Preparation of one-step organic anion-modified MgAl-LDH films under mild conditions for Mg alloy corrosion protection
Source abstract
Abstract
The chelator-assisted method is considered to be an effective strategy for the in-situ growth of layered double hydroxide (LDH) films on magnesium alloy at atmospheric pressure. In this study, two organic anions, 2-Mercaptobenzothiazole (MBT) and sodium dodecyl benzene sulfonate (SDBS), were introduced separately during the synthesis of LDH films by chelator-assisted method to complete the organic modification of LDH films. The results demonstrated that the two organic anions promoted the growth of LDH in distinct forms. MBT could form an insoluble organic complex layer on the surface of LDH films, thereby enhancing their structural stability. The long carbon chain structure of the SDBS anion was successfully inserted into the LDH interlayer, resulting in a self-sealing microstructure and enhancing hydrophobicity of the LDH films. Both anions achieved by one-step preparation of organically modified LDH films on AZ31B magnesium alloy. The electrochemical test results showed that the modified LDH films had higher impedance modulus in the low-frequency region (|Z|LDH-SDBS (1.15 × 106 Ω cm2) >|Z|LDH-MBT (8.58 × 105 Ω cm2) >|Z|MgAl-LDH (4.09 × 105 Ω cm2)), which improved the corrosion resistance of the LDH films.
Source: expertdata · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Layered Double Hydroxides Synthesis and Applications · Magnesium Oxide Properties and Applications · Magnesium Alloys: Properties and Applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (37)
Show source-provided references
1. Saranya K, Bhuvaneswari S, Chatterjee S et al (2020) Biocompatible gadolinium-coated magnesium alloy for biomedical applications. J Mater Sci 55:11582–11596. https://doi.org/10.1007/s10853-020-04742-z10.1007/s10853-020-04742-z ↗
2. Arruebarrena G, Hurtado I, Väinölä J et al (2007) Development of investment-casting process of Mg-alloys for aerospace applications. Adv Eng Mater 9:751–756. https://doi.org/10.1002/adem.20070015410.1002/adem.200700154 ↗
3. Wang Q, Zhang Z, Zhang X, Li G (2010) New extrusion process of Mg alloy automobile wheels. Trans Nonferrous Metals Soc China 20:s599–s603. https://doi.org/10.1016/S1003-6326(10)60546-810.1016/S1003-6326(10)60546-8 ↗
4. Rocca E, Juers C, Steinmetz J (2010) Corrosion behaviour of chemical conversion treatments on as-cast Mg–Al alloys: electrochemical and non-electrochemical methods. Corros Sci 52:2172–2178. https://doi.org/10.1016/j.corsci.2010.02.03610.1016/j.corsci.2010.02.036 ↗
5. Moon S, Nam Y (2012) Anodic oxidation of Mg–Sn alloys in alkaline solutions. Corros Sci 65:494–501. https://doi.org/10.1016/j.corsci.2012.08.05010.1016/j.corsci.2012.08.050 ↗
6. Lin Z, Wang T, Yu X et al (2021) Functionalization treatment of micro-arc oxidation coatings on magnesium alloys: a review. J Alloy Compd 879:160453. https://doi.org/10.1016/j.jallcom.2021.16045310.1016/j.jallcom.2021.160453 ↗
7. Shi Y, Qi M, Chen Y, Shi P (2011) MAO-DCPD composite coating on Mg alloy for degradable implant applications. Mater Lett 65:2201–2204. https://doi.org/10.1016/j.matlet.2011.04.03710.1016/j.matlet.2011.04.037 ↗
8. Wu H, Zhang L, Zhang Y et al (2020) Corrosion behavior of Mg–Al LDH film in-situ assembled with graphene on Mg alloy pre-sprayed Al layer. J Alloy Compd 834:155107. https://doi.org/10.1016/j.jallcom.2020.15510710.1016/j.jallcom.2020.155107 ↗
9. Wang DY, Costa FR, Vyalikh A et al (2009) One-step synthesis of organic ldh and its comparison with regeneration and anion exchange method. Chem Mater 21:4490–4497. https://doi.org/10.1021/cm901238a10.1021/cm901238a ↗
