journal article·2024-05-28

Thermoelectric Preferred Orientation of (GeTe)0.962(Bi2Te3)0.038

Naor Madar, Yatir Sadia, Yaniv Gelbstein

Publisher page

Abstract

In an attempt to reduce our reliance on fossil fuels, associated with severe environmental effects, the current research is focused on the identification of the thermoelectric potential of p -type (GeTe) 1– x (Bi 2 Te 3 ) x alloys. The doping potential of GeTe was extended by the Bi 2 Te 3 donor dopant for an effective compensation of the high inherent hole concentration of GeTe toward thermoelectrically optimal values. In the current research, the effect of the preferred orientation of the (GeTe) 0.962 (Bi 2 Te 3 ) 0.038 alloy is studied. For this purpose, a (GeTe) 0.962 (Bi 2 Te 3 ) 0.038 ingot was synthesized by a rocking furnace melt, pulverized to a powder, and sieved to powder particle sizes of either smaller than 1 μm or smaller than 25 μm. It was found from X-ray diffraction after hot pressing that a rhombohedral structure was observed. Variations in the crystallographic structure were obtained depending on the pressing direction and the sizes of powder particles. Moreover, the percentage of preferred orientation decreases with reducing the powder particle size. Parallel to the pressing direction, a plate-like pattern in the ⟨HK0⟩ orientation was observed, compared to the vertical direction, exhibiting a preferred orientation toward ⟨00L⟩. The thermoelectric properties transverse to the hot-pressing direction showed lower electrical resistivity values and higher thermal conductivity values, compared to the hot-pressing direction. This is due to the nature of van der Waals, VDW, bonds which exist along the c -axis, while introducing bismuth telluride to GeTe. At the particle size range of <1 μm, a maximal thermoelectric figure of merit, ZT, of ∼2 was obtained at ∼440 °C, which is one of the highest ever reported for any p -type thermoelectric alloy.
Source: openalex_inverted_index · Quality: baseline

Research context

OpenAlex topics: Advanced Thermoelectric Materials and Devices · Chalcogenide Semiconductor Thin Films · Phase-change materials and chalcogenides

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

The Department of Materials Engineering, Ben-Gurion University of the Negev, Beer-Sheva 8410501, Israel

Nuclear Research Center of the Negev, NRCN, P.O. Box 9001, Beer-Sheva 84190, Israel

Funding

Israel Science Foundation

References (57)

Show source-provided references
1. Vining C. B. · 2005 · AI-1
2. 10.1016/j.intermet.2015.08.00910.1016/j.intermet.2015.08.009 ↗
3. 10.1007/s11664-014-3500-z10.1007/s11664-014-3500-z ↗
4. 10.1002/aenm.20180005610.1002/aenm.201800056 ↗
5. 10.1021/acsami.9b0939710.1021/acsami.9b09397 ↗
6. 10.1007/s11664-013-2930-310.1007/s11664-013-2930-3 ↗
7. 10.1039/C4CP02868F10.1039/C4CP02868F ↗
8. 10.1038/s41467-020-16913-210.1038/s41467-020-16913-2 ↗
9. 10.1038/nature1318410.1038/nature13184 ↗
10. 10.1038/s41563-021-01064-610.1038/s41563-021-01064-6 ↗
11. 10.1002/adma.20220372510.1002/adma.202203725 ↗
12. 10.1021/jacs.0c0771210.1021/jacs.0c07712 ↗
13. 10.1038/s41467-021-23569-z10.1038/s41467-021-23569-z ↗
14. 10.1002/adma.20170314810.1002/adma.201703148 ↗
15. 10.1016/j.joule.2018.04.02510.1016/j.joule.2018.04.025 ↗
16. 10.1038/nchem.95510.1038/nchem.955 ↗
17. 10.1002/aenm.20110075610.1002/aenm.201100756 ↗
18. 10.1002/aenm.20110077010.1002/aenm.201100770 ↗
19. 10.1016/j.physb.2005.03.02210.1016/j.physb.2005.03.022 ↗
20. 10.1007/s11664-010-1435-610.1007/s11664-010-1435-6 ↗
21. 10.1063/1.492845910.1063/1.4928459 ↗
22. 10.1039/C5TC01781E10.1039/C5TC01781E ↗
23. 10.1016/j.jallcom.2016.04.07210.1016/j.jallcom.2016.04.072 ↗
24. 10.1007/s11664-015-4003-210.1007/s11664-015-4003-2 ↗
25. 10.1007/s11664-014-3381-110.1007/s11664-014-3381-1 ↗
26. 10.1039/D0EE01349H10.1039/D0EE01349H ↗
27. 10.1016/j.mtphys.2023.10098610.1016/j.mtphys.2023.100986 ↗
28. 10.1126/sciadv.aar560610.1126/sciadv.aar5606 ↗
29. 10.1016/j.actamat.2012.11.02710.1016/j.actamat.2012.11.027 ↗
30. 10.1039/C5TC90161H10.1039/C5TC90161H ↗
31. 10.1016/j.joule.2019.08.01710.1016/j.joule.2019.08.017 ↗
32. Popescu M. A. · 200010.1007/0-306-47129-9 ↗
33. 10.1016/S0364-5916(99)00012-710.1016/S0364-5916(99)00012-7 ↗
34. 10.1063/1.502507010.1063/1.5025070 ↗
35. 10.1007/s40948-019-00134-z10.1007/s40948-019-00134-z ↗
36. 10.1002/aelm.20180090410.1002/aelm.201800904 ↗
37. 10.1007/BF0275792810.1007/BF02757928 ↗
38. 10.1063/1.495897310.1063/1.4958973 ↗
39. 10.1021/acs.nanolett.5b0075510.1021/acs.nanolett.5b00755 ↗
40. 10.1023/B:INMA.0000027590.43038.a810.1023/B:INMA.0000027590.43038.a8 ↗
41. 10.1103/PhysRevB.93.07511910.1103/PhysRevB.93.075119 ↗
42. 10.1002/adfm.20180661310.1002/adfm.201806613 ↗
43. 10.1039/c3ta12623d10.1039/c3ta12623d ↗
44. 10.1021/acsaem.9b0005710.1021/acsaem.9b00057 ↗
45. 10.1155/2014/28463410.1155/2014/284634 ↗
46. 10.1016/j.jallcom.2019.15174710.1016/j.jallcom.2019.151747 ↗
47. 10.1134/S207511331504022X10.1134/S207511331504022X ↗
48. 10.1134/S106378261707019310.1134/S1063782617070193 ↗
49. 10.1134/S106378261707020X10.1134/S106378261707020X ↗
50. 10.1016/j.jallcom.2022.16566310.1016/j.jallcom.2022.165663 ↗
51. 10.1107/S002188981300353110.1107/S0021889813003531 ↗
52. 10.1107/S002188980901372710.1107/S0021889809013727 ↗
53. 10.1016/j.physb.2007.02.06710.1016/j.physb.2007.02.067 ↗
54. 10.1002/adfm.20140047410.1002/adfm.201400474 ↗
55. 10.1021/acsami.9b1519810.1021/acsami.9b15198 ↗
56. 10.1016/S0025-5408(96)00149-310.1016/S0025-5408(96)00149-3 ↗
57. 10.1016/j.physb.2006.10.00110.1016/j.physb.2006.10.001 ↗