Influence of grain size on the electrochemical behavior of pure copper
Source abstract
Abstract
Despite numerous research works a thorough understanding on how grain size influences the electrochemical behavior of metals is still lacking due to the inability to decouple grain size effects from other microstructural characteristics. In this work, the combination of potentiodynamic polarization measurements and the gold-nanoplating technique was used on high purity copper to further explore this relationship. The high purity copper was thermomechanically processed in such a way that three samples were produced with markedly different average grain sizes, namely 1.4, 48 and 191 µm. All other parameters influencing the electrochemical behavior, such as internal stresses and texture were kept constant; microstructural characterization was performed by electron backscatter diffraction. In 0.1 M HCl, the anodic polarization curves demonstrate that for the smaller the grain size a lower corrosion potential and higher corrosion current density is observed. The gold-nanoplating experiments show that the material with the smallest grain size is corroding more uniformly than the samples with the larger grain sizes. In the sample with the medium grain size, the higher electrochemical activity of the grain boundaries is demonstrated. In the largest grain size sample, both the grain boundaries as well as some of the grain interiors are covered with gold.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Microstructure and mechanical properties · Corrosion Behavior and Inhibition · Hydrogen embrittlement and corrosion behaviors in metals
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (38)
Show source-provided references
1. Ralston KD, Birbilis N (2010) Effect of grain size on corrosion: a review. Corrosion 66:075005-1–075005-1310.5006/1.3462912 ↗
2. Ralston KD, Birbilis N, Davies CHJ (2010) Revealing the relationship between grain size and corrosion rate of metals. Scr Mater 63:1201–120410.1016/j.scriptamat.2010.08.035 ↗
3. Hellmig RJ, Janecek M, Hadzima B et al (2008) A portrait of copper processed by equal channel angular pressing. Mater Trans 49:31–3710.2320/matertrans.ME200717 ↗
4. Yu B, Woo P, Erb U (2007) Corrosion behaviour of nanocrystalline copper foil in sodium hydroxide solution. Scr Mater 56:353–35610.1016/j.scriptamat.2006.11.007 ↗
5. Luo W, Qian C, Wu XJ, Yan M (2007) Electrochemical corrosion behavior of nanocrystalline copper bulk. Mater Sci Eng 452:524–52810.1016/j.msea.2006.10.123 ↗
6. Vinogradov A, Mimaki T, Hashimoto S, Valiev R (1999) On the corrosion behaviour of ultra-fine grain copper. Scr Mater 41:319–32610.1016/S1359-6462(99)00170-0 ↗
7. Barbucci A, Farne G, Matteazzi P, Riccieri R, Cerisola G (1999) Corrosion behaviour of nanocrystalline Cu90Ni10 alloy in neutral solution containing chlorides. Corros Sci 41:463–47510.1016/S0010-938X(98)00129-2 ↗
8. Wang YM, Chen MW, Zhou FH, Ma E (2002) High tensile ductility in a nanostructured metal. Nature 419:912–91510.1038/nature01133 ↗
9. Wang YM, Chen MW, Sheng HW, Ma E (2002) Nanocrystalline grain structures developed in commercial purity Cu by low-temperature cold rolling. J Mater Res 17:3004–300710.1557/JMR.2002.0436 ↗
10. Nikfahm A, Danaee I, Ashrafi A, Toroghinejad MR (2013) Effect of grain size changes on corrosion behavior of copper produced by accumulative roll bonding process. Mater Res 16:1379–138610.1590/S1516-14392013005000135 ↗
11. Tao S, Li DY (2006) Tribological, mechanical and electrochemical properties of nanocrystalline copper deposits produced by pulse electrodeposition. Nanotechnology 17:65–7810.1088/0957-4484/17/1/012 ↗
12. Yu JK, Han EH, Lu L, Wei XJ, Leung M (2005) Corrosion behaviors of nanocrystalline and conventional polycrystalline copper. J Mater Sci 40:1019–1022. doi: 10.1007/s10853-005-6524-110.1007/s10853-005-6524-1 ↗
13. Song GL, Atrens A, Dargusch M (1999) Influence of microstructure on the corrosion of diecast AZ91D. Corros Sci 41:249–27310.1016/S0010-938X(98)00121-8 ↗
14. Ambat R, Aung NN, Zhou W (2000) Evaluation of microstructural effects on corrosion behaviour of AZ91D magnesium alloy. Corros Sci 42:1433–145510.1016/S0010-938X(99)00143-2 ↗
15. Hoog CO, Birbilis N, Estrin Y (2008) Corrosion of pure Mg as a function of grain size and processing route. Adv Eng Mater 10:579–58210.1002/adem.200800046 ↗
