Acoustic emission study of corrosion fatigue crack propagation mechanism for LY12CZ and 7075-T6 aluminum alloys
Source abstract
Abstract
Acoustic emission signals were continuously monitored during fatigue crack propagation for LY12CZ and 7075-T6 aluminum alloys in laboratory air and 3.5% NaCl solution. The results showed that the acoustic emission count rate was as a linear function of crack propagation rate during fatigue and corrosion fatigue. The acoustic emission activity for LY12CZ was smaller in solution than that in air; but for 7075-T6, greater in solution than that in air. The acoustic emission waveform parameter, the frequency centroid ratio, was tried to use as a criterion to distinguish the corrosion fatigue crack propagation mechanism for anodic dissolution of LY12CZ and hydrogen embrittlement of 7075-T6.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Non-Destructive Testing Techniques · Ultrasonics and Acoustic Wave Propagation · Fatigue and fracture mechanics
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (20)
Show source-provided references
1. M. A. HAMSTAD and J. D. MCCOLSKEY, J. Acoustic Emission. 15 (1997) 1.
2. Idem., Mater. Evalu. 57 (1999) 1165.
3. K. ONO, J. Acoustic Emission. 15 (1997) S95.
4. F. P. FORD, Corrosion. 35 (1979) 281.10.5006/0010-9312-35.7.281 ↗
5. W. GRUHL, Z. Metallkde. 75 (1984) 819.
6. N. J. H. HOLROYD and D. HARDIE, Corros. Sci. 23 (1983) 527.10.1016/0010-938X(83)90117-8 ↗
7. R. E. RICKER and D. J. DUQUETTE, Metall. Trans: A, 19A (1988) 1775.10.1007/BF02645146 ↗
8. F. D. WALL and G. E. STONER, Corros. Sci. 39 (1997) 835.10.1016/S0010-938X(97)81154-7 ↗
9. K. URUSHINO and K. SUGIMOTO, ibid. 19 (1979) 225.10.1016/0010-938X(79)90008-8 ↗
10. G. M. SCAMANS et al, ibid. 16 (1976) 443.10.1016/0010-938X(76)90065-2 ↗
11. D. J. DUQUETTE, AGARD Report, No. AGARD-CP-316, 1981
12. F. P. FORD, Corrosion. 35 (1979) 281.10.5006/0010-9312-35.7.281 ↗
13. M. GAO, P. S. PAO and R. P. WEI, Metall. Trans: A 19A (1988) 1739.10.1007/BF02645142 ↗
14. P. C. PARIS and F. ERDOGAN, J. Basic Eng. Trans ASME (D). 85 (1963) 528.10.1115/1.3656900 ↗
15. T. M. MORTON, S. SMITH and R. M. HARRINGTON, Exp. Mech. 14 (1974) 208.10.1007/BF02323071 ↗
16. T. M. MORTON, R. M. HARRINGTON and J. G. BJELETICH, Eng. Fract. Mech. 5 (1973) 691.10.1016/0013-7944(73)90047-7 ↗
17. T. KISHI and Y. HISAMATSU, in Proc. 6th Acoustic Emission Symp. (Susono, Japan, JSNDI, 1982), p. 115.
18. Z. F. WANG, Z. ZHU and W. KE, Metall. Trans: A. 22A (1991) 2677.10.1007/BF02851361 ↗
19. F. P. FORD, F. T. BURSTEIN and T. P. HOAR, J. Electrochem. Soc. 127 (1980) 1325.10.1149/1.2129893 ↗
20. N. J. H. HOLROYD and D. HARDIE, Corros. Sci. 23 (1983) 527.10.1016/0010-938X(83)90117-8 ↗