The relationship between atomic partitioning and corrosion resistance in the weld-heat affected zone microstructures of UNS S32304 duplex stainless steel
Source abstract
Abstract
Wrought material as well as physically simulated welding heat affected zone (HAZ) samples of an UNS S32304 duplex stainless steel were subjected to electrochemical corrosion tests and electron microscopy characterization. An impaired corrosion resistance of the HAZ microstructures compared to the wrought material microstructure was observed. Calphad-based numerical simulation of phase transformations and solute redistribution taking place during welding provided an explanation of the observed corrosion behavior. The poor corrosion resistance of the HAZ microstructures studied was mainly attributed to a decrease in corrosion resistance of ferritic grains after welding, which exhibited lower chromium content than ferritic grains in the wrought material.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Hydrogen embrittlement and corrosion behaviors in metals · Corrosion Behavior and Inhibition · Welding Techniques and Residual Stresses
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (15)
Show source-provided references
1. Ogawa TO, Koseki T (1989) Weld J 68:181
2. Atamert S, King JE (1991) Z Metallkd 82:230
3. Nilsson JO, Karlsson L, Andersson JO (1995) Mat Sci Techn 11:27610.1179/mst.1995.11.3.276 ↗
4. Gooch TG (1996) Weld J 75:135
5. Gregory A, Nilsson J-O (2002) Met Mat Trans – A 33A:100910.1007/s11661-002-0202-6 ↗
6. Ramirez AJ, Lippold JC, Brandi SD (2003) Met Mat Trans – A 34A:157510.1007/s11661-003-0304-9 ↗
7. Ramirez AJ, Ph.D. Thesis, University of São Paulo, São Paulo, Brazil, 2001, p. 241. Full text available at http://www.teses.usp.br/teses/disponiveis/3/3133/tde–02012002–175418/
8. Hertman S, Huhtala T, Karlsson L, Nilsson J-O, Jargelius-Pettersson R, Wilson A (1997) Mater Sci Tech 13:60410.1179/mst.1997.13.7.604 ↗
9. Nilsson J-O, Huhtala T, Jonsson P, Karlsson L, Wilson A (1996) Met Mat Trans – A 27A:219610.1007/BF02651874 ↗
10. Majidi AP, Streicher MA (1984) Corrosion 40:39310.5006/1.3593944 ↗
11. Andersson JO, Helander T, Hoglund LH, Shi PF, Sundman B (2002) CALPHAD 26:27310.1016/S0364-5916(02)00037-8 ↗
12. Garzón CM, Ramirez AJ (2006) Acta Mater 54:332110.1016/j.actamat.2006.03.018 ↗
13. Andersson JO, Ågren J (1992) J Appl Phys 72:135010.1063/1.351745 ↗
14. Muthupandi V, Bala Srinivasan P, Seshadri SK, Sundaresan S (2004) Sci Technol Weld Joi 9:4710.1179/136217104225017143 ↗
15. Menendez H, Devine TM (1990) Corrosion 46:41010.5006/1.3585125 ↗