10. Wen T, Yan R, Wang N et al (2020) PPA-containing layered double hydroxide (LDH) films for corrosion protection of a magnesium alloy. Surf Coat Technol 383:125255. https://doi.org/10.1016/j.surfcoat.2019.12525510.1016/j.surfcoat.2019.125255 ↗
11. Zhang D, Peng F, Tan J, Liu X (2019) In-situ growth of layered double hydroxide films on biomedical magnesium alloy by transforming metal oxyhydroxide. Appl Surf Sci 496:143690. https://doi.org/10.1016/j.apsusc.2019.14369010.1016/j.apsusc.2019.143690 ↗
12. Iqbal MA, Fedel M (2018) The effect of the surface morphologies on the corrosion resistance of in situ growth MgAl-LDH based conversion film on AA6082. Surf Coat Technol 352:166–174. https://doi.org/10.1016/j.surfcoat.2018.08.00610.1016/j.surfcoat.2018.08.006 ↗
13. Shulha TN, Serdechnova M, Lamaka SV et al (2018) Chelating agent-assisted in situ LDH growth on the surface of magnesium alloy. Sci Rep 8:16409. https://doi.org/10.1038/s41598-018-34751-710.1038/s41598-018-34751-7 ↗
14. Petrova E, Serdechnova M, Shulha T et al (2020) Use of synergistic mixture of chelating agents for in situ LDH growth on the surface of PEO-treated AZ91. Sci Rep 10:8645. https://doi.org/10.1038/s41598-020-65396-010.1038/s41598-020-65396-0 ↗
15. Anjum MJ, Zhao JM, Asl VZ et al (2021) Green corrosion inhibitors intercalated Mg: Al layered double hydroxide coatings to protect Mg alloy. Rare Met 40:2254–2265. https://doi.org/10.1007/s12598-020-01538-710.1007/s12598-020-01538-7 ↗
16. Anjum MJ, Zhao J, Zahedi AV et al (2019) In-situ intercalation of 8-hydroxyquinoline in Mg–Al LDH coating to improve the corrosion resistance of AZ31. Corros Sci 157:1–10. https://doi.org/10.1016/j.corsci.2019.05.02210.1016/j.corsci.2019.05.022 ↗
17. Dong Y, Wang F, Zhou Q (2014) Protective behaviors of 2-mercaptobenzothiazole intercalated Zn–Al-layered double hydroxide coating. J Coat Technol Res 11:793–803. https://doi.org/10.1007/s11998-014-9568-910.1007/s11998-014-9568-9 ↗
18. Wang Y, Zhang D (2012) Synthesis, characterization, and controlled release antibacterial behavior of antibiotic intercalated Mg-Al layered double hydroxides. Mater Res Bull 47:3185–3194. https://doi.org/10.1016/j.materresbull.2012.08.02910.1016/j.materresbull.2012.08.029 ↗
19. Zhang Y, Liu J, Li Y et al (2015) Fabrication of inhibitor anion-intercalated layered double hydroxide host films on aluminum alloy 2024 and their anticorrosion properties. J Coat Technol Res 12:293–302. https://doi.org/10.1007/s11998-014-9644-110.1007/s11998-014-9644-1 ↗
20. Trikeriotis M, Ghanotakis DF (2007) Intercalation of hydrophilic and hydrophobic antibiotics in layered double hydroxides. Int J Pharm 332:176–184. https://doi.org/10.1016/j.ijpharm.2006.09.03110.1016/j.ijpharm.2006.09.031 ↗
21. Morlat-Thérias S, Mousty C, Palvadeau P et al (1999) Concomitant intercalation and decomplexation of ferrocene sulfonates in layered double hydroxides. J Solid State Chem 144:143–151. https://doi.org/10.1006/jssc.1999.813410.1006/jssc.1999.8134 ↗
22. Xu ZP, Braterman PS (2007) Competitive intercalation of sulfonates into layered double hydroxides (LDHs): the Key Role of hydrophobic interactions. J Phys Chem C 111:4021–4026. https://doi.org/10.1021/jp068372310.1021/jp0683723 ↗
23. Dai X, Wu L, Xia Y et al (2021) Intercalation of Y in Mg–Al layered double hydroxide films on anodized AZ31 and Mg–Y alloys to influence corrosion protective performance. Appl Surf Sci 551:149432. https://doi.org/10.1016/j.apsusc.2021.14943210.1016/j.apsusc.2021.149432 ↗
