Nanostructured thin palladium-silver membranes: Effects of grain size on gas permeation properties

Submicron-thick Pd-Ag alloy membranes, prepared on 4 nm pore γ-alumina support by magnetron sputter deposition, are nanocrystalline with a grain (crystallite) size of about 20 nm. The membranes show good selectivity for hydrogen over helium (about 4000 at 300°C). Hydrogen permeation is dominated by the surface reaction steps in 100–200°C with an activation energy of about 30 kJ/mol. Bulk diffusion resistance becomes important at higher temperatures (>200 °C). Grain size is the most critical parameter affecting the hydrogen permeance of the thin nanostructued Pd-Ag membranes. Increase in Pd-Ag grain size from about 20 to 60 nm results in a substantial improvement in hydrogen permeance with a higher apparent activation energy in 100–300°C. Grain growth appears to increase the hydrogen permeability in the bulk phase of the Pd-Ag membranes. Helium permeance through the grain boundary decreases with increasing temperature or hydrogen partial pressure due to grain expansion. Carbonation and the accompanied grain expansion have detrimental effects on the perm-selectivity of the Pd-Ag membranes.