Characterization of dynamic recrystallisation in as-homogenized Mg–Zn–Y–Zr alloy using processing map
Source abstract
Abstract
The hot working behavior of a as-homogenized Mg–Zn–Y–Zr alloy has been investigated in the temperature range 200–400°C and strain rate range 0.0015–7.5 s−1 using processing map. The power dissipation map reveals that a domain of dynamic recrystallisation (DRX) in the temperature range 300–400°C and strain rate range 0.0015–0.15 s−1, with its peak efficiency of 38% at 350°C and 0.0015 s−1, which are the optimum hot working parameters. The apparent activation energy in the hot deformation process is 148 ± 3 KJ/mol that is larger than that of ZK60 alloy because of the obstruction of Y atoms for diffusion. DRX model indicates that DRX of Mg–Zn–Y–Zr alloy is controlled by the rate of nucleation, which is lower one order of magnitude than growth. And the rate of nucleation depends on the process of mechanical recovery by cross-slip of screw dislocations.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Magnesium Alloys: Properties and Applications · Metal and Thin Film Mechanics · Microstructure and mechanical properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (22)
Show source-provided references
1. J. KOIKE, T. KOBAYASHI, T. MUKAI, H. WATANABE, M. SUZUKI, K. MARUYAMA and K. HIGASHI, Acta Materilia. 51 (2003) 2055.10.1016/S1359-6454(03)00005-3 ↗
2. M. R. BARNETT, Z. KESHAVARZ, A. G. BEER and D. ATWELL, ibid. 52 (2004) 5093.10.1016/j.actamat.2004.07.015 ↗
3. A. SINGH and A. P. TSAI, Scripta Materialia. 49 (2003) 143.10.1016/S1359-6462(03)00217-3 ↗
4. E. M. PADEZHNOVA, E. V. MEL'NIK, R. A. MILIYEVSKIY, T. V. DOBATKINA and V. V. KINZHIBAO, Russ. Metall. (Metally) 4 (1982) 185.
5. Z. P. LUO and S. Q. ZHANG, J. Mater. Sci. Lett. 12 (1993) 1490.10.1007/BF00277074 ↗
6. W. F. SMITH (Ed.), in “Structure and Properties of Engineering Alloys”, (McGraw-Hill, New York, 1993) p. 542.
7. F. S. PIERCE, S. J. POON and Q. GUO, Science 261 (1993) 737.10.1126/science.261.5122.737 ↗
8. Y. ZHANG, X. Q. ZENG, L. F. LIU, C. LU, H. T. ZHOU, Q. LI and Y. P. ZHU, Mater. Sci. Engng. A 373 (2004) 320.10.1016/j.msea.2004.02.007 ↗
9. Y. V. R. K. PRASAD and S. SASIDHARA, “Hot working Guide: A compendium of processing maps”, (ASM International Materials Park, OH, 1997).
10. J. K. CHAKRAVARTY, Y. V. R. K. PRASAD and M. K. ASUNDI, Metall. Trans. A 22 (1991) 829.10.1007/BF02658992 ↗
11. Y. V. R. K. PRASAD and K. P. RAO, Mater. Sci. Engi. A 374 (2004) 335.10.1016/j.msea.2004.03.007 ↗
12. O. SIVAKESAVAM, I. S. RAO and Y. V. R. K. PRASAD, Mater. Sci. Technol. 9 (1993) 805.
13. O. SIVAKESAVAM and Y. V. R. K. PRASAD, Mater. Sci. Engi. A 323 (2002) 270.10.1016/S0921-5093(01)01392-2 ↗
14. Idem., Z. Metallkd. 93 (2002) 123.10.3139/146.020123 ↗
15. Idem., Mater. Sci. Engi. A 362 (2003) 118.10.1016/S0921-5093(03)00296-X ↗
16. N. SRINIVASAN and Y. V. R. K. PRASAD, Mater. Sci. Technol. 8 (1992) 206.10.1179/026708392790170603 ↗
17. A. MWEMBELA, E. B. KONOPLEVA and H. J. MCQUEEN, Scripta Mater. 37 (1997) 1789.10.1016/S1359-6462(97)00344-8 ↗
18. H. J. MCQUEEN, M. M. MYSHLYAEV and A. MWEMBELA, Canadian Metall. Quarterly 42 (2003) 97.10.1179/000844303794535780 ↗
19. B. DERBY, Scripta Metall. Mater. 27 (1992) 1581.10.1016/0956-716X(92)90148-8 ↗
20. A. GALIYEV, R. KAIBYSHEV and G. GOTTSTEIN, Acta Mater. 49 (2001) 1199.10.1016/S1359-6454(01)00020-9 ↗
21. H. J. FROST and M. F. ASHBY, in “Deformation-mechanism maps: the plasticity and creep of metals and ceramics”, (Pergamon, Oxford, 1982) p. 44.
22. T. SAKAI and J. J. JONAS. Acta Metall. 32 (1984) 189.10.1016/0001-6160(84)90049-X ↗