16. Martinez-Lombardia E, Lapeire L, De Graeve I, Verbeken K, Kestens LAI, Terryn H (2015) Study of the influence of the microstructure on the corrosion properties of pure copper. Mater Corros. doi: 10.1002/maco.20150871910.1002/maco.201508719 ↗
17. Gaggiano R, Lombardia EM, De Graeve I et al (2012) Gold nanoplating as a new method for the quantification of the electrochemical activity of grain boundaries in polycrystalline metals. Electrochem Commun 24:97–9910.1016/j.elecom.2012.08.004 ↗
18. Lapeire L, Lombardia EM, Verbeken K, De Graeve I, Terryn H, Kestens LAI (2014) Structural dependence of gold deposition by nanoplating in polycrystalline copper. J Mater Sci 49:3909–3916. doi: 10.1007/s10853-013-7939-810.1007/s10853-013-7939-8 ↗
19. Garcia AL, Tikare V, Holm EA (2008) Three-dimensional simulation of grain growth in a thermal gradient with non-uniform grain boundary mobility. Scr Mater 59:661–66410.1016/j.scriptamat.2008.05.039 ↗
20. Liu H, Li N, Bi S, Li D (2007) Gold immersion deposition on electroless nickel substrates—deposition process and influence factor analysis. J Electrochem Soc 154:D662–D66810.1149/1.2790281 ↗
21. Lapeire L, Sidor J, Verleysen P et al (2015) Texture comparison between room temperature rolled and cryogenically rolled pure copper. Acta Mater 95:224–23510.1016/j.actamat.2015.05.035 ↗
22. Konkova TN, Mironov SY, Korznikov AV, Myshlyaev MM (2013) Formation of the microstructure in the course of low-temperature annealing of cryogenically deformed copper. Dokl Phys 58:240–24310.1134/S1028335813060062 ↗
23. Konkova T, Mironov S, Korznikov A, Semiatin SL (2010) Microstructural response of pure copper to cryogenic rolling. Acta Mater 58:5262–527310.1016/j.actamat.2010.05.056 ↗
24. Verbeken K, Kestens L (2003) Strain-induced selective growth in an ultra low carbon steel after a small rolling reduction. Acta Mater 51:1679–169010.1016/S1359-6454(02)00569-4 ↗
25. Palumbo G, Aust KT, Lehockey EM, Erb U, Lin P (1998) On a more restrictive geometric criterion for “special” CSL grain boundaries. Scr Mater 38:1685–169010.1016/S1359-6462(98)00077-3 ↗
26. Pourbaix M (1974) Atlas of electrochemical equilibria in aqueous solutions. National Association of Corrosion Engineers, Houston
27. Konkova T, Mironov S, Korznikov A, Semiatin SL (2011) On the room-temperature annealing of cryogenically rolled copper. Mater Sci Eng 528:7432–744310.1016/j.msea.2011.06.047 ↗
28. Dziaszyk S, Payton EJ, Friedel F, Marx V, Eggeler G (2010) On the characterization of recrystallized fraction using electron backscatter diffraction: a direct comparison to local hardness in an IF steel using nanoindentation. Mater Sci Eng 527:7854–786410.1016/j.msea.2010.08.063 ↗
29. Wang SY, Wang JQ (2014) Effect of grain orientation on the corrosion behavior of polycrystalline Alloy 690. Corros Sci 85:183–19210.1016/j.corsci.2014.04.014 ↗
30. Ashton RF, Hepworth MT (1968) Effect of crystal orientation on anodic polarization and passivity of zinc. Corrosion 24:50–5610.5006/0010-9312-24.2.50 ↗
31. Wiame F, Maurice V, Marcus P (2007) Initial stages of oxidation of Cu(111). Surf Sci 601:1193–120410.1016/j.susc.2006.12.028 ↗
32. Zhang DQ, Cai QR, He XM, Ga LX, Zhou GD (2008) Inhibition effect of some amino acids on copper corrosion in HCl solution. Mater Chem Phys 112:353–35810.1016/j.matchemphys.2008.05.060 ↗
33. Randle V (2004) Twinning-related grain boundary engineering. Acta Mater 52:4067–408110.1016/j.actamat.2004.05.031 ↗
34. Martinez-Lombardia E, Lapeire L, Maurice V et al (2014) In situ scanning tunneling microscopy study of the intergranular corrosion of copper. Electrochem Commun 41:1–410.1016/j.elecom.2014.01.007 ↗
35. Flewitt PEJ, Wild RK (2001) Grain boundaries: their microstructure and chemistry. Wiley, Chichester
36. Randle V (2001) The coincidence site lattice and the ‘sigma enigma’. Mater Charact 47:411–41610.1016/S1044-5803(02)00193-6 ↗
37. Martinez-Lombardia E, Gonzalez-Garcia Y, Lapeire L et al (2014) Scanning electrochemical microscopy to study the effect of crystallographic orientation on the electrochemical activity of pure copper. Electrochim Acta 116:89–9610.1016/j.electacta.2013.11.048 ↗
38. Schreiber A, Schultze JW, Lohrengel MM, Karman F, Kalman E (2006) Grain dependent electrochemical investigations on pure iron in acetate buffer pH 6.0. Electrochim Acta 51:2625–263010.1016/j.electacta.2005.07.052 ↗