Effect of UHMWPE concentration on the extracting, drawing, and crystallizing properties of gel fibers
Source abstract
Abstract
In this study, ultra-high molecular weight polyethylene (UHMWPE) gel fibers were made by gel-spinning with different concentration solutions of 8–16 wt%. The solvent separation and extracting dynamics of different gel fibers were studied. The thermal and crystallizing properties of different fibers were characterized with differential scanning calorimeter and wide-angle X-ray diffraction. The morphological structure of different gel fibers was observed using scanning electron microscope (SEM). The maximum drawing ratios (DRs) of different fibers and the tenacity of ultra-drawn fibers were measured and compared. The results showed that the phase separation of different concentration UHMWPE gel fibers were severe at the first hour and reached equilibrium state after about 48 h placing. The critical extraction time of different gel fibers and the optimum bath ratios of extraction agent to gel fibers were 2 min and 10 mL/g, respectively. The melting point and the crystallinity of extracted fibers were both higher than that of gel fibers, and the crystallinity of fibers increased with increasing of UHMWPE concentration. High concentration UHMWPE fiber has more dense morphological structure while compared with lower concentration ones. The maximum achieved DRs of gel fibers were higher than that of extracted fibers. The DR and tensile strength of extracted fibers decreased with increasing of UHMWPE concentration.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Polymer crystallization and properties · Natural Fiber Reinforced Composites · Polymer Foaming and Composites
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (21)
Show source-provided references
1. Zwijnenburg A, Pennings AJ (1975) Colloid Polym Sci 253:45210.1007/BF01491823 ↗
2. Paul S, Lemstra Piet J (1979) Makromol Chem Phys 180(12):298310.1002/macp.1979.021801220 ↗
3. Paul S, Lemstra Piet J, Booij Henk C (1981) J Polym Sci B 19(5):877
4. Barham PJ, Keller A (1985) J Mater Sci 20:2281. doi:https://doi.org/10.1007/BF0055605910.1007/BF00556059 ↗
5. Hoogsteen W, ten Brinke G, Pennings AJ (1987) Polymer 28(6):92310.1016/0032-3861(87)90164-9 ↗
6. Kaji A, Otha Y, Yasuda H, Murano M (1990) Polym J 22(6):45510.1295/polymj.22.455 ↗
7. Smith P, Boudet A, Chanzy H (1985) J Mater Sci Lett 4:13. doi:https://doi.org/10.1007/BF0071988310.1007/BF00719883 ↗
8. Kalb B, Pennings AJ (1980) J Mater Sci 15:2584. doi:https://doi.org/10.1007/BF0055076310.1007/BF00550763 ↗
9. Bastiaansen CWM (1992) Polymer 33(8):164910.1016/0032-3861(92)91061-6 ↗
10. Bastiaansen, Cees WM (1997) Mater Sci Technol 18:551
11. Maghsoud Z, Moaddel H (2007) Iran Polym J 16(6):363
12. Zhang Y, Xiao C, GuanXia J, ShuLin A (1999) J Appl Polym Sci 74:67010.1002/(SICI)1097-4628(19991017)74:3<670::AID-APP21>3.0.CO;2-8 ↗
13. Xin Z, Dong Z, Xin C (2009) Spinning process for high-strength and high-modulus ultrahigh molecular weight polyethylene fibre. CN, CN101525769
14. Zhao G, Xu J (2009) Beijing Fuzhuang Xueyuan Xuebao 29(2):7 (in Chinese)
15. Yin S., X. Qiao (2003) Method for preparing extra high molecular polyethylene high- concentrated solution for spinning, CN, CN1405367
16. Jian T, Shyu W, Lin Y, Chen K, Yeh J (2003) Polym Eng Sci 43(11):176510.1002/pen.10149 ↗
17. Yeh J, Lin S, Tu C, Hsie K, Chang F (2008) J Mater Sci 43:4892. doi:https://doi.org/10.1007/s10853-008-2711-110.1007/s10853-008-2711-1 ↗
18. Yeh J, Lin Y, Jiang H (2004) J Appl Polym Sci 91:155910.1002/app.13259 ↗
19. Tsubakihara S, Nakamura A, Yasuniwa M (1996) Polym J 28(6):48910.1295/polymj.28.489 ↗
20. Kwon YK, Boller A, Pyda M, Wunderlich B (2000) Polymer 41:623710.1016/S0032-3861(99)00839-3 ↗
21. Chiu H, Wang J (1998) J Appl Polym Sci 70:100910.1002/(SICI)1097-4628(19981031)70:5<1009::AID-APP22>3.0.CO;2-1 ↗