The influence of Gd content on the microstructure, mechanical properties, corrosion behavior and corrosion film deposition mechanisms of as-extruded Mg–Zn–Mn–Sr–Gd alloys for biomedical applications
Source abstract
Abstract
The microstructure, corrosion behavior and corrosive film formation of as-extruded Mg–2Zn–0.4Mn–0.1Sr–xGd alloys (x = 0, 0.5, 1 and 2 wt%) in Hank’s solution were studied. Microstructure was investigated by scanning electron microscopy (SEM), scanning Kelvin probe force microscopy (SKPFM), X-ray photoelectron spectroscopy (XPS). Corrosion behavior was evaluated by immersion and electrochemical tests. The microstructural observations indicated that the addition of 0.5–2 wt% Gd led to the formation of Mg3Zn3Gd2 phase and grain refinement. SKPFM results showed that the Gd-rich (Mg3Zn3Gd2) phase was nobler than the α-Mg matrix in Gd-containing alloys and formed micro-galvanic corrosion. The alloy with 0.5–1 wt% Gd addition had better corrosion resistance and displayed uniform corrosion behavior than that Gd-free alloy. However, excessive Gd addition (2 wt%) decreased the corrosion rate and caused severe localized corrosion due to massive cathode Gd-rich particles. Combined with mechanical properties and corrosion resistance, the alloy with 1 wt% Gd exhibited a potential for degradable implant applications. The obtained superior corrosion resistance was due to the refined microstructure and the compactness of Gd-containing corrosion products film. In addition, a systematic discussion of corrosion behavior and corrosion film formation was provided by means of schematic illustration.
Source: expertdata · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Magnesium Alloys: Properties and Applications · Aluminum Alloys Composites Properties · Corrosion Behavior and Inhibition
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (62)
Show source-provided references
1. Liu Y, Zheng Y, Chen XH, Yang JA, Pan H, Chen D, Wang L, Zhang J, Zhu D, Wu S (2019) Fundamental theory of biodegradable metals—definition, criteria, and design. Adv Funct Mater 29(18):180540210.1002/adfm.201805402 ↗
2. Kiani F, Wen C, Li Y (2020) Prospects and strategies for magnesium alloys as biodegradable implants from crystalline to bulk metallic glasses and composites a—review—sciencedirect. Acta Biomater 103:1–2310.1016/j.actbio.2019.12.023 ↗
3. Chen K, Lu Y, Tang HY, Gao YM, Zhao F (2020) Effect of strain on degradation behaviors of WE43, Fe and Zn wires. Acta Biomater 113:627–64510.1016/j.actbio.2020.06.028 ↗
4. Li Tao, Wang SF, Liu HT, Wu JH, Tang SQ (2021) Improved corrosion resistance of Mg alloy by a green phosphating: insights into pre-activation, temperature, and growth mechanism J Mater Sci 56:828–843.10.1007/s10853-020-05288-w ↗
5. Chen K, Xie X, Tang H, Sun H, Fan Y (2020) In vitro and in vivo degradation behavior of Mg–2Sr–Ca and Mg–2Sr–Zn alloys. Bioactive Mater 5(2):275–28510.1016/j.bioactmat.2020.02.014 ↗
6. Bakhsheshi-Rad HR, Majid A, Esah H (2016) Modelling corrosion rate of biodegradable magnesium-based alloys: The case study of Mg-Zn-RE-xCa (x = 0, 0.5, 1.5, 3 and 6 wt%) alloys. J Alloys Compd 687:630–64210.1016/j.jallcom.2016.06.149 ↗
7. Pulido-González N, Torres B, García-Rodríguez S, Rodrigo P, Bonache V (2020) Mg–1Zn–1Ca alloy for biomedical applications. Influence of the secondary phases on the mechanical and corrosion behavior. J Alloys Compd 831:15473510.1016/j.jallcom.2020.154735 ↗
8. Pulido-González N, Torres B, Rodrigo P, Hort N (2020) Microstructural, mechanical and corrosion characterization of an as-cast Mg–3Zn–0.4Ca alloy for biomedical applications. J Magnes Alloys 8:510–52210.1016/j.jma.2020.02.007 ↗
