Microstructural refinement and intermetallic strengthening in Zn–Mn alloys
Source abstract
Abstract
The influence of Mn addition on the microstructure, defect structure, intermetallic phase evolution, and mechanical performance of as-cast Zn-Mn alloys was systematically investigated across Mn compositions from 0 to 2.4 wt%. Field emission scanning electron microscopy (FESEM) and electron backscatter diffraction (EBSD) analyses revealed a monotonic reduction in average grain size from 626 ± 15 µm to 282 ± 7 µm at Mn2.4, accompanied by an increase in high-angle boundary (HAB) fraction from 58 to 75%. At low-Mn contents (0.4–0.8 wt%), refinement was governed primarily by solute drag and constitutional undercooling, with fine, discrete MnZn₁₃ precipitates providing moderate Zener pinning. When Mn addition above 1.0 wt%, lamellar polygonal MnZn₁₃ networks became prevalent, imposing stronger boundary mobility constraints and increasing lattice strain. Mechanical testing showed that Vickers hardness increased from 38.42 ± 4.33 HV to 51.24 ± 6.31 HV with Mn addition, corresponding to estimated yield strength and Young’s modulus increases from ~ 125 MPa and ~ 37.7 GPa to ~ 168 MPa and ~ 50.5 GPa, respectively. Hall–Petch analysis confirmed grain boundary strengthening as the primary hardening mechanism, supplemented by dislocation-based and particle strengthening at higher Mn levels. The results establish a clear processing microstructure property relationship in Zn-Mn alloys, highlighting low to moderate Mn additions as optimal for balancing strength, ductility, and corrosion resistance, while higher Mn levels maximize strength at the expense of potential galvanic stability.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Microstructure and mechanical properties · Electronic Packaging and Soldering Technologies · Aluminum Alloys Composites Properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (47)
Show source-provided references
1. Ding Y, Wen C, Hodgson P, Li Y (2014) Effects of alloying elements on the corrosion behavior and biocompatibility of biodegradable magnesium alloys: a review. J Mater Chem B 2:1912–1933. https://doi.org/10.1039/C3TB21746A10.1039/C3TB21746A ↗
2. Katarivas Levy G, Goldman J, Aghion E (2017) The prospects of zinc as a structural material for biodegradable implants—a review paper. Metals 7:402. https://doi.org/10.3390/met710040210.3390/met7100402 ↗
3. Antoniac I, Miculescu F, Cotrut C et al (2020) Controlling the degradation rate of biodegradable Mg–Zn-Mn alloys for orthopedic applications by electrophoretic deposition of hydroxyapatite coating. Materials 13:263. https://doi.org/10.3390/ma1302026310.3390/ma13020263 ↗
4. Liu J, Linsley CS, Su Y et al (2024) Nanoparticle-enabled Zn-0.1Mg alloy with long-term stability, refined degradation, and favorable biocompatibility for biodegradable implant devices. ACS Appl Mater Interfaces 16:50125–50138. https://doi.org/10.1021/acsami.4c0471410.1021/acsami.4c04714 ↗
5. Kafri A, Ovadia S, Goldman J et al (2018) The suitability of Zn–1.3%Fe alloy as a biodegradable implant material. Metals 8:153. https://doi.org/10.3390/met803015310.3390/met8030153 ↗
6. Nidadavolu E, Feyerabend F, Ebel T et al (2016) On the determination of magnesium degradation rates under physiological conditions. Materials (Basel) 9:627. https://doi.org/10.3390/ma908062710.3390/ma9080627 ↗
