TEM and EBSD investigation of continuous and discontinuous precipitation of CrN in nitrided pure Fe-Cr alloys
Source abstract
Abstract
Pure Fe-Cr alloys (1 and 3 wt% Cr) were gas nitrided (NH3, N2, N2O mixture at 823 K). Two modes of CrN precipitation: continuous (fine disc-shaped precipitates) and discontinuous (lamellae-like precipitates) were identified and investigated using transmission electron microscopy (TEM) and scanning electron microscopy (SEM). Both types of precipitates presented a cubic NaCl-type structure and Baker-Nutting orientation relationship with respect to the ferritic matrix. A quantification procedure based on TEM images exploitation revealed that the size and the number of the fine precipitates vary inversely with nitriding depth. This result was compared to the profile of micro-hardness. SEM observations showed that only superficial regions in the Fe-3 wt% Cr were transformed by the discontinuous precipitation of CrN. Electron back-scattered diffraction (EBSD) studies of lamella revealed singular initiation and growth features. A qualitative mechanism of lamella initiation and growth is discussed.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Metal and Thin Film Mechanics · Diamond and Carbon-based Materials Research · Semiconductor materials and devices
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (20)
Show source-provided references
1. H. Elghazal, G. Lormand, A. Hamel, D. Girodin and A. Vincent, Mater. Sci. Eng. A 303 (2001) 110.10.1016/S0921-5093(00)01852-9 ↗
2. C. Jacq, G. Lormand, D. NÉlias, D. Girodin and A. Vincent, ibid. 342 (2003) 311.10.1016/S0921-5093(02)00309-X ↗
3. L. Barralier, PhD thesis, ENSAM de Aix en Provence, 1992.
4. D. H. Jack and K. H. Jack, Mater. Sci. Eng. 1 (1973) 1.10.1016/0025-5416(73)90055-4 ↗
5. B. Mortimer, P. Grieveson and K. H. Jack, Scan. J. Metall. 1 (1972) 203.
6. H. C. F. Hekker, P. M. Rozendaal and E. J. Mittemeijer, J. Mater. Sci. 20 (1985) 718.10.1007/BF01026547 ↗
7. P. C. Van Wiggen, H. C. F. Rozendaal and E. J. Mittemeijer, ibid. 20 (1985) 4561.10.1007/BF00559347 ↗
8. D. B. Williams and E. P. Butler, Inter. Met. Rev. 3 (1983) 153.
9. M. Kikuchi, M. Kajihara and S. Choi, Mater. Sci. Eng. A 146 (1991) 131.10.1016/0921-5093(91)90273-P ↗
10. N. C. Santhi Srinvas and V. V. Kutumbarao, Scripta Mater. 37 (1997) 285.10.1016/S1359-6462(97)00112-7 ↗
11. Y. Ustinovshikov, A. Ruts, O. Bannykh and V. Blinov, Acta. Mater. 44 (1995) 1119.10.1016/1359-6454(95)00232-4 ↗
12. Y. Ustinovshikov, A. Ruts, O. Bannykh, V. Blinov and M. Kostina, Mater. Sci. Eng. A 262 (1999) 82.10.1016/S0921-5093(98)01015-6 ↗
13. F. Vanderschaeve, R. Taillard and J. J. Foct, Mater. Sci. 30 (1995) 6035.10.1007/BF01151525 ↗
14. M. Sennour, PhD thesis, INSA de Lyon (2002) p. 156.
15. B. J. Lightfoot and D.H. Jack, in Proceedings of the Conference on Heat Treatment, 1973 (The Metals Society, London, 1975) p. 59.
16. K. N. Tu and D. Turnbull, Acta. Metall. 15 (1967) 369.10.1016/0001-6160(67)90214-3 ↗
17. D. Turnbull and H. N. Treaftis, Trans AIME. 212 (1958) 33.
18. S. K. Budurov, G. Russev, A. Zlatev and R. Petrov, Z. Metallkde. 70 (1973) 372.
19. D. B. Williams and E. P. Butler, Int. Met. Rev. 3 (1981) 153.
20. G. Hinojosa, J. Oseguera and P. S. Schabes-Retchkiman, Thin Solid Films 349 (1999) 171.10.1016/S0040-6090(99)00196-0 ↗