High performance nano hydroxyapatite coating on zinc for biomedical applications
Source abstract
Abstract
Abstract Zinc and its alloys have been given promising consideration as a new biodegradable implant for use in the human body. Compact and uniform nano hydroxyapatite coatings containing chitosan were successfully deposited onto zinc substrate in an aqueous solution utilizing microwave-assisted process in about 10 min. The quick composite coatings are derived by microwave heating compared with the coatings derived by electrodeposition. The as-deposited coatings formed by electrodeposition synthesis were known as brushite, which was converted to hydroxyapatite after 1 h of immersion (post treated) in 1 M aqueous sodium hydroxide solutions at 100 °C. The incorporation of chitosan (from 0.01–0.05 g/l) into the coating composition results in a smooth and uniform coating structure. SEM, EDS, and an X-ray diffractometer were utilized to analyze coated samples' surfaces to evaluate their surface morphology, chemical composition, and crystalline structures. The in vitro degradation behavior of the composite-coated samples in simulated body fluid at pH 7.4 and 37 °C was evaluated using electrochemical impedance spectroscopy and potentiodynamic polarization. The outcomes showed that microwave-derived coatings provided superior corrosion resistance for zinc implants as compared to electrodeposited coatings. Furthermore, the use of chitosan in hydroxyapatite coatings increased electrochemical corrosion performance. Low chitosan concentrations (0.01–0.03 g/l) exhibit superior anti-corrosion properties than higher concentrations (0.05 g/l). Against Staphylococcus aureus, the coatings demonstrated strong antibacterial efficacy. These corrosion outcomes and the fruitful deposition of a hydroxyapatite/chitosan composite coating on zinc substrate indicate that the coating is efficient for the creation of new composite coatings for either functional implants or regenerative medicine. The resultant coating may be an excellent option for bone implants.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Bone Tissue Engineering Materials · Magnesium Alloys: Properties and Applications · Corrosion Behavior and Inhibition
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (72)
Show source-provided references
1. Meng Y, Liu L, Zhang D, Dong C, Yan Y, Volinsky AA, Wang L-N (2019) Initial formation of corrosion products on pure zinc in saline solution. Bioact mater 4:87–9610.1016/j.bioactmat.2018.08.003 ↗
2. Bowen PK, Drelich J, Goldman J (2013) Zinc exhibits ideal physiological corrosion behavior for bioabsorbable stents. Adv Mater 25:2577–258210.1002/adma.201300226 ↗
3. Purnama A, Hermawan H, Mantovani D (2014) Biodegradable metal stents: a focused review on materials and clinical studies. J Biomater Tissue Eng 4:868–87410.1166/jbt.2014.1263 ↗
4. Li H, Zheng Y, Qin L (2014) Progress of biodegradable metals. Prog Nat Sci Mater Int 24:414–42210.1016/j.pnsc.2014.08.014 ↗
5. Frederickson CJ, Koh J-Y, Bush AI (2005) The neurobiology of zinc in health and disease. Nat Rev Neurosci 6:449–46210.1038/nrn1671 ↗
6. Vojtěch D, Kubásek J, Šerák J, Novák P (2011) Mechanical and corrosion properties of newly developed biodegradable Zn-based alloys for bone fixation. Acta Biomater 7:3515–352210.1016/j.actbio.2011.05.008 ↗
7. Zhang S, Zhang X, Zhao C, Li J, Song Y, Xie C, Tao H, Zhang Y, He Y, Jiang Y (2010) Research on an Mg–Zn alloy as a degradable biomaterial. Acta Biomater 6:626–64010.1016/j.actbio.2009.06.028 ↗
