Laser powder bed fusion of Al–10 wt% Ce alloys: microstructure and tensile property
Source abstract
Abstract
The increasing potential for additive manufacturing technology continuously drives the need for printable materials, including novel aluminum alloys. Ce is considered an economically feasible addition that is beneficial to corrosion resistance and high temperature performance of aluminum alloys. In this study, a binary Al–10Ce alloy was additively manufactured by laser powder bed fusion (LPBF) using gas-atomized powders for the first time. Initial investigation was carried out to determine the optimal LPBF parameters for the Al–10Ce alloy, which was found using the laser power of 350 W and scan speed of 1400 mm/s. Alloy samples with nearly full density and outstanding printability were obtained. Room temperature tensile tests of the as-built Al–10Ce alloy yielded 222 ± 2 MPa in yield strength, 319 ± 1 MPa in tensile strength and 10.8 ± 0.1% in elongation. This is superior to the cast counterpart reported in the literature. A uniform microstructure was observed throughout the alloy, and it primarily consisted of extremely fine-scale eutectic Al and Al11Ce3 intermetallic ribbons, arranged in a skeleton pattern. This fine microstructure would have originated from the rapid cooling inherent to the LPBF process, and strongly suggests the presence of the Orowan strengthening mechanism. This study demonstrated that the binary Al–10Ce alloy is a promising base composition with good printability that brings new possibilities for future ternary and higher-order alloy design for LPBF.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Additive Manufacturing Materials and Processes · Additive Manufacturing and 3D Printing Technologies · High Entropy Alloys Studies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (49)
Show source-provided references
1. Thijs L, Verhaeghe F, Craeghs T, Van Humbeeck J, Kruth J-P (2010) A study of the microstructural evolution during selective laser melting of Ti–6Al–4V. Acta Mater 58(9):3303–331210.1016/j.actamat.2010.02.004 ↗
2. Xu W, Brandt M, Sun S, Elambasseril J, Liu Q, Latham K, Xia K, Qian M (2015) Additive manufacturing of strong and ductile Ti–6Al–4V by selective laser melting via in situ martensite decomposition. Acta Mater 85:74–8410.1016/j.actamat.2014.11.028 ↗
3. Zhou L, Mehta A, McWilliams B, Cho K, Sohn Y (2019) Microstructure, precipitates and mechanical properties of powder bed fused Inconel 718 before and after heat treatment. J Mater Sci Technol 35(6):1153–116410.1016/j.jmst.2018.12.006 ↗
4. Zhang F, Levine LE, Allen AJ, Stoudt MR, Lindwall G, Lass EA, Williams ME, Idell Y, Campbell CE (2018) Effect of heat treatment on the microstructural evolution of a nickel-based superalloy additive-manufactured by laser powder bed fusion. Acta Mater 152:200–21410.1016/j.actamat.2018.03.017 ↗
5. Amato K, Gaytan S, Murr L, Martinez E, Shindo P, Hernandez J, Collins S, Medina F (2012) Microstructures and mechanical behavior of Inconel 718 fabricated by selective laser melting. Acta Mater 60(5):2229–223910.1016/j.actamat.2011.12.032 ↗
6. Sun Z, Tan X, Tor SB, Yeong WY (2016) Selective laser melting of stainless steel 316L with low porosity and high build rates. Mater Des 104:197–20410.1016/j.matdes.2016.05.035 ↗
7. Kudzal A, McWilliams B, Hofmeister C, Kellogg F, Yu J, Taggart-Scarff J, Liang J (2017) Effect of scan pattern on the microstructure and mechanical properties of powder bed fusion additive manufactured 17-4 stainless steel. Mater Des 133:205–21510.1016/j.matdes.2017.07.047 ↗
8. Thijs L, Kempen K, Kruth J-P, Van Humbeeck J (2013) Fine-structured aluminium products with controllable texture by selective laser melting of pre-alloyed AlSi10Mg powder. Acta Mater 61(5):1809–181910.1016/j.actamat.2012.11.052 ↗
9. Zhou L, Mehta A, Schulz E, McWilliams B, Cho K, Sohn Y (2018) Microstructure, precipitates and hardness of selectively laser melted AlSi10Mg alloy before and after heat treatment. Mater Charact 143:5–1710.1016/j.matchar.2018.04.022 ↗
10. Martin JH, Yahata BD, Hundley JM, Mayer JA, Schaedler TA, Pollock TM (2017) 3D printing of high-strength aluminium alloys. Nature 549(7672):365–36910.1038/nature23894 ↗
