Reaction of 316L stainless steel with a galvanizing bath
Source abstract
Abstract
Type 316L stainless steel (316L SS), commonly used as pot roll material, was tested in an industrial Zn–Al galvanizing bath, with an effective Al content of 0.2 wt.%. Samples welded to the supporting roll arms and sides of the sink roll experienced heavy dross buildup. Samples placed at locations away from the incoming strip generally experienced much less dross buildup. Dross particles within the buildup on samples attached to supporting roll arms were small in size but numerous while particles on samples welded to the sides of the sink roll were much larger. SEM-EDS analyses indicated that the buildup consisted of two layers. The inner layer was the product of the corrosive reaction of 316L SS with the bath metal, and the outer layer was formed by dross particles built up on the inner reaction layer. The intermetallic phase, which formed at the reaction front of the samples was the inhibition compound Fe2Al5 containing some Mo and Cr. The formation of this intermetallic layer provided a thermodynamically favourable base for the attachment and further buildup of suspended dross particles on the sample surfaces.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Aluminum Alloy Microstructure Properties · Metallurgy and Material Science · Corrosion Behavior and Inhibition
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (13)
Show source-provided references
1. Horstmann D (1961) Proceedings of the 6th international conference on ‘Hot Dip Galvanizing’. Interlaken, Switzerland, June 1961, pp 319–328
2. Nakagawa M, Sakai J, Ohkouchi T, Ohkoshi H (1996) Tetsu-to-Hagane 81(3):226–23110.2355/tetsutohagane1955.82.3_226 ↗
3. Brunnock MS, Jones RD, Jenkins GA, Llewellyn DT (1996) Ironmaking Steelmaking 23(2):171–176
4. Brunnock MS, Jones RD, Jenkins GA, Llewellyn DT (1996) Proc. Galvanizers Association. Chicago, IL, October 1996, pp 3–15
5. Nakagawa M, Sakai J, Ohkouchi T, Ohkoshi H (1995) Tetsu-to-Hagane 81(10):47–52 (English translation)10.2355/tetsutohagane1955.81.10_989 ↗
6. Gay B, Piccinin A, Dubois M (2001) Proc. Galvatech’01. Brussels, Belgium, June 2001, pp 262–269
7. Liu X, Barbero E, Irwin C, Sikka V, Hemrick J, Headrick W, Goodwin FE (2005) Proc. AISTech 2005. vol II, Charlotte, NC, May 9–12, 2005, pp 403–411
8. Zhang K (2005) ZCO-15-4 project report, ILZRO GAP Meetings. Charlotte, NC, May 2005
9. Dubois M (2005) Private communication, October 2005
10. Zhang K, Tang N-Y (2004) Mater Sci Technol 20:739–74610.1179/026708304225017300 ↗
11. Ajersch F, Ilinca F, Hetu J-F, Goodwin FE (2005) Can Metall Quart 44(3):369–37810.1179/cmq.2005.44.3.369 ↗
12. Metals Handbook (1990) vol 1, 10th edn, ASM International, Materials Park, OH, March 1990, pp 871–872
13. Tang N-Y, Adams GR (1993) The physical metallurgy of zinc coated steel. In: Marder AR (ed) The minerals, metals & materials society, pp 41–54