materials: high temperature alloys for gas turbines. Applied Science Publishers, England, pp 285–316
20. Metallurgical Analysis, Liburdi Engineering, Technology Update 1(2), 1996