7. Chen Y, Zhang W, Maitz MF et al (2016) Comparative corrosion behavior of Zn with Fe and Mg in the course of immersion degradation in phosphate buffered saline. Corros Sci 111:541–555. https://doi.org/10.1016/j.corsci.2016.05.03910.1016/j.corsci.2016.05.039 ↗
8. Su Y, Fu J, Zhou J et al (2023) Blending with transition metals improves bioresorbable zinc as better medical implants. Bioact Mater 20:243–258. https://doi.org/10.1016/j.bioactmat.2022.05.03310.1016/j.bioactmat.2022.05.033 ↗
9. Bandekian S, Baghbaderani MZ, Drelich JW et al (2025) Additive manufacturing of zinc-based biomaterials: fabrication, performance and property evaluation. J Mater Res Technol 36:5484–5508. https://doi.org/10.1016/j.jmrt.2025.04.12710.1016/j.jmrt.2025.04.127 ↗
10. Waqas M, He D, Wu X et al (2023) Investigation on the preparation, microstructure, mechanical and degradation properties of laser additive manufactured Zn–Li–Mg alloy for bioresorbable application. J Mater Res Technol 26:8509–8526. https://doi.org/10.1016/j.jmrt.2023.09.16010.1016/j.jmrt.2023.09.160 ↗
11. Tang L, Chen H, Zhu X et al (2025) Enhancing mechanical and biodegradation properties of Zn-0.5Fe alloys through rotary forging. Materials 18:722. https://doi.org/10.3390/ma1803072210.3390/ma18030722 ↗
12. Liu S, Zhan H, Kent D et al (2022) Effect of Mg on dynamic recrystallization of Zn–Mg alloys during room-temperature compression. Mater Sci Eng A 830:142243. https://doi.org/10.1016/j.msea.2021.14224310.1016/j.msea.2021.142243 ↗
13. Shi L, Yan Y, Shao C et al (2024) The influence of yttrium and manganese additions on the degradation and biocompatibility of magnesium-zinc-based alloys: in vitro and in vivo studies. J Magnes Alloys 12:608–624. https://doi.org/10.1016/j.jma.2022.06.01010.1016/j.jma.2022.06.010 ↗
14. Cheng X, Lin Q, Jin H et al (2025) Effect of Mn content on the corrosion behavior and biocompatibility of biodegradable Zn-Mn alloys. Sci Rep 15:8958. https://doi.org/10.1038/s41598-025-93296-810.1038/s41598-025-93296-8 ↗
15. Ben Tzion-Mottye L, Ron T, Eliezer D, Aghion E (2022) The effect of Mn on the mechanical properties and in vitro behavior of biodegradable Zn-2%Fe alloy. Metals 12:1291. https://doi.org/10.3390/met1208129110.3390/met12081291 ↗
16. Mollaei N, Razavi SH, Aboutalebi MR, Fatemi SM (2023) Effect of Mn addition on the microstructure, mechanical, and corrosion properties of an extruded biodegradable Zn-0.2Mg alloy. J Mater Res Technol 22:1983–1998. https://doi.org/10.1016/j.jmrt.2022.12.04910.1016/j.jmrt.2022.12.049 ↗
17. Yang X, Bao W, Cai Z et al (2024) Enhanced mechanical performance and tailored degradation characteristics of rolled Zn-0.8Li-0.4Mn alloy. Mater Des 245:113259. https://doi.org/10.1016/j.matdes.2024.11325910.1016/j.matdes.2024.113259 ↗
18. Xiao C, Sun S, Meng D et al (2025) Effect of Mn on microstructures and properties of backward extruded Zn-0.5 Mg alloys. J Mater Res Technol 35:1546–1555. https://doi.org/10.1016/j.jmrt.2025.01.14810.1016/j.jmrt.2025.01.148 ↗
19. Lolov M, Djulgerov N, Gyurov S (2016) Study of the peculiarities of the Zn-Mn phase diagram and their effect on the superplastic behavior of fine-grained Zn-Mn alloys. J Mater Eng Perform 25:3838–3844. https://doi.org/10.1007/s11665-016-2184-310.1007/s11665-016-2184-3 ↗
20. Shi Z-Z, Yu J, Liu X-F (2018) Microalloyed Zn-Mn alloys: from extremely brittle to extraordinarily ductile at room temperature. Mater Des 144:343–352. https://doi.org/10.1016/j.matdes.2018.02.04910.1016/j.matdes.2018.02.049 ↗
