The processing optimization and property evaluations of HVOF Co-base alloy T800 coating
Source abstract
Abstract
Co-base alloy Tribaloy-800 (T800) powders were coated on Inconel718 (IN718) by high velocity oxygen fuel thermal spraying. The optimal coating process (OCP) was obtained via studying the surface properties of 16 coatings prepared by Taguchi program. Surface hardness and porosity were 560–630 Hv and 1.0–2.7%, respectively, strongly depending on spraying processes. The OCP of hardness was oxygen flow rate (FR) 38 FMR, hydrogen FR 75 FMR, and feed rate 30 g/min at spray distance 5 inch. The adhesion strength of T800 coating with substrate had a slight increase and the thermal shock resistance of T800 coating was improved greatly by introduction of bonding layer Ni–Cr. Friction and wear behaviors have been investigated by a reciprocating sliding test at both 25 °C and an elevated temperature 538 °C (1,000 °F). Both friction coefficients (FC) and wear traces of the coating were smaller than those of IN718 substrate at both 25 and 538 °C. FC and wear traces of IN718 and coating decreased with increasing the surface temperature due to the lubricant effect of cobalt oxides formed on the sliding surface. As a result, T800 coating was highly recommended as a durability improvement coating for the protection of sliding surface, such as high speed spindle.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: High-Temperature Coating Behaviors · Metal and Thin Film Mechanics · Advanced materials and composites
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (28)
Show source-provided references
1. Zhang S-H, Cho T-Y, Yoon J-H, Li M-X, Shum PW, Kwon S-C (2009) Mater Sci Eng B 162:12710.1016/j.mseb.2009.03.017 ↗
2. Kim KS, Baek NK, Yoon JH, Cho TY, Youn SJ, Oh SK, Hwang SY, Chun HG (2006) J Kor Inst Surf Eng 39–4:179
3. Zhang S-H, Cho T-Y, Yoon J-H, Fang W, Song K-O, Li M-X, Joo Y-K, Lee CG (2008) Mater Charact 59:141210.1016/j.matchar.2008.01.003 ↗
4. Sayman O, Sen F, Celik E, Arman Y (2009) Mater Des 30:77010.1016/j.matdes.2008.06.004 ↗
5. Matthews S, James B, Hyland M (2009) Surf Coat Technol 203:114410.1016/j.surfcoat.2008.10.008 ↗
6. Mahesh RA, Jayaganthan R, Prakash S (2009) J Alloys Compd 468:39210.1016/j.jallcom.2008.01.025 ↗
7. Ni HS, Liu XH, Chang XC, Hou WL, Liu W, Wang JQ (2009) J Alloys Compd 467:16310.1016/j.jallcom.2007.11.133 ↗
8. Souza RC, Voorwald HJC, Cioffi MOH (2008) Surf Coat Technol 203:19110.1016/j.surfcoat.2008.07.038 ↗
9. Cho TY, Yoon JH, Kim KS, Song KO, Joo YK, Fang W, Zhang SH, Youn SJ, Chun HG, Hwang SY (2008) Surf Coat Technol 202:555610.1016/j.surfcoat.2008.06.106 ↗
10. Bolelli G, Cannillo V, Lusvarghi L, Montorsi M, Mantini FP, Barletta M (2007) Wear 263:139710.1016/j.wear.2006.12.002 ↗
11. Bolelli G, Lusvarghi L, Giovanardi R (2008) Surf Coat Technol 202:479310.1016/j.surfcoat.2008.04.056 ↗
12. Kim H-J, Yoon B-H, Lee C-H (2003) Wear 254:40810.1016/S0043-1648(03)00186-8 ↗
13. Navas C, Cadenas M, Cuetos JM, de Damborenea J (2006) Wear 260:83810.1016/j.wear.2005.04.020 ↗
14. Sahraoui T, Feraoun HI, Fenineche N, Montavon G, Aourag H, Coddet C (2004) Mater Lett 58:243310.1016/j.matlet.2004.02.025 ↗
15. Zhang Y, Yang Z (2007) J Iron Steel Res Int 14:30
16. Yao MX, Wu JBC, Liu R (2005) Mater Sci Eng A 407:29910.1016/j.msea.2005.07.054 ↗
17. Przybylowicz J, Kusinski J (2000) Surf Coat Technol 125:1310.1016/S0257-8972(99)00563-0 ↗
18. Ishikawa Y, Kuroda S, Kawakita J, Sakamoto Y, Takaya M (2007) Surf Coat Technol 201:471810.1016/j.surfcoat.2006.10.007 ↗
19. Khameneh Asl Sh, Heydarzadeh Sohi M, Hokamotoa K, Uemurad M (2006) Wear 260:120310.1016/j.wear.2005.07.013 ↗
20. Davis JR (2004) Handbook of thermal spray technology. ASM Thermal Spray Society, USA, pp 1–10
21. Sartwell BD et al (2004) Validation of HVOF WC/Co thermal spray coatings as a replacement for hard chrome plating on aircraft landing gear. Naval Research Laboratory Report Number NRL/MR/6170-04-8762, pp 1–15
22. Sartwell BD, Legg K, Bodger B (1999) HVOF thermal spray coatings as an alternative to hard chrome plating on military and commercial aircraft, AESF/EPA. Conference for environmental excellence, 231, USA, pp 1–150
23. Cho TY, Yoon JH, Kim KS, Baek NK, Hwang SY, Youn SJ, Chun HG (2006) HVOF coating for the improvement of the performance and durability of military hardware components. In: 15th aero technology symposium. Logistics Command ROKAF
24. Li M, Christofides PD (2006) Chem Eng Sci 61:654010.1016/j.ces.2006.05.050 ↗
25. Cho TY, Yoon JH, Kim KS, Park BK, Youn SJ, Baek NK, Chun HG (2006) J Kor Cryst Growth Cryst Technol 16(3):121
26. Cho TY, Yoon JH, Kim KS, Baek NK, Song KO, Youn SJ, Hwang SY, Chun HG (2006) J Kor Inst Surf Eng 39–6:295
27. Massalski TG et al (1986) Am Soc Metals 1:600
28. Kim NJ (2003) Dictionary of metal engineering, Junyong, p 2031