Particle size-dependent electrical properties of nanocrystalline NiO
Source abstract
Abstract
Nickel oxide nanoparticles are formed by chemical precipitation and subsequent drying and calcinations at temperatures ≥523 K. Samples are characterized using X-ray diffraction and BET surface area measurements indicating the formation of a single NiO phase whose crystallite size increases with increasing calcination temperature. The electrical properties are examined by measuring DC and AC conductivities and dielectric properties as functions of temperature. Electrical conductivities first slightly increases with increasing particle size up to 7–10 nm and are about 8 orders of magnitude higher than that of NiO single crystals. Further increasing the particle size above 10 nm, leads to a monotonic decrease of conductivity. The data are discussed in view of variations of grain boundary as well as triple junction volume fractions as the particle size varies. At temperatures above θD/2 (θD is the Debye temperature), the conductivity is ascribed to a band-like conduction due to the large polaron. The activation energy of conduction was found to be minimal for the highly conducting samples of 7–10 nm, and gradually increases to ~0.5 eV with increasing the particle size above 10 nm. For T < θD/2, the conductivity is best described by variable–range–hopping models. Model parameters are thus estimated and presented as functions of particle size. Frequency as well as temperature dependencies of the AC conductivity and dielectric constant exhibit trends usually observed in carrier dominated dielectrics.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Transition Metal Oxide Nanomaterials · ZnO doping and properties · Multiferroics and related materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (47)
Show source-provided references
1. Gleiter H (1989) Prog Mater Sci 33:22310.1016/0079-6425(89)90001-7 ↗
2. Siegel RW (1990) MRS Bull 15:6010.1557/S0883769400058681 ↗
3. Siegel RW (1991) Annu Rev Mater Sci 21:55910.1146/annurev.ms.21.080191.003015 ↗
4. Siegel RW (1991) In: Chan RW (ed) Materials science and technology, vol 15. Processing of metals and alloys. VCH, Wienheim
5. Gleiter H (1992) Nanostruct Mater 1:110.1016/0965-9773(92)90045-Y ↗
6. Siegel RW (1994) In: Fujita FE (ed) Physics of new materials. Springer, Berlin
7. Hotovy I, Buc D, Hascik S, Nennewitz O (1998) Vacuum 50:4110.1016/S0042-207X(98)00011-6 ↗
8. Hotovy I, Huran J, Spiess L, Liday J, Sitter H, Hascik S (2003) Vacuum 69:23710.1016/S0042-207X(02)00338-X ↗
9. Fujii E, Tomozawa A, Torii H, Takayama R (1996) Jpn J Appl Phys 35:L32810.1143/JJAP.35.L328 ↗
10. Estrada W, Andersson A, Granqvist C (1998) J Appl Phys 64:367810.1063/1.341410 ↗
11. Azens A, Kullman L, Vaivars G, Nordborg H, Granqvist C (1998) Solid State Ion 113:44910.1016/S0167-2738(98)00309-9 ↗
12. Lee JW, Park IH, Chung CW (2005) Integr Ferroelectr 74:7110.1080/10584580500413921 ↗
13. Makhlouf SA (2008) Thin Solid Films 516:311210.1016/j.tsf.2007.07.213 ↗