21. Hu Y, Dong D, Wang X et al (2021) Synthesis and properties of Mg-Mn-Zn alloys for medical applications. Materials 14:1855. https://doi.org/10.3390/ma1408185510.3390/ma14081855 ↗
22. Tang Y, Huang S, Chen W et al (2025) Zn-Mn-Mg alloy with superior mechanical properties and antibacterial performance. Adv Compos Hybrid Mater 8:153. https://doi.org/10.1007/s42114-024-01071-610.1007/s42114-024-01071-6 ↗
23. Shi Z-Z, Yu J, Liu X-F (2018) Twinning in MnZn13 intermetallic compound with base-centered monoclinic structure in Zn-0.75Mn alloy. Mater Charact 137:9–13. https://doi.org/10.1016/j.matchar.2018.01.02110.1016/j.matchar.2018.01.021 ↗
24. Chan KF, Yaakob Y, Tanemura M, Yusop MZM (2025) Influence of Mn content on microhardness in Zn-Mn/CNF cubical cast alloys: a 3D topographical study. J Alloys Compd 1012:178486. https://doi.org/10.1016/j.jallcom.2025.17848610.1016/j.jallcom.2025.178486 ↗
25. Li Z, Wang L, Liu C et al (2023) Hall-petch strengthening by grain boundaries and annealing twin boundaries in non-equiatomic Ni2FeCr medium-entropy alloy. Metals (Basel) 13:134. https://doi.org/10.3390/met1301013410.3390/met13010134 ↗
26. Zhilyaev AP, Gálvez F, Sharafutdinov A, Pérez-Prado MT (2010) Influence of the high pressure torsion die geometry on the allotropic phase transformations in pure Zr. Mater Sci Eng A 527:3918–3928. https://doi.org/10.1016/j.msea.2010.02.06610.1016/j.msea.2010.02.066 ↗
27. Kapoor R, Kumar N, Mishra RS et al (2010) Influence of fraction of high angle boundaries on the mechanical behavior of an ultrafine grained Al–Mg alloy. Mater Sci Eng A 527:5246–5254. https://doi.org/10.1016/j.msea.2010.04.08610.1016/j.msea.2010.04.086 ↗
28. Sun J, Liu J, Chen Q et al (2022) Study of the effect of grain-boundary misorientation on slip transfer in magnesium alloy using a misorientation distribution map. Crystals 12:388. https://doi.org/10.3390/cryst1203038810.3390/cryst12030388 ↗
29. Rui S-S, Han Q-N, Wang X et al (2021) Correlations between two EBSD-based metrics kernel average misorientation and image quality on indicating dislocations of near-failure low alloy steels induced by tensile and cyclic deformations. Mater Today Commun 27:102445. https://doi.org/10.1016/j.mtcomm.2021.10244510.1016/j.mtcomm.2021.102445 ↗
30. Liu Z, Qiu D, Wang F et al (2016) Effect of grain refinement on tensile properties of cast zinc alloys. Metall Mater Trans A 47:830–841. https://doi.org/10.1007/s11661-015-3229-110.1007/s11661-015-3229-1 ↗
31. Wątroba M, Bednarczyk W, Kawałko J, Bała P (2021) Fine-tuning of mechanical properties in a Zn–Ag–Mg alloy via cold plastic deformation process and post-deformation annealing. Bioact Mater 6:3424–3436. https://doi.org/10.1016/j.bioactmat.2021.03.01710.1016/j.bioactmat.2021.03.017 ↗
32. Chen H, Zhou X, Li Q et al (2021) Dynamic compressive strength tests of corroded SFRC exposed to drying–wetting cycles with a 37 mm diameter SHPB. Materials (Basel) 14:2267. https://doi.org/10.3390/ma1409226710.3390/ma14092267 ↗
33. Bialorucki C, Subramanian G, Elsaadany M, Yildirim-Ayan E (2014) In situ osteoblast mineralization mediates post-injection mechanical properties of osteoconductive material. J Mech Behav Biomed Mater 38:143–153. https://doi.org/10.1016/j.jmbbm.2014.06.01810.1016/j.jmbbm.2014.06.018 ↗