8. Jain D, Pareek S, Agarwala A, Shrivastava R, Sassi W, Parida SK, Behera D (2021) Effect of exposure time on corrosion behavior of zinc-alloy in simulated body fluid solution: electrochemical and surface investigation. J Mater Res Technol 10:738–75110.1016/j.jmrt.2020.12.050 ↗
9. Murni N, Dambatta M, Yeap S, Froemming G, Hermawan H (2015) Cytotoxicity evaluation of biodegradable Zn–3Mg alloy toward normal human osteoblast cells. Mater Sci Eng C 49:560–56610.1016/j.msec.2015.01.056 ↗
10. Moravej M, Mantovani D (2011) Biodegradable metals for cardiovascular stent application: interests and new opportunities. Int J Mol Sci 12:4250–427010.3390/ijms12074250 ↗
11. Kuhlmann J, Bartsch I, Willbold E, Schuchardt S, Holz O, Hort N, Höche D, Heineman WR, Witte F (2013) Fast escape of hydrogen from gas cavities around corroding magnesium implants. Acta Biomater 9:8714–872110.1016/j.actbio.2012.10.008 ↗
12. Staiger MP, Pietak AM, Huadmai J, Dias G (2006) Magnesium and its alloys as orthopedic biomaterials: a review. Biomaterials 27:1728–173410.1016/j.biomaterials.2005.10.003 ↗
13. Chen J, Tan L, Yang K (2017) Effect of heat treatment on mechanical and biodegradable properties of an extruded ZK60 alloy. Bioact mater 2:19–2610.1016/j.bioactmat.2016.12.002 ↗
14. Schinhammer M, Hänzi AC, Löffler JF, Uggowitzer PJ (2010) Design strategy for biodegradable Fe-based alloys for medical applications. Acta Biomater 6:1705–171310.1016/j.actbio.2009.07.039 ↗
15. Schinhammer M (2012) Development and characterization of biodegradable Fe-based alloys for temporary medical applications, in, ETH Zurich, viii–xiii
16. Cheng J, Liu B, Wu Y, Zheng Y (2013) Comparative in vitro study on pure metals (Fe, Mn, Mg, Zn and W) as biodegradable metals. J Mater Sci Technol 29:619–62710.1016/j.jmst.2013.03.019 ↗
17. Yanovska G, Bolshanina SB, Kuznetsov V (2017) Formation of hydroxyapatite coatings with addition of chitosan from aqueous solutions by thermal substrate method. J eng sci, F1-F410.21272/jes.2017.4(2).f1 ↗
18. Furko M, Horváth ZE, Sulyok A, Kis VK, Balázsi K, Mihály J, Balázsi C (2021) Preparation and morphological investigation on bioactive ion-modified carbonated hydroxyapatite-biopolymer composite ceramics as coatings for orthopaedic implants. Ceram Int 48(1):760–76810.1016/j.ceramint.2021.09.156 ↗
19. Park KH, Kim S-J, Hwang M-J, Song H-J, Park Y-J (2017) Pulse electrodeposition of hydroxyapatite/chitosan coatings on titanium substrate for dental implant. Colloid Polym Sci 295:1843–184910.1007/s00396-017-4166-x ↗
20. Dorozhkin SV, Epple M (2002) Biological and medical significance of calcium phosphates. Angew Chem Int Ed 41:3130–314610.1002/1521-3773(20020902)41:17<3130::AID-ANIE3130>3.0.CO;2-1 ↗
21. Suzuki O, Imaizumi H, Kamakura S, Katagiri T (2008) Bone regeneration by synthetic octacalcium phosphate and its role in biological mineralization. Curr Med Chem 15:305–31310.2174/092986708783497283 ↗
22. Zhang F, Cai S, Xu G, Wang F, Yu N, Ling R, Wu X (2016) Preparation and bioactivity of apatite coating on Ti6Al4V alloy by microwave assisted aqueous chemical method. Ceram Int 42:18466–1847310.1016/j.ceramint.2016.08.182 ↗
23. Shoeib M (2004) Beschichtung von verbundwerkstoffen mit hydroxylapatit: anwendungen in der medizin-und biotechnologie. Galvanotechnik 95:1860–1867
24. kumar Balu S, Andra S, Jeevanandam J, Vidyavathy SM, Sampath V (2021) Emerging marine derived nanohydroxyapatite and their composites for implant and biomedical applications. J Mech Behav Biomed Mat 119:10452310.1016/j.jmbbm.2021.104523 ↗