9. Bakhsheshi-Rad HR, Idris MH, Abdul-Kadir MR, Ourdjini A (2014) Mechanical and bio-corrosion properties of quaternary Mg–Ca–Mn–Zn alloys compared with binary Mg–Ca alloys. Mater Des 53(1):283–29210.1016/j.matdes.2013.06.055 ↗
10. Chen J, Tan L, Yu X (2018) Effect of minor content of Gd on the mechanical and degradable properties of as-cast Mg–2Zn–xGd–0.5Zr alloys. J Mater Sci Technol 35:503–51110.1016/j.jmst.2018.10.022 ↗
11. Huai Y, Fang BY, Shi H, Harishchandra S (2021) Microstructures, mechanical properties and degradation behavior of as-extruded Mg-1.8Zn-0.5Zr-xGd (0 ≤ x 2.5 ≤ wt%) biodegradable alloys. J Mater Sci 56:11137–1115310.1007/s10853-021-05982-3 ↗
12. Du B, Hu Z, Wang J, Sheng L (2020) Effect of extrusion process on the mechanical and in vitro degradation performance of a biomedical Mg–Zn–Y–Nd alloy. Bioactive Mater 5(2):219–22710.1016/j.bioactmat.2020.02.002 ↗
13. Li T, He Y, Wu J, Zhou J, Tang S, Yang Y, Wang X (2018) Effects of scandium addition on the in vitro degradation behavior of biodegradable Mg–1.5Zn–0.6Zr alloy. J Mater Sci 53:14075–1408610.1007/s10853-018-2626-4 ↗
14. Liu J, Lin Y, Bian D, Wang M, Lin Z (2019) In vitro and in vivo studies of Mg–30Sc alloys with different phase structure for potential usage within bone. Acta Biomater 98:50–6610.1016/j.actbio.2019.03.009 ↗
15. Song Y, Han E-H, Shan D, Yim CD, You BS (2012) The effect of Zn concentration on the corrosion behavior of Mg–xZn alloys. Corros Sci 65:322–33010.1016/j.corsci.2012.08.037 ↗
16. Bornapour M, Celikin M, Pekguleryuz M (2015) Thermal exposure effects on the in vitro degradation and mechanical properties of Mg–Sr and Mg–Ca–Sr biodegradable implant alloys and the role of the microstructure. Mater Sci Eng C 46:16–2410.1016/j.msec.2014.10.008 ↗
17. Liu JN, Bian D, Zheng YF, Chu X, Lin YL, Wang M, Lin ZF, Li M, Zhang Y, Guan SK (2020) Comparative in vitro study on binary Mg–RE (Sc, Y, La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb and Lu) alloy systems. Acta Biomater 102:508–52810.1016/j.actbio.2019.11.013 ↗
18. Kubásek J, Minárik P, Hosová K, Šašek S, Knapek M, Veselý J (2021) Novel magnesium alloy containing Y, Gd and Ca with enhanced ignition temperature and mechanical properties for aviation applications. J Alloys Compd 877:16008910.1016/j.jallcom.2021.160089 ↗
19. Kubásek J, Vojtěch D (2013) Structural and corrosion characterization of biodegradable Mg–RE (RE = Gd, Y, Nd) alloys. Trans Nonferrous Metals Soc China 23(5):1215–122510.1016/S1003-6326(13)62586-8 ↗
20. Yin Z, He R, Chen Y, Yin Z, Yan K (2021) Effects of surface micro–galvanic corrosion and corrosive film on the corrosion resistance of AZ91–xNd alloys. Appl Surf Sci 536:14776110.1016/j.apsusc.2020.147761 ↗
21. Leleu S, Rives B, Bour J, Causse N, Pébère N (2018) On the stability of the oxides film formed on a magnesium alloy containing rare–earth elements. Electrochim Acta 290:586–59410.1016/j.electacta.2018.08.093 ↗
22. GuangMei S (2006) Corrosion and protection of magnesium alloys. Chemical Industry Press, Beijing (in Chinese)
23. Yin Z, Chen Y, Yan H, Zhou GH, Wu XQ (2019) Effects of the second phases on corrosion resistance of AZ91–xGd alloys treated with ultrasonic vibration. J Alloys Compd 783:877–88510.1016/j.jallcom.2019.01.002 ↗
24. Miao HW, Huang H, Shi YG (2017) Effects of solution treatment before extrusion on the microstructure, mechanical properties and corrosion of Mg–Zn–Gd alloy in vitro. Corros Sci 122:90–9910.1016/j.corsci.2017.01.001 ↗
25. Gui Z, Kang Z, Li Y (2019) Corrosion mechanism of the as–cast and as–extruded biodegradable Mg–3.0Gd–2.7Zn–0.4Zr–0.1Mn alloys. Mater Sci Eng C 96:831–84010.1016/j.msec.2018.11.037 ↗