14. Patil PS, Kadam LD (2002) Appl Surf Sci 199:21110.1016/S0169-4332(02)00839-5 ↗
15. Boscloo G, Hagfeldt A (2001) J Phys Chem B 105:303910.1021/jp003499s ↗
16. Biju V, Abdul Khadar M (2001) Mater Res Bull 36:2110.1016/S0025-5408(01)00488-3 ↗
17. Biju V, Abdul Khadar M (2003) J Mater Sci 38:4055. doi: https://doi.org/10.1023/A:102613110389810.1023/A:1026131103898 ↗
18. Morin FJ (1954) Phys Rev B 93:119910.1103/PhysRev.93.1199 ↗
19. Adler D, Feinleib J (1970) Phys Rev B 2:311210.1103/PhysRevB.2.3112 ↗
20. Bosman AJ, Vandaal HJ (1970) Adv Phys 19:110.1080/00018737000101071 ↗
21. Pushparajah P, Radhakrishna S (1997) J Mater Sci 32:3001. doi: https://doi.org/10.1023/A:101865742456610.1023/A:1018657424566 ↗
22. Bosman AJ, Crevecoeur C (1965) Phys Rev 144:76310.1103/PhysRev.144.763 ↗
23. Van Houten S (1960) J Phys Chem Solids 17:710.1016/0022-3697(60)90169-4 ↗
24. Heikes RR, Johnston WD (1957) J Chem Phys 26:58210.1063/1.1743350 ↗
25. Lunkenheimer P, Loidl A, Ottermann CR, Bange K (1991) Phys Rev B 44:592710.1103/PhysRevB.44.5927 ↗
26. Li L, Chen L, Qihe R, Li G (2006) Appl Phys Lett 89:13410210.1063/1.2357562 ↗
27. Richardson JT, Yiagas DI, Turk B, Forster K (1991) J Appl Phys 70:697710.1063/1.349826 ↗
28. Makhlouf SA, Parker FT, Spada FE, Berkowitz AE (1997) J Appl Phys 81:556110.1063/1.364661 ↗
29. Kotov YA, Bagazeyev AV, Beketov IV, Murzakaev AM, Samatov OM, Medvedev AI, Moskalenko NI, Timoshenkova OR, Demina TM, Shtolts AK (2005) Tech Phys 50:1279. Translated from Zhurnal TekhnicheskoĭFiziki (2005) 75:29
30. Powder Diffraction File JCPDS-International Centre for Diffraction Data (1999) ICDD Card No. 47-1049
31. Williamson GK, Hall WH (1953) Acta Metall 1:2210.1016/0001-6160(53)90006-6 ↗
32. Holland TJB, Redfern SAT (1997) Miner Mag 61:6510.1180/minmag.1997.061.404.07 ↗
33. Nunes AC, Yang L (1998) Surf Sci 399:22510.1016/S0039-6028(97)00821-2 ↗
34. Wittenauer MA, Van Zandt LL (1982) Philos Mag B 46:65910.1080/01418638208223551 ↗
35. Suryanarayan C (1994) Bull Mater Sci 17:30710.1007/BF02745220 ↗
36. Bollman W (1984) Philos Mag A 49:7310.1080/01418618408233430 ↗
37. Meilikhov EZ, Farzetdinova RM (1998) Physica E 3:19010.1016/S1386-9477(98)00235-5 ↗
38. Palumbo G, Thorpe SJ, Aust KT (1990) Scr Metall Mater 24:134710.1016/0956-716X(90)90354-J ↗
39. Snowden DP, Saltzburg H (1965) Phys Rev Lett 14:49710.1103/PhysRevLett.14.497 ↗
40. Osburn CM, Vest RW (1971) J Phys Chem Solids 32:135510.1016/S0022-3697(71)80193-2 ↗
41. Mott NF (1968) J Non-Cryst Solids 1:110.1016/0022-3093(68)90002-1 ↗
42. Mott NF (1969) Philo Mag 19:83510.1080/14786436908216338 ↗
43. Greaves GN (1973) J Non-Cryst Solids 11:42710.1016/0022-3093(73)90089-6 ↗
44. Elliot SR (1984) Physics of amorphous materials. Longman, London and New York
45. El-Desoky MM (2003) J Mater Sci Mater Electron 14:21510.1023/A:1022981929472 ↗
46. Austin I, Mott NF (1969) Adv Phys 18:4110.1080/00018736900101267 ↗
47. Jonscher AK, Reau JM (1978) J Mater Sci 13:563. doi: https://doi.org/10.1007/BF0054180610.1007/BF00541806 ↗