Hydrogen embrittlement susceptibility of over aged 7010 Al-alloy
Source abstract
Abstract
Slow strain rate testing (SSRT) was carried out on over aged 7010 Al-alloy in laboratory air, glycerin and 3.5 wt.% NaCl solution with and without cathodic charging to study the hydrogen embrittlement susceptibility of the alloy in over aged condition. It was found that the over aged alloy exhibited high resistance to stress corrosion cracking (SCC) than hydrogen embrittlement (HE). The high SCC resistance is due to the modification in the grain boundary precipitate morphology and chemistry due to over aging, however it is suggested that the dislocations in the alloy are not completed annealed during over aging to arrest HE.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Hydrogen embrittlement and corrosion behaviors in metals · Material Properties and Failure Mechanisms · Non-Destructive Testing Techniques
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (16)
Show source-provided references
1. Bobby Kannan M, Raja VS, Raman R, Mukhopadhyay AK (2003) Corrosion 59:88110.5006/1.3287709 ↗
2. Polmear IJ (1989) In: Light alloys: metallurgy of light metals, 2nd edn. Edward Arnold, London, p 101
3. Sarkar B, Marek M, Starke EA Jr (1981) Metall Trans 12A:193910.1007/BF02643806 ↗
4. Sprowls DO (1996) In: Jones RH (eds) Evaluation of stress corrosion cracking: stress corrosion cracking-material performance and evaluation. ASM, USA, p 394
5. Bobby Kannan M, Raja VS, Mukhopadhyay AK (2004) Scripta Materialia 51:107510.1016/j.scriptamat.2004.08.002 ↗
6. Hardwick DA, Thompson AW, Bernstein IM (1983) Metall Trans 14A:251710.1007/BF02668893 ↗
7. Albrecht J, Thompson AW, Bernstein IM (1979) Metall Trans 10A:175910.1007/BF02811712 ↗
8. Nguyen D, Thompson AW, Bernstein IM (1987) Acta Metall 35:241710.1016/0001-6160(87)90139-8 ↗
9. Klimowicz TF, Latanision RM (1978) Metall Trans 9A:59710.1007/BF02646418 ↗
10. Nguyen TH, Brown BF, Foley RT (1982) Corrosion 38:31910.5006/1.3621692 ↗
11. Haas M (2002) Grain boundary phenomena and failure of aluminium alloys, Ph.D. thesis, University of Groningen, Netherlands. University Press, Groningen, p 96
12. Ohnishi T, Higashi K (1984) J Jpn Inst Light Met 34:1850
13. Mukhopadhyay AK, Reddy GM, Prasad KS, Kamat SV, Dutta A, Mondal C (2001) In: Tiryakioglu M (ed) J.T. Staley Honorary Symposium on Al Alloys. ASM Materials Solution Conference and Exposition, Indianapolis, USA, p 63
14. Ramgopal T, Gouma PI, Frankel GS (2002) Corrosion 58:68710.5006/1.3287699 ↗
15. Albrecht J, Thompson AW, Bernstein IM (1982) Metall Trans 13A:81110.1007/BF02642394 ↗
16. Talianker M, Cina B (1989) Metall Trans 20A:208710.1007/BF02650294 ↗