Fabrication and characterization of cellulose nanofibrils/epoxy nanocomposite foam
Source abstract
Abstract
Plant-derived cellulose nanofibrils (CNFs) have shown reinforcing effects in polymer nanocomposites. However, freeze-dried CNFs are foam-like material, namely aerogel, that are challenging to disperse in a polymer matrix. In this work, a liquid infusion process was developed for a CNF/epoxy nanocomposite cross-linked foam structure with alterable properties without damaging the foam structure. Microstructures of CNF/epoxy composite foams with different formulations were evaluated using a scanning electron microscope. Surface morphology showed that the CNF cross-linked fibers were well attached by epoxy resin. All absolute and specific mechanical properties [by normalizing the measured parameters against the measured density (ρ)] were investigated. Water resistance and thermal stability of CNF/epoxy composite foams were investigated by water absorption test and thermogravimetric analysis. The concentration of epoxy solution in both tetrahydrofuran (THF) solvents and ethyl acetate (EA) solvents was shown to improve compressive properties and water resistance. The samples fabricated with higher epoxy concentration had higher compressive properties, better water resistance, and better thermal stability. The CNF/epoxy composite foams exhibited compressive modulus and compressive strength up to 175 and 10 MPa, respectively. The water diffusion coefficient of CNF/epoxy composite foams was reduced with an increase in epoxy loading. Further, the CNF/epoxy nanocomposite foams fabricated by the epoxy/THF solution had a more uniform structure and better strength performance than foams fabricated by the epoxy/EA solution, due to the increased solubility of the epoxy in THF compared to epoxy in EA. The glass transition temperature (Tg) was determined by differential scanning calorimetry. The Tg of the nanocomposites was influenced by the CNF/epoxy composition. Therefore, the properties of CNF/epoxy nanocomposite foams can be optimized via changing the solvent and concentration of epoxy resin in solvent.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Advanced Cellulose Research Studies · Natural Fiber Reinforced Composites · Lignin and Wood Chemistry
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (36)
Show source-provided references
1. Fowler PA, Hughes JM, Elias RM (2006) Biocomposites: technology, environmental credentials and market forces. J Sci Food Agric 86:1781–178910.1002/jsfa.2558 ↗
2. Zhang J, Luo N, Zhang X, Xu L, Wu J, Yu J et al (2016) All-cellulose nanocomposites reinforced with in situ retained cellulose nanocrystals during selective dissolution of cellulose in an ionic liquid. ACS Sustain Chem Eng 4:4417–442310.1021/acssuschemeng.6b01034 ↗
3. Huber T, Müssig J, Curnow O, Pang S, Bickerton S, Staiger MP (2012) A critical review of all-cellulose composites. J Mater Sci 47:1171–1186. doi:10.1007/s10853-011-5774-310.1007/s10853-011-5774-3 ↗
4. Lee S-Y, Chun S-J, Kang I-A, Park J-Y (2009) Preparation of cellulose nanofibrils by high-pressure homogenizer and cellulose-based composite films. J Ind Eng Chem 15:50–5510.1016/j.jiec.2008.07.008 ↗
5. Khalil HPSA, Bhat AH, Yusra AFI (2012) Green composites from sustainable cellulose nanofibrils: a review. Carbohydr Polym 87:963–97910.1016/j.carbpol.2011.08.078 ↗
6. Jeronimidis G (1980) Wood, one of nature’s challenging composites. Symp Soc Exp Biol 34:169–182
7. Bledzki AK, Gassan J (1999) Composites reinforced with cellulose based fibres. Prog Polym Sci 24:221–27410.1016/S0079-6700(98)00018-5 ↗
8. Gebald C, Wurzbacher JA, Tingaut P, Zimmermann T, Steinfeld A (2011) Amine-based nanofibrillated cellulose as adsorbent for CO2 capture from air. Environ Sci Technol 45:9101–910810.1021/es202223p ↗
9. Zhang Z, Sèbe G, Rentsch D, Zimmermann T, Tingaut P (2014) Ultralightweight and flexible silylated nanocellulose sponges for the selective removal of oil from water. Chem Mater 26:2659–266810.1021/cm5004164 ↗
10. Yao C, Hernandez A, Yu Y, Cai Z, Wang X (2016) Triboelectric nanogenerators and power-boards from cellulose nanofibrils and recycled materials. Nano Energy 30:103–10810.1016/j.nanoen.2016.09.036 ↗
11. Chen B, Zheng Q, Zhu J, Li J, Cai Z, Chen L et al (2016) Mechanically strong fully biobased anisotropic cellulose aerogels. RSC Adv 6:96518–9652610.1039/C6RA19280G ↗
12. Jung YH, Chang T-H, Zhang H, Yao C, Zheng Q, Yang VW et al (2015) High-performance green flexible electronics based on biodegradable cellulose nanofibril paper. Nat Commun 6:717010.1038/ncomms8170 ↗
13. Zheng Q, Javadi A, Sabo R, Cai Z, Gong S (2013) Polyvinyl alcohol (PVA)–cellulose nanofibril (CNF)–multiwalled carbon nanotube (MWCNT) hybrid organic aerogels with superior mechanical properties. RSC Adv 3:20816–2082310.1039/c3ra42321b ↗