25. Bartmański M, Pawłowski Ł, Belcarz A, Przekora A, Ginalska G, Strugała G, Cieślik BM, Pałubicka A, Zieliński A (2021) The chemical and biological properties of nanohydroxyapatite Coatings with antibacterial nanometals, obtained in the electrophoretic process on the Ti13Zr13Nb alloy. Int J Mol Sci 22:317210.3390/ijms22063172 ↗
26. Neacsu IA, Arsenie LV, Trusca R, Ardelean IL, Mihailescu N, Mihailescu IN, Ristoscu C, Bleotu C, Ficai A, Andronescu E (2019) Biomimetic collagen/Zn2+-Substituted calcium phosphate composite coatings on titanium substrates as prospective bioactive layer for implants: a comparative study spin coating vs. MAPLE. Nanomaterials 9:69210.3390/nano9050692 ↗
27. Kar A, Raja K, Misra M (2006) Electrodeposition of hydroxyapatite onto nanotubular TiO2 for implant applications. Surf Coat Technol 201:3723–373110.1016/j.surfcoat.2006.09.008 ↗
28. Yusoff MFM, Kasim NHA, Himratul-Aznita WH, Saidin S, Genasan K, Kamarul T, Radzi Z (2021) Physicochemical, antibacterial and biocompatibility assessments of silver incorporated nano-hydroxyapatite synthesized using a novel microwave-assisted wet precipitation technique. Mater Charact 178:11116910.1016/j.matchar.2021.111169 ↗
29. Hassan MN, Mahmoud MM, Abd El-Fattah A, Kandil S (2016) Microwave-assisted preparation of nano-hydroxyapatite for bone substitutes. Ceram Int 42:3725–374410.1016/j.ceramint.2015.11.044 ↗
30. Şimsek Y, Avci Ş (2019) Synthesis and characterization of hydroxyapatite produced by microwave assisted precipitation technique. Acta Phys Pol A 135:974–97610.12693/APhysPolA.135.974 ↗
31. Demirtaş TT, Kaynak G, Gümüşderelioğlu M (2015) Bone-like hydroxyapatite precipitated from 10× SBF-like solution by microwave irradiation. Mater Sci Eng C 49:713–71910.1016/j.msec.2015.01.057 ↗
32. Vandecandelaere N, Rey C, Drouet C (2012) Biomimetic apatite-based biomaterials: on the critical impact of synthesis and post-synthesis parameters. J Mater Sci Mater Med 23:2593–2606. https://doi.org/10.1007/s10856-012-4719-y10.1007/s10856-012-4719-y ↗
33. Sheikh Z, Najeeb S, Khurshid Z, Verma V, Rashid H, Glogauer M (2015) Biodegradable materials for bone repair and tissue engineering applications. Materials 8:5744–579410.3390/ma8095273 ↗
34. Bartmański M, Pawłowski Ł, Mielewczyk-Gryń A, Strugała G, Rokosz K, Gaiaschi S, Chapon P, Raaen S, Zieliński A (2021) The influence of nanometals, dispersed in the electrophoretic nanohydroxyapatite coatings on the ti13zr13nb alloy, on their morphology and mechanical properties. Materials 14:163810.3390/ma14071638 ↗
35. Hu H, Lin C, Hu R, Leng Y (2002) A study on hybrid bioceramic coatings of HA/poly (vinyl acetate) co-deposited electrochemically on Ti–6Al–4V alloy surface. Mater Sci Eng C 20:209–21410.1016/S0928-4931(02)00035-8 ↗
36. Park K, Kim S, Hwang M, Song H, Park Y (2017) Biomimetic fabrication of calcium phosphate/chitosan nanohybrid composite in modified simulated body fluids. Express Polym Lett 11:14–2010.3144/expresspolymlett.2017.3 ↗
37. Szőke ÁF, Szabó GS, Hórvölgyi Z, Albert E, Gaina L, Muresan LM (2019) Eco-friendly indigo carmine-loaded chitosan coatings for improved anti-corrosion protection of zinc substrates. Carbohyd Polym 215:63–7210.1016/j.carbpol.2019.03.077 ↗
38. Szőke ÁF, Szabó GS, Hórvölgyi Z, Albert E, Végh AG, Zimányi L, Muresan LM (2020) Accumulation of 2-Acetylamino-5-mercapto-1, 3, 4-thiadiazole in chitosan coatings for improved anticorrosive effect on zinc. Int J Biol Macromol 142:423–43110.1016/j.ijbiomac.2019.09.114 ↗
39. Wang J, de Boer J, De Groot K (2004) Preparation and characterization of electrodeposited calcium phosphate/chitosan coating on Ti6Al4V plates. J Dent Res 83:296–30110.1177/154405910408300405 ↗