26. Tang HY, Wang F, Li D, Gu XN (2020) Mechanical properties, degradation behaviors and biocompatibility of micro–alloyed Mg–Sr–RE alloys for stent applications. Mater Lett 264:12728510.1016/j.matlet.2019.127285 ↗
27. Ratzinger G, Agrawal P, Körner W, Lonkai J, Sanders HM, Terreno HF (2010) Surface modification of PLGA nanospheres with Gd–DTPA and Gd–DOTA for high-relaxivity MRI contrast agents. Biomaterials 31:8716–872310.1016/j.biomaterials.2010.07.095 ↗
28. Cai C, Song R, Wang L (2018) Surface corrosion behavior and reaction product film deposition mechanism of Mg–Zn–Zr–Nd alloys during degradation process in Hank’s solution. Surf Coat Technol 342:57–6810.1016/j.surfcoat.2018.02.085 ↗
29. Xin Y, Hu T, Chu PK (2011) In vitro studies of biomedical magnesium alloys in a simulated physiological environment: a review. Acta Biomater 7(4):1452–145910.1016/j.actbio.2010.12.004 ↗
30. Liu LJ, Meng Y, Dong CF, Yan Yu (2018) Initial formation of corrosion products on pure zinc in simulated body fluid. J Mater Sci Technol 34(12):2271–228210.1016/j.jmst.2018.05.005 ↗
31. A. NACE, ASTMG31-12a (2012) Standard guide for laboratory immersion corrosion testing of metals. ASTM International, West Conshohocken, PA
32. Li T, He Y, Zhou J, Tang S, Yang Y, Wang X (2018) Influence of albumin on in vitro degradation behavior of biodegradable Mg–1.5Zn–0.6Zr–0.2Sc alloy. Mater Lett 217:227–23010.1016/j.matlet.2018.01.082 ↗
33. Liu LJ, Yao M, AlexA V (2019) Influences of albumin on in vitro corrosion of pure zn in artificial plasma. Corros Sci 153:341–35610.1016/j.corsci.2019.04.003 ↗
34. Liu Y, Wen JB, He JG, Li H (2020) Enhanced mechanical properties and corrosion resistance of biodegradable Mg–Zn–Zr–Gd alloy by Y microalloying. J Mater Sci 55:1813–182510.1007/s10853-019-04026-1 ↗
35. Li X, Li X, Ye Y, Zhang R, Tang G (2019) Deformation mechanisms and recrystallization behavior of Mg–3Al–1Zn and Mg–1Gd alloys deformed by electroplastic–asymmetric rolling. Mater Sci Eng A 742:722–73310.1016/j.msea.2018.09.041 ↗
36. Humphreys FJ (1977) The nucleation of recrystallization at second phase particles in deformed aluminium. Acta Metall 25(11):1323–134410.1016/0001-6160(77)90109-2 ↗
37. Wang J, Zhang YN, Hudon P (2015) Experimental study of the crystal structure of the Mg15–xZn–xSr3 ternary solid solution in the Mg–Zn–Sr system at 300°C. Mater Des 86:305–31210.1016/j.matdes.2015.07.038 ↗
38. Cheng M, Chen J, Yan H, Su B, Yu Z, Xia W, Gong X (2017) Effects of minor Sr addition on microstructure, mechanical and bio–corrosion properties of the Mg–5Zn based alloy system. J Alloys Compd 691:95–10210.1016/j.jallcom.2016.08.164 ↗
39. Pulido–González N, Torres B, Zheludkevich ML, Rams J (2020) High power diode laser (HPDL) surface treatments to improve the mechanical properties and the corrosion behaviour of Mg–Zn–Ca alloys for biodegradable implants. Surf Coat. Technol 402:12631410.1016/j.surfcoat.2020.126314 ↗
40. Yin SQ, Duan WC, Liu WH, Wu L (2020) Improving the corrosion resistance of MgZn1.2GdxZr0.18 (x = 0, 0.8, 1.4, 2.0) alloys via Gd additions. Corros Sci 177:10896210.1016/j.corsci.2020.108962 ↗
41. Tiyyagura HR, Petovar B, Matjaz F (2019) Degradation behaviour of Mg–4Ag and Mg–5Gd alloys underin–vitroconditions and different time–frames. J Alloys Compd 774:980–98710.1016/j.jallcom.2018.09.330 ↗
42. Jin Y, Blawert C, Yang H, Wiese B, Willumeit R (2020) Microstructure–corrosion behaviour relationship of micro–alloyed Mg–0.5Zn alloy with the addition of Ca, Sr, Ag, In and Cu. Mater Des 195:10898010.1016/j.matdes.2020.108980 ↗
43. Gomes MP, Costa I, Pébère N, Rossi JL, Tribollet B, Vivier V (2019) On the corrosion mechanism of Mg investigated by electrochemical impedance spectroscopy. Electrochim Acta 306:61–7010.1016/j.electacta.2019.03.080 ↗