14. Yao C, Wang F, Cai Z, Wang X (2016) Aldehyde-functionalized porous nanocellulose for effective removal of heavy metal ions from aqueous solutions. RSC Adv 6:92648–9265410.1039/C6RA20598D ↗
15. Lee Y, Choi J-W, Suh DJ, Ha J-M, Lee C-H (2015) Ketonization of hexanoic acid to diesel-blendable 6-undecanone on the stable zirconia aerogel catalyst. Appl Catal A 506:288–29310.1016/j.apcata.2015.09.008 ↗
16. Buratti C, Moretti E, Belloni E, Agosti F (2014) Development of innovative aerogel based plasters: preliminary thermal and acoustic performance evaluation. Sustainability 6:5839–585210.3390/su6095839 ↗
17. Li Z, Yao C, Wang F, Cai Z, Wang X (2014) Cellulose nanofiber-templated three-dimension TiO2 hierarchical nanowire network for photoelectrochemical photoanode. Nanotechnology 25:50400510.1088/0957-4484/25/50/504005 ↗
18. Zheng Q, Cai Z, Ma Z, Gong S (2015) Cellulose nanofibril/reduced graphene oxide/carbon nanotube hybrid aerogels for highly flexible and all-solid-state supercapacitors. ACS Appl Mater Interfaces 7:3263–327110.1021/am507999s ↗
19. Zheng Q, Cai Z, Gong S (2014) Green synthesis of polyvinyl alcohol (PVA)–cellulose nanofibril (CNF) hybrid aerogels and their use as superabsorbents. J Mater Chem A 2:3110–311810.1039/C3TA14642A ↗
20. Hodgkin JH, Simon GP, Varley RJ (1998) Thermoplastic toughening of epoxy resins: a critical review. Polym Adv Technol 9:3–1010.1002/(SICI)1099-1581(199801)9:1<3::AID-PAT727>3.0.CO;2-I ↗
21. Li J, Hunt JF, Cai Z, Zhou X (2013) Bending analyses for 3D engineered structural panels made from laminated paper and carbon fabric. Compos Part B Eng 53:17–2410.1016/j.compositesb.2013.04.041 ↗
22. Li J, Hunt JF, Gong S, Cai Z (2016) Simplified analytical model and balanced design approach for light-weight wood-based structural panel in bending. Compos Struct 136:16–2410.1016/j.compstruct.2015.09.045 ↗
23. Li J, Hunt JF, Gong S, Cai Z (2016) Fatigue behavior of wood-fiber-based tri-axial engineered sandwich composite panels (ESCP). Holzforschung 70:567–57510.1515/hf-2015-0091 ↗
24. Li J, Hunt JF, Gong S, Cai Z (2015) Testing and evaluation of a slot and tab construction technique for light-weight wood-fiber-based structural panels under bending. J Test Eval 44:357–36610.1520/JTE20140270 ↗
25. Li J, Hunt JF, Gong S, Cai Z (2014) High strength wood-based sandwich panels reinforced with fiberglass and foam. BioResources 9:1898–1913
26. Saito T, Hirota M, Tamura N, Kimura S, Fukuzumi H, Heux L et al (2009) Individualization of nano-sized plant cellulose fibrils by direct surface carboxylation using TEMPO catalyst under neutral conditions. Biomacromolecules 10:1992–199610.1021/bm900414t ↗
27. Qing Y, Sabo R, Zhu J, Agarwal U, Cai Z, Wu Y (2013) A comparative study of cellulose nanofibrils disintegrated via multiple processing approaches. Carbohydr Polym 97:226–23410.1016/j.carbpol.2013.04.086 ↗
28. Standard A (2010) D695, 2010 standard test method for compressive properties of rigid plastics. ASTM International, West Conshohocken
29. Wei L, Liang S, McDonald AG (2015) Thermophysical properties and biodegradation behavior of green composites made from polyhydroxybutyrate and potato peel waste fermentation residue. Ind Crops Prod 69:91–10310.1016/j.indcrop.2015.02.011 ↗
30. Standard A (1998) D570-98: standard test method for water absorption of plastics. American Society for Testing and Materials, New York
31. Wei L, McDonald AG, Freitag C, Morrell JJ (2013) Effects of wood fiber esterification on properties, weatherability and biodurability of wood plastic composites. Polym Degrad Stab 98:1348–136110.1016/j.polymdegradstab.2013.03.027 ↗
32. Mueller S, Sapkota J, Nicharat A, Zimmermann T, Tingaut P, Weder C et al (2015) Influence of the nanofiber dimensions on the properties of nanocellulose/poly (vinyl alcohol) aerogels. J Appl Polym Sci 132:1310.1002/app.41740 ↗
33. Kumar A, Negi YS, Choudhary V, Bhardwaj NK (2014) Characterization of cellulose nanocrystals produced by acid-hydrolysis from sugarcane bagasse as agro-waste. J Mater Phys Chem 2:1–8
34. Soni B, Mahmoud B (2015) Chemical isolation and characterization of different cellulose nanofibers from cotton stalks. Carbohydr Polym 134:581–58910.1016/j.carbpol.2015.08.031 ↗
35. Xu X, Liu F, Jiang L, Zhu J, Haagenson D, Wiesenborn DP (2013) Cellulose nanocrystals vs. cellulose nanofibrils: a comparative study on their microstructures and effects as polymer reinforcing agents. ACS Appl Mater Interfaces 5:2999–300910.1021/am302624t ↗
36. Wan Y-J, Gong L-X, Tang L-C, Wu L-B, Jiang J-X (2014) Mechanical properties of epoxy composites filled with silane-functionalized graphene oxide. Compos Part A Appl Sci Manuf 64:79–8910.1016/j.compositesa.2014.04.023 ↗