Morphology and microstructure of M2C carbide formed at different cooling rates in AISI M2 high speed steel

X. F. Zhou, F. Fang, F. Li, J. Q. Jiang

Journal of Materials Science· Volume 46· Issue 5
Publisher page

Abstract

In as-cast structure of AISI M2 high speed steel, M2C carbide prevails, the morphology of which has crucial influence on distribution and dimension of carbides in final products. In this study, the morphology and microstructure of M2C formed at different cooling rates have been investigated by scanning electron microscope, X-ray diffraction, transmission electron microscope, and electron back-scatter diffraction. The results show that the morphology of M2C carbide changes from the plate-like type to the fibrous one with increasing cooling rates. Surprisingly, the microstructure between plate-like and fibrous M2C is significantly different. Twining and stacking faults are observed in the plate-like M2C, which is supported by great misorientations between adjacent carbides. However, no planar faults are identified in fibrous M2C and the carbides in one colony have almost identical orientation. It is expected that plate-like M2C grows as a faceted phase, while fibrous M2C formed at high cooling rates is likely a non-faceted phase. The difference of liquid/solid interface structure is supposed to result in the morphology change of M2C.
Source: openaire · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Metal Alloys Wear and Properties · Advanced materials and composites · High-Temperature Coating Behaviors

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (20)

Show source-provided references
1. Roberts GA, Hamaker JC (1980) Tool steels, 3rd edn. American Society for Metals, Metals Park
2. Fischmeister HF, Riedl R, Karagoz S (1989) Metall Trans A 20A:213310.1007/BF02650299 ↗
3. Lee ES, Park WJ, Baik KH et al (1998) Scripta Mater 39:113310.1016/S1359-6462(98)00270-X ↗
4. Nagakura S, Oketani S (1968) Trans ISIJ 8:26510.2355/isijinternational1966.8.265 ↗
5. Boccalini M, Goldenstein H (2001) Int Mater Rev 46:9210.1179/095066001101528411 ↗
6. Fredriksson H, Brising S (1976) Scand J Metall 5:268
7. Fredriksson H, Nica M (1979) Scand J Metall 8:243
8. Boccalini M, Matsubara Y, Goldenstein H (1996) AFS Trans 8:907
9. Taran YN, Nizhnikovskaya PF, Snagovskii LM et al (1979) Met Sci Heat Treat 21:79110.1007/BF00708387 ↗
10. Petrov R, Kestens L, Wasilkowska A et al (2007) Mater Sci Eng A 447:28510.1016/j.msea.2006.10.023 ↗
11. Hong SH, Lee DN (2003) Mater Sci Eng A 351:13310.1016/S0921-5093(02)00834-1 ↗
12. Hetzner DW, Geertruyden WV (2008) Mater Charact 59:82510.1016/j.matchar.2007.07.005 ↗
13. Randle V, Laird G (1993) J Mater Sci 28:4245. doi: 10.1007/BF0035126110.1007/BF00351261 ↗
14. Zhou XF, Fang F, Jiang JQ (2008) Foundry 57:658
15. Zhou XF, Fang F, Jiang JQ et al (2009) Kang T’ieh 44:76
16. Flemings MC (1974) Solidification processing, 1st edn. McGraw-Hill, New York
17. Chen Y, Wang HM (2006) J Mater Res 21:37510.1557/jmr.2006.0043 ↗
18. Boccalini M, Correa AVO, Goldenstein H (1999) Mater Sci Technol 15:62110.1179/026708399101506355 ↗
19. Flood SC, Hunt JD (1981) Met Sci 15:28710.1179/030634581790426813 ↗
20. Zhang DL, Cantor B (1993) Metall Trans A 24A:119510.1007/BF02657251 ↗