Effect of the chemical structure of aromatic polyimides on their thermal aging, relaxation behavior and mechanical properties

Giuseppe Ragosta, Mario Abbate, Pellegrino Musto, Gennaro Scarinzi

Journal of Materials Science· Volume 47· Issue 6
Publisher page

Abstract

This article examines the effects of structural changes and thermal aging treatments on the relaxation processes and mechanical properties of three polyimides differing for their molecular structure i.e. PMDA-ODA, 6FDA-ODA, and 6FDA-6FpDA. These polyimides were obtained by thermal imidization of their polyamic acid precursors, which were synthesized from the respective dianhydrides [pyromellitic anhydride (PMDA), hexahydrofluoroisopropylidene diphthalic anhydride (6FDA)], and diamines [4,4'-diaminodiphenyl ether (ODA), 4,4'-(hexafluoroisopropylidene) dianiline (6FpDA)]. After the curing process, the polyimides were thermally aged at a fixed temperature for various times Dynamic mechanical measurements performed in a multi-frequency mode, were used to determine the glass-rubber and sub-glass transitions, as well as the activation energy of the ? transition. It was found that the Tg decreased in the order PMDA-ODA?6FDA- 6FpDA?6FDA-ODA as a result of an increased chain rigidity and molecular packing induced by charge transfer interactions during the thermal imidization process. The ? sub-glass transition showed two relaxation processes identified as ?' and ?" The ?' process was attributed to the local motion of the diamine constituents while the ?"process was caused by the local motion of the dianhydride moiety. The cooperativity of these molecular motions was also assessed via the Starkweather method. The thermal aging enhanced the state of aggregation of polyimide chains and thus the Tg and the sub-glass transition properties. This effect was particularly marked for the PMDA-ODA polyimide. Also the mechanical properties were significantly affected by chemical structure and aging treatments. For non-aged samples the more influenced parameter was the elongation at break, which decreased in the order PMDA-ODA?6FDAODA?6FDA-6FpDA. The aging enhanced the elastic modulus and the tensile strength and reduced the elongation at break.
Source: openaire · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Synthesis and properties of polymers · Epoxy Resin Curing Processes · Tribology and Wear Analysis

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (33)

Show source-provided references
1. Ghosh MK, Mittal KL (eds) (1996) Polyimide: fundamentals and applications. Marcel Dekker, New York
2. Bessonov MI, Zubkov VA (1993) Polyamic acids and polyimides: synthesis, transformation and structure. CRC Press, Boca Raton
3. Thompson LF, Wilson CG, Tagawa S (eds) (1994) Polymers for microelectronics: resists and dielectric. In: ACS symposium series, vol 537. ACS, Washington DC10.1021/bk-1994-0537 ↗
4. Mengxian D (2007) Prog Polym Sci 32:62310.1016/j.progpolymsci.2007.01.007 ↗
5. Banerjee S, Madera MK, Salunke AK, Jaiswal DK (2003) Polymer 44:200310.1016/S0032-3861(02)00801-7 ↗
6. Liaw DJ, Chang FC, Leung MK, Chou MY, Muellen K (2005) Macromolecules 28:402410.1021/ma048559x ↗
7. Han Y, Fang X, Zhong Z, Xiu X (2010) J Mater Sci 45:1921. doi: 10.1007/s10853-009-4179-z10.1007/s10853-009-4179-z ↗
8. Lu YC, Tandon GP, Putthanarat S, Schoeppner GA (2009) J Mater Sci 44:2119. doi: 10.1007/s10853-009-3311-410.1007/s10853-009-3311-4 ↗
9. Li H, Liu J, Wang K, Fan L, Yang S (2006) Polymer 47:144310.1016/j.polymer.2005.12.074 ↗
10. Chung CL, Hsiao SH (2008) Polymer 49:247610.1016/j.polymer.2008.03.047 ↗
11. Hasegava M, Horie K (2001) Prog Polym Sci 26:25910.1016/S0079-6700(00)00042-3 ↗
12. Li N, Cui Z, Zhang S, Xing W (2007) Polymer 48:725510.1016/j.polymer.2007.10.026 ↗
13. Qu W, KO TM, Vora RH, Chung TS (2001) Polymer 42:639310.1016/S0032-3861(01)00111-2 ↗
14. Arnold FE Jr, Brono KR, Shen DX, Eashoo M, Lee CJ, Harris FW, Chen SZD (1966) Polym Sci Polym Lett Ed 4:35310.1002/pol.1966.110040510 ↗
15. Habas JP, Peyrelasse J, Grenier-Loustalot MF (1996) High Perfor Polym 8:51510.1088/0954-0083/8/4/004 ↗
16. Li FM, Fang S, Ge JJ, Honigfort PS, Chen JC, Harris FW, Cheng SZD (1999) Polymer 40:498710.1016/S0032-3861(98)00721-6 ↗
17. Xu G, Gryte CC, Nowick AS, Li SZ, Pak YS, Greenbaum SG (1989) J Appl Phys 66:529010.1063/1.343719 ↗
18. Cheng SZD, Chalmers TM, Gu Y, Yoon Y, Harris F-W, Chen J (1995) Macromol Chem Phys 196:143910.1002/macp.1995.021960507 ↗
19. Sun Z, Dong L, Zhuang Y, Cao L, Ding M, Feng Z (1992) Polymer 33:472810.1016/0032-3861(92)90684-O ↗
20. Arnold FE Jr, Bruno KR, Shen D, Eashoo M, Lee CJ, Harris FW (1993) Polym Eng Sci 33:137310.1002/pen.760332102 ↗
21. Ragosta G, Musto P, Abbate M, Scarinzi G (2011) J Appl Polym Sci 121:216810.1002/app.33788 ↗
22. Anannarukan W, Tantayanon S, Zhang D, Alema’n EA, Modarelli DA, Harris FW (2006) Polymer 47:493610.1016/j.polymer.2006.05.023 ↗
23. Yan J, Wang Z, Gao L, Ding M (2006) Macromolecules 39:755510.1021/ma0608727 ↗
24. Takahashi N, Do YY, William P (1984) Macromolecules 17:258310.1021/ma00142a021 ↗
25. Wahsman ED, Frank CW (1988) Polymer 29:119110.1016/0032-3861(88)90043-2 ↗
26. Chen KM, Wang TH, King JS (1993) J Appl Polym Sci 48:29110.1002/app.1993.070480213 ↗
27. Li F, Fang S, Ge JJ, Honigfort PS, Chen JC, Harris FW, Cheng SZD (1999) Polymer 40:457110.1016/S0032-3861(99)00066-X ↗
28. Qu W, Ko TM, Vora RH, Chung TS (2001) Polymer 42:639310.1016/S0032-3861(01)00111-2 ↗
29. Starkweather HWJ (1990) Macromolecules 23:32810.1021/ma00203a056 ↗
30. Cho K, Lee D, Lee MS, Park CE (1997) Polymer 38:161510.1016/S0032-3861(96)00597-6 ↗
31. Pater RH, Soucek MD, Toughened Jang BZ, Plastics I (1993) Riew and Kinlock editors. American Chemical Society, Washington
32. Musto P, Ragosta G, Scarinzi G, Mascia L (2004) Polymer 45:426510.1016/j.polymer.2004.03.099 ↗
33. Kinlock AJ, Young RI (1983) Fracture behaviour of polymers. Applied Science. Springer, London