Effect of exfoliated graphite nanoplatelets on the mechanical and viscoelastic properties of poly(lactic acid) biocomposites reinforced with kenaf fibers

The focus of this study is to explore synergy between nanomaterials such as exfoliated graphite nanoplatelets (xGnP) and micro-size reinforcements such as kenaf natural fibers, in poly(lactic acid) based composites. The nano-biocomposites are made by melt-mixing followed by injection molding. Prior to melt-mixing the kenaf fibers were coated with the xGnP using sonication. The reinforcement content used in the study was up to 5 wt% and up to 40 wt% for xGnP and kenaf fibers, respectively. The flexural strength and modulus and the viscoelastic properties such as storage modulus were determined. It was found that addition of 5 wt% xGnP did not increase the viscosity of the polymer melt, enhanced the flexural modulus by 25–30% at any fiber loading used but did not increase the strength, indicating insufficient load transfer at the polymer-xGnP or xGnP-kenaf interface. Finally, addition of xGnP had a positive effect on the heat distortion temperature but only at higher fiber loadings.