44. Wang BJ, Xu DK, Dong JH, Ke W (2018) Effect of corrosion product films on the in vitro degradation behavior of Mg–3%Al–1%Zn (in wt%) alloy in Hank’s solution. J Mater Sci Technol 34:46–5410.1016/j.jmst.2018.02.013 ↗
45. Zeng RC, Sun L, Zheng YF, Cui HZ, Han EH (2014) Corrosion and characterisation of dual phase Mg–Li–Ca alloy in Hank’s solution: The influence of microstructural features. Corros Sci 79:69–8210.1016/j.corsci.2013.10.028 ↗
46. Zhou J, Fink M, Bruns M, Yang Y, Detsch R, Boccaccini AR, Ermert H, Virtanen S (2019) Modification of in vitro degradation behavior of pure iron with ultrasonication treatment: comparison of two different pseudo–physiological solutions. Mater Sci Eng C 95:275–28510.1016/j.msec.2018.10.079 ↗
47. Dong H, Lin F, Boccaccini AR (2021) Corrosion behavior of biodegradable metals in two different simulated physiological solutions: Comparison of Mg, Zn and Fe. Corros Sci 182:10927810.1016/j.corsci.2021.109278 ↗
48. Mei D, Lamaka SV, Feiler C, Zheludkevich ML (2019) The effect of small–molecule bio–relevant organic components at low concentration on the corrosion of commercially pure Mg and Mg–0.8Ca alloy: an overall perspective. Corros Sci 153:258–27110.1016/j.corsci.2019.03.039 ↗
49. Pan H, Pang K, Cui F, Ge F, Man C (2019) Effect of alloyed Sr on the microstructure and corrosion behavior of biodegradable Mg–Zn–Mn alloy in Hanks’ solution. Corros Sci 157:420–43710.1016/j.corsci.2019.06.022 ↗
50. Liu Y, Liu X, Zhang Z (2019) Comparative, real–time in situ monitoring of galvanic corrosion in Mg–Mg2Ca and Mg–MgZn2 couples in Hank's solution. Corros Sci 161:10818510.1016/j.corsci.2019.108185 ↗
51. CRC Press (2016) CRC handbook of chemistry and physics (97th eds.), CRC Press, Inc, Boca Raton, FL (2016).
52. Bahmani A, Arthanari S, Shin KS (2020) Formulation of corrosion rate of magnesium alloys using microstructural parameters. J Magnes Alloys 8:134–14910.1016/j.jma.2019.12.001 ↗
53. Argade GR, Kandasamy K, Panigrahi SK, Mishra RS (2012) Corrosion behavior of a friction stir processed rare–earth added magnesium alloy. Corros Sci 58:321–32610.1016/j.corsci.2012.01.007 ↗
54. Saikrishna N, Reddy GPK, Munirathinam B, Sunil BR (2016) Influence of bimodal grain size distribution on the corrosion behavior of friction stir processed biodegradable AZ31 magnesium alloy. J Magnes Alloys 4:68–7610.1016/j.jma.2015.12.004 ↗
55. Yin S, Duan W, Liu W (2019) Influence of specific second phases on corrosion behaviors of Mg–Zn–Gd–Zr alloys. Corros Sci. 166:10841910.1016/j.corsci.2019.108419 ↗
56. Li TF (2003) Oxidation of metals at high temperature and hot corrosion. Chemistry Industry Press, Beijing (in Chinese)
57. Liu J, Han E, Song Y (2018) Effect of twins on the corrosion behavior of Mg–5Y–7Gd–1Nd–0.5Zr Mg alloy. J Alloys Compd 757:356–36310.1016/j.jallcom.2018.05.105 ↗
58. Hort N, Huang Y, Fechner D (2010) Magnesium alloys as implant materials––principles of property design for Mg–RE alloys. Acta Biomater 6:1714–172510.1016/j.actbio.2009.09.010 ↗
59. Bao L, Zhang ZQ, Le QC, Zhang SRL, Cui JZ (2017) Corrosion behavior and mechanism of Mg–Y–Zn–Zr alloys with various Y/Zn mole ratios. J Alloys Compd 712:15–2310.1016/j.jallcom.2017.04.053 ↗
60. Zhang Y, Li JX, Li JY (2018) Microstructure, mechanical properties, corrosion behavior and film formation mechanism of Mg–Zn–Mn–xNd in Kokubo’s solution. J Alloys Compd 730:458–47010.1016/j.jallcom.2017.09.325 ↗
61. Hansen N (2004) Hall-Petch relation and boundary strengthening. Scr Mater 51(8):801–80610.1016/j.scriptamat.2004.06.002 ↗
62. Park SH, You BS (2015) Effect of homogenization temperature on the microstructure and mechanical properties of extruded Mg–7Sn–1Al–1Zn alloy. J Alloy Comp 637:332–33810.1016/j.jallcom.2015.03.030 ↗