Formation of strain-induced martensite in austempered ductile iron

Srinivasmurthy Daber, P. Prasad Rao

Journal of Materials Science· Volume 43· Issue 1
Publisher page

Abstract

The present work has been taken up to study the influence of microstructure on the formation of martensite in austempered ductile iron. Ductile iron containing 1.5 wt.% nickel and 0.3 wt.% molybdenum was subjected to two types of austempering treatments. In the first, called as conventional austempering, the samples were austempered for 2 h at 300, 350 or 400 °C. In the second treatment, called as stepped austempering, the samples were initially austempered at 300 °C for 10, 20, 30, 45 or 60 min. These were subsequently austempered for 2 h at 400 °C. Tensile tests revealed considerable variation in the strain-hardening behaviour of the samples with different heat treatments. In the case of samples subjected to conventional austempering, it was found that strain-hardening exponent increased with increasing austempering temperature. In the case of samples subjected to stepped austempering, increased strain hardening was observed in samples subjected to short periods of first step austempering. Study of the microstructures revealed that increased strain hardening was associated with the formation of strain-induced martensite. There was a greater propensity for the formation of strain-induced martensite in the samples containing more of blocky austenite. Retained austenite in the form of fine films between sheaths of ferrite was relatively more stable. Studies revealed that the morphology, size and carbon content of the retained austenite were important parameters controlling their tendency to transform to martensite.
Source: openaire · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Microstructure and Mechanical Properties of Steels · Metal Alloys Wear and Properties · Electromagnetic Effects on Materials

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (21)

Show source-provided references
1. Johansson M (1977) AFS Trans 85:117
2. Gundalach RB, Janowak JF (1983) AFS Trans 91:377
3. Rouns TN, Rundman KB, Moore DM (1984) AFS Trans 92:815
4. Gundalach RB, Janowak JF (1986) In: Proceedings of the 2nd International Conference on Austempered ductile iron, Ann Arbor, MI, USA, March. ASME Gear Research Institute, p 23
5. Arnzabal J, Gutierrez I, Rodriguez-Ibabe JM, Urcola JJ (1992) Mater Sci Technol 8:26310.1179/mst.1992.8.3.263 ↗
6. Timokhina IB, Hodgson PD, Pereloma EV (2004) Metall Mater Trans A 35A:233110.1007/s11661-006-0213-9 ↗
7. Tommita Y (1995) Mater Sci 30:10510.1007/BF00352138 ↗
8. Reisner G, Werner EA, Kerschbhaummaur P, Papst I, Fischer FD (1997) J Met 49(9):62
9. De Meyer M, Vanderschueren D, De Cooman BC (1999) Iron Steel Inst Jpn Int 39(8):81310.2355/isijinternational.39.813 ↗
10. Bai DQ, Di Chiro A, Yue S (1998) Mater Sci Forum 284–286:253
11. Chen HC, Era H, Shimizu M (1989) Metal Trans A 20A:43710.1007/BF02653923 ↗
12. Miihkinen VTT, Edmonds DV (1987) Mater Sci Technol 3:42210.1179/mst.1987.3.6.422 ↗
13. Takahashi M, Bhadeshia HKDH (1991) Mater Trans JIM 32:68910.2320/matertrans1989.32.689 ↗
14. Wang J, Van Der Zwaag S (2001) Wire 50:1527
15. Tsukatani I, Hashimoto S, Inoue T (1991) Iron Steel Inst Jpn Int 31(9):99210.2355/isijinternational.31.992 ↗
16. Cullity BD (1974) Elements of x-ray diffraction. Addison-Wesley, Reading, MA, p 411
17. Roberts CS (1953) Trans AIME 197:203
18. Prasad Rao P, Putatunda SK (1998) Metall Mater Trans A 29A:3005
19. Rundman KB, Klug RC (1982) AFS Trans 90:499
20. Voigt RC, Loper CR (1984) In: Proceedings of the 1st International Conference on austempered ductile iron. ASM, Metals Park, OH, p 83
21. Hollomon TH (1945) Trans AIME 162:268