Spark plasma sintering of ZrB2–ZrC powder mixtures synthesized by MA-SHS in air
Source abstract
Abstract
Mechanical activation-assisted self-propagating high-temperature synthesis (MA-SHS) in air was successfully applied to the synthesis of the powder mixtures of ZrB2 and ZrC as a precursor of the ZrB2–ZrC composite. When the powder mixtures of Zr/B/C = 4/2/3–6/10/1 in molar ratio were mechanically activated (MA) by ball milling for 45–60 min and then exposed to air, they self-ignited spontaneously and the self-propagating high-temperature synthesis (SHS) was occurred to form ZrB2 and ZrC. The ZrB2–ZrC composites were produced from these MA-SHS powders by spark plasma sintering (SPS) at 1800 °C for 5–10 min and showed the fine and homogeneous microstructure composed of the <5 μm-sized grains. The mechanical properties of the composites evaluated by Vickers indentation method showed the values of Vickers hardness of 13.6–17.8 GPa and fracture toughness of 2.9–5.1 MPa·m1/2, depending on the molar ratio of ZrB2/ZrC. Thus, the better microstructure and mechanical properties of the ZrB2–ZrC composites were obtained from the MA-SHS powder mixtures, compared with those obtained from the MA powder, the mixing powder and the commercial powder mixtures.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Advanced ceramic materials synthesis · Advanced materials and composites · MXene and MAX Phase Materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (18)
Show source-provided references
1. Johnson WB, Nagelberg AS, Breval E (1991) J Am Ceram Soc 74(9):209310.1111/j.1151-2916.1991.tb08265.x ↗
2. Breval E, Johnson WB (1992) J Am Ceram Soc 75(8):213910.1111/j.1151-2916.1992.tb04476.x ↗
3. Shim SH, Niihara K, Auh KH, Shim B (2002) J Microscopy 205(3):23810.1046/j.1365-2818.2002.00994.x ↗
4. Kuwabara K, (2002) Ceram Jpn 37(4):267
5. Niihara K, (1991) J Ceram Soc Jpn 99(10):97410.2109/jcersj.99.974 ↗
6. Tsuchida T, Hasegawa T, Inagaki M (1994) J Am Ceram Soc 77(12):322710.1111/j.1151-2916.1994.tb04574.x ↗
7. Tsuchida T, Kitagawa T, Inagaki M, (1995) Eur J Solid State Inorg Chem 32:629
8. Tsuchida T, Hasegawa T, (1996) Thermochim Acta 276:12310.1016/0040-6031(95)02763-7 ↗
9. Tsuchida T, Hasegawa T, Kitagawa T, Inagaki M (1997) J Eur Ceram Soc 17:179310.1016/S0955-2219(97)00074-5 ↗
10. Tsuchida T, Kitagawa T, Inagaki M (1997) J Mater Sci 32:512310.1023/A:1018669501136 ↗
11. Tsuchida T, Kawaguchi M, Kodaira K (1997) Solid State Ionics 101–103:149
12. Tsuchida T, Azuma Y (1997) J Mater Chem 7(11):226510.1039/a704235c ↗
13. Tsuchida T, Kan T (1999) J Eur Ceram Soc 19:179510.1016/S0955-2219(98)00278-7 ↗
14. Tsuchida T, Yamamoto S (2004) J Eur Ceram Soc 24:4510.1016/S0955-2219(03)00120-1 ↗
15. Tokita M (1993) J Soc Powder Technol Jpn 30:79010.4164/sptj.30.11_790 ↗
16. Shen Z, Johnsson M, Zhao Z, Nygren M (2002) J Am Ceram Soc 85:192110.1111/j.1151-2916.2002.tb00381.x ↗
17. Japanese Industrial Standard No. JIS R 1607, Testing methods for fracture toughness of fine ceramics, 1995, p 1
18. Krell A, Blank P (1995) J Am Ceram Soc 78(4):111810.1111/j.1151-2916.1995.tb08452.x ↗