40. Boccaccini A, Keim S, Ma R, Li Y, Zhitomirsky I (2010) Electrophoretic deposition of biomaterials. J R Soc Interface 7:S581–S61310.1098/rsif.2010.0156.focus ↗
41. Shalaby HA, Hashem AM, Badr NA, Shoeib MM, Khafagy MG (2011) Preparation of ordered nano-titania arrays and electrodeposition of nano-hydroxyapatite crystals on Ti-6Al%-4% V dental implant surfaces. J Am Sci 7:574–584
42. Abdeltawab A, Shoeib M, Mohamed S (2011) Electrophoretic deposition of hydroxyapatite coatings on titanium from dimethylformamide suspensions. Surf Coat Technol 206:43–5010.1016/j.surfcoat.2011.06.034 ↗
43. DileepKumar V, Sridhar MS, Aramwit P, Krut’ko VK, Musskaya ON, Glazov IE, Reddy N (2021) A Review on the Synthesis and Properties of hydroxyapatite for biomedical applications. J Biomater Sci Polymer Ed 33:1–29
44. Abd El-Salam H, Abd El-Hafez G, Askalany H, Fekry A (2020) A creation of poly (N-2-hydroxyethylaniline-co-2-chloroaniline) for corrosion control of mild steel in acidic medium. J Bio- Tribo- Corros 6:1–1410.1007/s40735-019-0297-6 ↗
45. Abdel-Gawad SA, Sadik MA, Shoeib MA (2019) Preparation and properties of a novel nano Ni-B-Sn by electroless deposition on 7075–T6 aluminum alloy for aerospace application. J Alloy Compd 785:1284–129210.1016/j.jallcom.2019.01.245 ↗
46. S. Sathiyanarayanan, C. Marikkannu, P.B. Srinivasan, V. Muthupandi (2002) Corrosion behaviour of Ti6Al4V and duplex stainless steel (UNS31803) in synthetic bio‐fluids. Anti-Corros Methods Mater10.1108/0003559021043584 ↗
47. Francis A, Abdel-Gawad S, Shoeib M (2021) Toward CNT-reinforced chitosan-based ceramic composite coatings on biodegradable magnesium for surgical implants. J Coat Technol Res 18:1–1810.1007/s11998-021-00468-y ↗
48. Abdel-Gawad SA, Shoeib MA (2019) Corrosion studies and microstructure of Mg−Zn−Ca alloys for biomedical applications. Surf Interfaces 14:108–11610.1016/j.surfin.2018.11.011 ↗
49. Redepenning J, Venkataraman G, Chen J, Stafford N (2003) Electrochemical preparation of chitosan/hydroxyapatite composite coatings on titanium substrates, journal of biomedical materials research part a: an official journal of the society for biomaterials, the japanese society for biomaterials, and the australian society for biomaterials and the korean society for. Biomaterials 66:411–416
50. Awasthi S, Pandey SK, Arunan E, Srivastava C (2021) A review on hydroxyapatite coatings for the biomedical applications: experimental and theoretical perspectives. J Mater Chem B 9:228–24910.1039/D0TB02407D ↗
51. Yi H, Wu LQ, Ghodssi R, Rubloff GW, Payne GF, Bentley WE (2004) A robust technique for assembly of nucleic acid hybridization chips based on electrochemically templated chitosan. Anal Chem 76:365–37210.1021/ac034662t ↗
52. Wang X, Du Y, Liu H (2004) Preparation, characterization and antimicrobial activity of chitosan–Zn complex. Carbohyd Polym 56:21–2610.1016/j.carbpol.2003.11.007 ↗
53. Bartkowiak A, Hunkeler D (1999) Alginate–oligochitosan microcapsules: a mechanistic study relating membrane and capsule properties to reaction conditions. Chem Mater 11:2486–249210.1021/cm9910456 ↗
54. Pang X, Zhitomirsky I (2005) Electrodeposition of composite hydroxyapatite–chitosan films. Mater Chem Phys 94:245–25110.1016/j.matchemphys.2005.04.040 ↗
55. Nikpour M, Rabiee S, Jahanshahi M (2012) Synthesis and characterization of hydroxyapatite/chitosan nanocomposite materials for medical engineering applications. Compos B Eng 43:1881–188610.1016/j.compositesb.2012.01.056 ↗
56. Shen S, Cai S, Zhang M, Xu G, Li Y, Ling R, Wu X (2015) Microwave assisted deposition of hydroxyapatite coating on a magnesium alloy with enhanced corrosion resistance. Mater Lett 159:146–14910.1016/j.matlet.2015.06.096 ↗
