Synthesis of Ca3Co4O9 ceramics by polymerized complex and hydrothermal hot-pressing processes and the investigation of its thermoelectric properties
Source abstract
Abstract
Ca3Co4O9 ceramic powders were synthesized by the polymerized complex (PC) method and consolidated by the hydrothermal hot-pressing (HHP) technique. Observation by scanning electron microscope indicated that the form of powders by the PC process was fine and flaky. The density of the sintered body increased with an increase of the operating temperature and pressure during the HHP process. The electrical resistivity was greatly reduced with an increase of the operating pressure, but the thermal conductivity is prone to increase with an increase of the operating temperature and pressure. The Seebeck coefficient was hardly affected by the HHP condition. As a result, the sample treated by the HHP process under the condition of 573 K, 200 MPa, and 1 h showed a maximum ZT of about 0.29 at 1,073 K.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Advanced Thermoelectric Materials and Devices · Phase Change Materials Research · Thermal properties of materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (21)
Show source-provided references
1. Funahashi R, Matsubara T, Ikuta H, Takeuchi T, Mizutani U, Sodeoka S (2000) Jpn J Appl Phys 39:L112710.1143/JJAP.39.L1127 ↗
2. Moon J-W, Nagahama D, Masuda Y, Seo W-S, Koumoto K (2001) J Ceram Soc Jpn 109:64710.2109/jcersj.109.1272_647 ↗
3. Masset AC, Michel C, Maignam A, Herrieu M, Toulemonde O, Studer F, Raveau B (2000) Phys Rev B 62:16610.1103/PhysRevB.62.166 ↗
4. Zhang Y, Zhang J, Lu Q (2007) Ceram Int 32:130510.1016/j.ceramint.2006.04.011 ↗
5. Li S, Funahashi R, Matsubara I, Yamada H, Ueno K, Sodeoka S (2001) Ceram Int 27:32110.1016/S0272-8842(00)00083-3 ↗
6. Mikami M, Ando N, Funahashi R (2005) J Solid State Chem 178:218610.1016/j.jssc.2005.04.027 ↗
7. Zhang YF, Zhang JX, Lu QM, Zhang QY (2006) Mater Lett 60:244310.1016/j.matlet.2006.01.013 ↗
8. Kakihana M, Yoshimura M, Mazaki H, Yasuoka H, Börjesson L (1992) J Appl Phys 71:390410.1063/1.350858 ↗
9. Katsuyama S, Takagi Y, Ito M, Majima K, Nagai H, Sakai H, Yoshimura K, Kosuge K (2002) J Appl Phys 92:139110.1063/1.1489091 ↗
10. Yamasaki N, Kai T, Nishioka M, Yanagisawa K, Ioku K (1990) J Mater Sci Lett 9:115010.1007/BF00721872 ↗
11. Yamasaki N, Weiping T, Jiajun K (1992) J Mater Sci Lett 11:93410.1007/BF00729099 ↗
12. Uher C, Yang J, Hu S, Morelli DT, Meisner GP (1999) Phys Rev B 59:861510.1103/PhysRevB.59.8615 ↗
13. Nakagawa H, Tanaka H, Kasama A, Anno H, Matsubara K (1997) Proceedings of 16th international conference on thermoelectrics, Dresden, Germany, p 351
14. Katsuyama S, Kanayama Y, Ito M, Majima K, Nagai H (2000) J Appl Phys 88:348410.1063/1.1288015 ↗
15. Katsuyama S, Kishida A, Ito M (2006) J Alloys Compd 414:21510.1016/j.jallcom.2005.05.050 ↗
16. Katsuyama S, Takiguchi Y, Ito M (2007) Mater Trans 48:207310.2320/matertrans.E-MRA2007805 ↗
17. Lotgering FK (1959) J Inorg Nucl Chem 9:11310.1016/0022-1902(59)80070-1 ↗
18. Shikame M, Funahashi R (2003) Appl Phys Lett 82:185110.1063/1.1562337 ↗
19. Li S, Funahashi R, Matsubara I, Ueno K, Yamada H (1999) J Mater Chem 9:165910.1039/a904413b ↗
20. Katsuyama S, Shichijo Y, Ito M, Majima K, Nagai H (1998) J Appl Phys 84:670810.1063/1.369048 ↗
21. Prevel M, Lemonnier S, Klein Y, Hёbert S, Chateigner D, Ouladdiaf B, Noudem JG (2005) J Appl Phys 98:09370610.1063/1.2120892 ↗