34. Zhou Y, Wang J, Yang Y et al (2022) Laser additive manufacturing of zinc targeting for biomedical application. Int J Bioprint 8:501. https://doi.org/10.18063/ijb.v8i1.50110.18063/ijb.v8i1.501 ↗
35. Dong Z, Han C, Zhao Y et al (2024) Role of heterogenous microstructure and deformation behavior in achieving superior strength-ductility synergy in zinc fabricated via laser powder bed fusion. Int J Extrem Manuf 6:045003. https://doi.org/10.1088/2631-7990/ad392910.1088/2631-7990/ad3929 ↗
36. Shi Y, Xu W, Che H et al (2024) The effect of topological design on the degradation behavior of additively manufactured porous zinc alloy. NPJ Mater Degrad 8:42. https://doi.org/10.1038/s41529-024-00451-z10.1038/s41529-024-00451-z ↗
37. Zhao Q, Liu Z, Zheng T et al (2025) Substantial improvement of mechanical properties of Zn–Mg alloys to orthopedic implants via rotary swaging. Sci Rep 15:29942. https://doi.org/10.1038/s41598-025-15689-z10.1038/s41598-025-15689-z ↗
38. He F, Yang S, Cao J (2020) Effect of cold rolling and aging on the microstructure and mechanical properties of Ti-Nb-Zr alloy. J Mater Eng Perform 29:3411–3419. https://doi.org/10.1007/s11665-020-04810-010.1007/s11665-020-04810-0 ↗
39. Mostaed E, Sikora-Jasinska M, Drelich JW, Vedani M (2018) Zinc-based alloys for degradable vascular stent applications. Acta Biomater 71:1–23. https://doi.org/10.1016/j.actbio.2018.03.00510.1016/j.actbio.2018.03.005 ↗
40. Shi ZZ, Gao XX, Zhang HJ et al (2020) Design biodegradable Zn alloys: second phases and their significant influences on alloy properties. Bioact Mater 5:210–218. https://doi.org/10.1016/j.bioactmat.2020.02.01010.1016/j.bioactmat.2020.02.010 ↗
41. Calcagnotto M, Ponge D, Demir E, Raabe D (2010) Orientation gradients and geometrically necessary dislocations in ultrafine grained dual-phase steels studied by 2D and 3D EBSD. Mater Sci Eng A 527:2738–2746. https://doi.org/10.1016/j.msea.2010.01.00410.1016/j.msea.2010.01.004 ↗
42. Jiang X, Du P, Li M et al (2024) Investigating effects of element composition on the microstructure and mechanical properties of three types FeCrAl alloys through small punch test. Mater Des 238:112712. https://doi.org/10.1016/j.matdes.2024.11271210.1016/j.matdes.2024.112712 ↗
43. Hu GW, Zeng LC, Du H et al (2021) Combined effects of solute drag and Zener pinning on grain growth of a NiCoCr medium-entropy alloy. Intermetallics 136:107271. https://doi.org/10.1016/j.intermet.2021.10727110.1016/j.intermet.2021.107271 ↗
44. Fan X, Qu R, Zhang Z (2021) Relation between strength and hardness of high-entropy alloys. Acta Metallurgica Sinica (English Letters) 34:1461–1482. https://doi.org/10.1007/s40195-021-01252-y10.1007/s40195-021-01252-y ↗
45. Papenberg NP, Gneiger S, Uggowitzer PJ, Pogatscher S (2021) Lean wrought magnesium alloys. Materials 14:4282. https://doi.org/10.3390/ma1415428210.3390/ma14154282 ↗
46. Cho DH, Avey T, Kwon H et al (2025) A phase-based approach to optimizing the mechanical and corrosion properties of biodegradable Mg-Zn-Ca alloys. J Alloys Compd 1031:181127. https://doi.org/10.1016/j.jallcom.2025.18112710.1016/j.jallcom.2025.181127 ↗
47. Shuai C, Zhong S, Dong Z et al (2022) Peritectic-eutectic transformation of intermetallic in Zn alloy: effects of Mn on the microstructure, strength and ductility. Mater Charact 190:112054. https://doi.org/10.1016/j.matchar.2022.11205410.1016/j.matchar.2022.112054 ↗