57. Ban S, Hasegawa J (2002) Morphological regulation and crystal growth of hydrothermal-electrochemically deposited apatite. Biomaterials 23:2965–297210.1016/S0142-9612(02)00025-X ↗
58. Viswanath B, Ravishankar N (2008) Controlled synthesis of plate-shaped hydroxyapatite and implications for the morphology of the apatite phase in bone. Biomaterials 29:4855–486310.1016/j.biomaterials.2008.09.001 ↗
59. Haque E, Khan NA, Kim CM, Jhung SH (2011) Syntheses of metal-organic frameworks and aluminophosphates under microwave heating: quantitative analysis of accelerations. Cryst Growth Des 11:4413–442110.1021/cg200594e ↗
60. Hahn B-D, Park D-S, Choi J-J, Ryu J, Yoon W-H, Choi J-H, Kim H-E, Kim S-G (2011) Aerosol deposition of hydroxyapatite–chitosan composite coatings on biodegradable magnesium alloy. Surf Coat Technol 205:3112–311810.1016/j.surfcoat.2010.11.029 ↗
61. Huang S, Wu W, Su Y, Qiao L, Yan Y (2021) Insight into the corrosion behaviour and degradation mechanism of pure zinc in simulated body fluid. Corros Sci 178:10907110.1016/j.corsci.2020.109071 ↗
62. Gawad SA, Nasr A, Fekry AM, Filippov LO (2021) Electrochemical and hydrogen evolution behaviour of a novel nano-cobalt/nano-chitosan composite coating on a surgical 316L stainless steel alloy as an implant. Int J Hydrog Energy 46:18233–1824110.1016/j.ijhydene.2021.03.018 ↗
63. Abdel-Gawad SA, Sadik MA, Shoeib MA (2018) Enhancing corrosion resistance of galvanized steel by phosphating and silicate post–sealing. Int J Electrochem Sci 13:2688–270410.20964/2018.03.18 ↗
64. Nasr A, Gawad SA, Fekry AM (2020) A sensor for monitoring the corrosion behavior of orthopedic drug calcium hydrogen phosphate on a surgical 316L stainless steel alloy as implant. J Bio- Tribo- Corros 6:1–1010.1007/s40735-020-0334-5 ↗
65. Hirschorn B, Orazem ME, Tribollet B, Vivier V, Frateur I, Musiani M (2010) Determination of effective capacitance and film thickness from constant-phase-element parameters. Electrochim Acta 55:6218–622710.1016/j.electacta.2009.10.065 ↗
66. Heakal FE-T, Fekry A, Ghoneim A (2008) Corrosion characterization of new tin–silver binary alloys in nitric acid solutions. Corros Sci 50:1618–162610.1016/j.corsci.2008.02.003 ↗
67. Heakal FE-T, Fekry A, Jibril MAE-B (2011) Electrochemical behaviour of the Mg alloy AZ91D in borate solutions. Corros Sci 53:1174–118510.1016/j.corsci.2010.11.040 ↗
68. Ghoneim A, Mogoda A, Awad KA, Heakal F (2012) Electrochemical studies of titanium and its Ti–6Al–4V alloy in phosphoric acid solutions. Int J Electrochem Sci 7:6539–655410.1016/S1452-3981(23)19501-0 ↗
69. Szőke ÁF, Szabó G, Simó Z, Hórvölgyi Z, Albert E, Végh AG, Zimányi L, Muresan LM (2019) Chitosan coatings ionically cross-linked with ammonium paratungstate as anticorrosive coatings for zinc. Eur Polymer J 118:205–21210.1016/j.eurpolymj.2019.05.057 ↗
70. Zhu M, Lu Y, Zhang C, Li L, Xie M, Lin J, Tang K (2019) Facile fabrication of Mg-based coating to improve the biodegradable behavior and cytocompatibility of pure zinc. Surf Coat Technol 372:209–21710.1016/j.surfcoat.2019.05.034 ↗
71. Mo X, Qian J, Chen Y, Zhang W, Xian P, Tang S, Zhou C, Huang N, Ji H, Luo E (2021) Corrosion and degradation decelerating alendronate embedded zinc phosphate hybrid coating on biodegradable Zn biomaterials. Corros Sci 184:10939810.1016/j.corsci.2021.109398 ↗
72. Su Y, Yang H, Gao J, Qin YX, Zheng Y, Zhu D (2019) Interfacial zinc phosphate is the key to controlling biocompatibility of metallic zinc implants. Adv Sci 6:190011210.1002/advs.201900112 ↗