An alternative to the JMAK equation for a better description of phase transformation kinetics
Source abstract
Abstract
The kinetics of phase transformations is usually described by the Johnson–Mehl–Avrami–Kolmogorov (JMAK) equation. The article shows that this equation cannot give a sufficiently general description of austenitization kinetics of ferritic nodular cast iron. Therefore, another kinetics equation is proposed which catches the main circumstances and substance of austenitization more accurately than the JMAK equation does. It shows that the crucial phenomena in the transformation are not only the processes of the creation and growth of new austenite grains but also the change in specific volume and the chemical liquation of alloying additives, which retard the subsequent conversion. The proposed equation together with the Arrhenius equation allows describing simultaneously the temporal and temperature dependence of austenitization conversion including the partial transformation at insufficiently high overheating of transformed iron. It is verified by successful regression of experimental data, whose results allow drawing predictive curves for temperatures from the experimental temperature region or from its near vicinity, for which the conversion was not determined.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Microstructure and Mechanical Properties of Steels · Metal Alloys Wear and Properties · Metallurgy and Material Forming
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (20)
Show source-provided references
1. Keough JR (1995) Foundry Manage Technol 123(11):27
2. Nath SK, Ray S, Mathur VNS, Kapoor ML (1994) ISIJ Int 34:19110.2355/isijinternational.34.191 ↗
3. Zhang W, Elmer JW, Debroy T (2002) Mater Sci Eng A 333:32010.1016/S0921-5093(01)01857-3 ↗
4. Elmer JW, Palmer TA, Zhang W, Wood B, Debroy T (2003) Acta Mater 51:333310.1016/S1359-6454(03)00049-1 ↗
5. Elmer JW, Palmer TA, Babu SS, Zhang W, Debroy T (2004) Weld J 83:224S
6. Kumar A, Mishra S, Elmer JW, Debroy T (2005) Metal Mater Trans A 36:1510.1007/s11661-005-0134-z ↗
7. Johnson WA, Mehl RF (1939) Trans AIME 135:416
8. Avrami M (1939) J Chem Phys 7:110310.1063/1.1750380 ↗
9. Kolmogorov AN (1937) Izv Akad Nauk SSSR, Ser Matem 3:355
10. Todinov MT (2000) Acta Mater 48:421710.1016/S1359-6454(00)00280-9 ↗
11. Levine LE, Narayan KL, Kelton KF (1997) J Mater Res 12:12410.1557/JMR.1997.0020 ↗
12. Starink MJ, Zahra AM (1998) Philos Mag A 77:18710.1080/01418619808214237 ↗
13. Schmidt U, Schmidt B (2000) Mater Sci Forum 331–333:88910.4028/www.scientific.net/MSF.331-337.889 ↗
14. Starink MJ (2001) J Mater Sci 36:443310.1023/A:1017974517877 ↗
15. Starink MJ (2004) Int Mater Rev 49:19110.1179/095066004225010532 ↗
16. Herfurth K, Giesserei-Praxis (2003) 9910.1007/978-3-322-89946-0_3 ↗
17. Kohout J (1999) J Mater Sci 34:84310.1023/A:1004593417901 ↗
18. Kohout J (2004) J Phys IV 120:191
19. Kohout J (2007) Mater Sci Eng A 462:15910.1016/j.msea.2006.02.468 ↗
20. Dorazil E (1991) High strength austempered ductile cast iron. Horwood, London