24. Zahedi AV, Zhao J, Anjum MJ et al (2020) The effect of cerium cation on the microstructure and anti-corrosion performance of LDH conversion coatings on AZ31 magnesium alloy. J Alloy Compd 821:153248. https://doi.org/10.1016/j.jallcom.2019.15324810.1016/j.jallcom.2019.153248 ↗
25. Hu T, Ouyang Y, Xie ZH, Wu L (2021) One-pot scalable in situ growth of highly corrosion-resistant MgAl-LDH/MBT composite coating on magnesium alloy under mild conditions. J Mater Sci Technol 92:225–235. https://doi.org/10.1016/j.jmst.2021.03.02110.1016/j.jmst.2021.03.021 ↗
26. Purohit PJ, Huacuja-Sánchez JE, Wang DY et al (2011) Structure-property relationships of nanocomposites based on polypropylene and layered double hydroxides. Macromolecules 44:4342–4354. https://doi.org/10.1021/ma200323k10.1021/ma200323k ↗
27. Serdechnova M, Salak AN, Barbosa FS et al (2016) Interlayer intercalation and arrangement of 2-mercaptobenzothiazolate and 1,2,3-benzotriazolate anions in layered double hydroxides: In situ X-ray diffraction study. J Solid State Chem 233:158–165. https://doi.org/10.1016/j.jssc.2015.10.02310.1016/j.jssc.2015.10.023 ↗
28. Zhang K, Yarmolenko MA, Rogachev AA et al (2013) Formation of complex bis(β-mercaptobenzothiazole)-zinc(II) films by pulsed laser deposition. Appl Surf Sci 273:836–840. https://doi.org/10.1016/j.apsusc.2013.02.02810.1016/j.apsusc.2013.02.028 ↗
29. Zhang G, Wu T, Li Y et al (2012) Sorption of humic acid to organo layered double hydroxides in aqueous solution. Chem Eng J 191:306–313. https://doi.org/10.1016/j.cej.2012.03.02010.1016/j.cej.2012.03.020 ↗
30. Wu L, Ding X, Zheng Z et al (2021) Doublely-doped Mg–Al–Ce-V2O74-LDH composite film on magnesium alloy AZ31 for anticorrosion. J Mater Sci Technol 64:66–72. https://doi.org/10.1016/j.jmst.2019.09.03110.1016/j.jmst.2019.09.031 ↗
31. Önkal-Engin G, Wibulswas R, White DA (2000) Humic acid uptake from aqueous media using hydrotalcites and modified montmorillonite. Environ Technol 21:167–175. https://doi.org/10.1080/09593330.2000.961889710.1080/09593330.2000.9618897 ↗
32. Li Y, Gao B, Wu T et al (2009) Adsorption properties of aluminum magnesium mixed hydroxide for the model anionic dye reactive brilliant red K-2BP. J Hazard Mater 164:1098–1104. https://doi.org/10.1016/j.jhazmat.2008.09.00910.1016/j.jhazmat.2008.09.009 ↗
33. Kameda T, Tsuchiya Y, Yamazaki T, Yoshioka T (2009) Preparation of Mg–Al layered double hydroxides intercalated with alkyl sulfates and investigation of their capacity to take up N, N-dimethylaniline from aqueous solutions. Solid State Sci 11:2060–2064. https://doi.org/10.1016/j.solidstatesciences.2009.09.00810.1016/j.solidstatesciences.2009.09.008 ↗
34. Dou Z, Zhang Y, Shulha T et al (2022) Insight into chelating agent stimulated in-situ growth of MgAl-LDH films on magnesium alloy AZ31: The effect of initial cationic concentrations. Surf Coat Technol 439:128414. https://doi.org/10.1016/j.surfcoat.2022.12841410.1016/j.surfcoat.2022.128414 ↗
35. Chávez J, Jimenez O, Diaz-Luna J et al (2021) Microstructure and corrosion characterization of a Ti–30Zr alloy with Ta additions processed by arc-melting for biomedical applications. Mater Lett 284:129041. https://doi.org/10.1016/j.matlet.2020.12904110.1016/j.matlet.2020.129041 ↗
36. Zhang Y, Chen F, Zhang Y et al (2021) Microstructure and corrosion resistance of duplex coatings deposited on TC17 alloys by MAO and HiPIMS. Mater Lett 303:130506. https://doi.org/10.1016/j.matlet.2021.13050610.1016/j.matlet.2021.130506 ↗
37. Kartsonakis IA, Balaskas AC, Kordas GC (2011) Influence of cerium molybdate containers on the corrosion performance of epoxy coated aluminium alloys 2024–T3. Corros Sci 53:3771–3779. https://doi.org/10.1016/j.corsci.2011.07.02610.1016/j.corsci.2011.07.026 ↗