11. Fulcher BA, Leigh DK, Watt TJ (2014) Comparison of AlSi10Mg and Al 6061 processed through DMLS. In: Proceedings of solid freeform fabrication (SFF) symposium
12. Zhou L, Hyer H, Park S, Pan H, Bai Y, Rice KP, Sohn Y (2019) Microstructure and mechanical properties of Zr-modified aluminum alloy 5083 manufactured by laser powder bed fusion. Addit Manuf 28:485–496
13. Zhou L, Pan H, Hyer H, Park S, Bai Y, McWilliams B, Cho K, Sohn Y (2019) Microstructure and tensile property of a novel AlZnMgScZr alloy additively manufactured by gas atomization and laser powder bed fusion. Scr Mater 158:24–2810.1016/j.scriptamat.2018.08.025 ↗
14. Zhou L, Hyer H, Thapliyal S, Mishra RS, McWilliams B, Cho K, Sohn Y (2020) Process-dependent composition, microstructure, and printability of Al–Zn–Mg and Al–Zn–Mg–Sc–Zr alloys manufactured by laser powder bed fusion. Metall Mater Trans A 51(6):3215–322710.1007/s11661-020-05768-3 ↗
15. Croteau JR, Griffiths S, Rossell MD, Leinenbach C, Kenel C, Jansen V, Seidman DN, Dunand DC, Vo NQ (2018) Microstructure and mechanical properties of Al–Mg–Zr alloys processed by selective laser melting. Acta Mater 153:35–4410.1016/j.actamat.2018.04.053 ↗
16. Jia Q, Rometsch P, Kürnsteiner P, Chao Q, Huang A, Weyland M, Bourgeois L, Wu X (2019) Selective laser melting of a high strength AlMnSc alloy: alloy design and strengthening mechanisms. Acta Mater 171:108–11810.1016/j.actamat.2019.04.014 ↗
17. Spierings A, Dawson K, Uggowitzer P, Wegener K (2018) Influence of SLM scan-speed on microstructure, precipitation of Al3Sc particles and mechanical properties in Sc-and Zr-modified Al–Mg alloys. Mater Des 140:134–14310.1016/j.matdes.2017.11.053 ↗
18. Thapliyal S, Komarasamy M, Shukla S, Zhou L, Hyer H, Park S, Sohn Y, Mishra RS (2020) An integrated computational materials engineering-anchored closed-loop method for design of aluminum alloys for additive manufacturing. Materialia 9:10057410.1016/j.mtla.2019.100574 ↗
19. Plotkowski A, Rios O, Sridharan N, Sims Z, Unocic K, Ott R, Dehoff R, Babu S (2017) Evaluation of an Al–Ce alloy for laser additive manufacturing. Acta Mater 126:507–51910.1016/j.actamat.2016.12.065 ↗
20. Weiss D (2019) Improved high-temperature aluminum alloys containing cerium. J Mater Eng Perform 28(4):1903–190810.1007/s11665-019-3884-2 ↗
21. Liu Y, Michi RA, Dunand DC (2019) Cast near-eutectic Al–12.5 wt% Ce alloy with high coarsening and creep resistance. Mater Sci Eng A 767:13844010.1016/j.msea.2019.138440 ↗
22. Sun Y, Hung C, Hebert RJ, Fennessy C, Tulyani S, Aindow M (2019) Eutectic microstructures in dilute AlCe and AlCo alloys. Mater Charact 154:269–27610.1016/j.matchar.2019.06.010 ↗
23. Belov NA, Naumova EA, Eskin DG (1999) Casting alloys of the Al–Ce–Ni system: microstructural approach to alloy design. Mater Sci Eng A 271(1–2):134–14210.1016/S0921-5093(99)00343-3 ↗
24. Sims ZC, Weiss D, McCall S, McGuire MA, Ott RT, Geer T, Rios O, Turchi P (2016) Cerium-based, intermetallic-strengthened aluminum casting alloy: high-volume co-product development. JOM 68(7):1940–194710.1007/s11837-016-1943-9 ↗
25. Sims ZC, Rios OR, Weiss D, Turchi PE, Perron A, Lee JR, Li TT, Hammons JA, Bagge-Hansen M, Willey TM (2017) High performance aluminum–cerium alloys for high-temperature applications. Mater Horiz 4(6):1070–107810.1039/C7MH00391A ↗
26. Weiss D (2019) Developments in aluminum–scandium–ceramic and aluminum–scandium–cerium alloys, light metals. Springer, Berlin, pp 1439–1443
27. Murarka S, Agarwala R (1968) Diffusion of rare earth elements in aluminum. Bhabha Atomic Research Centre, Bombay
28. Knipling KE, Dunand DC, Seidman DN (2006) Criteria for developing castable, creep-resistant aluminum-based alloys—a review. Zeitschrift für Metallkunde 97(3):246–26510.3139/146.101249 ↗
29. Du Y, Chang Y, Huang B, Gong W, Jin Z, Xu H, Yuan Z, Liu Y, He Y, Xie F-Y (2003) Diffusion coefficients of some solutes in fcc and liquid Al: critical evaluation and correlation. Mater Sci Eng A 363(1–2):140–15110.1016/S0921-5093(03)00624-5 ↗
30. Voorhees PW (1992) Ostwald ripening of two-phase mixtures. Annu Rev Mater Sci 22(1):197–21510.1146/annurev.ms.22.080192.001213 ↗
31. Baldan A (2002) Review progress in Ostwald ripening theories and their applications to nickel-base superalloys part I: Ostwald ripening theories. J Mater Sci 37(11):2171–2202. https://doi.org/10.1023/A:101538891272910.1023/A:1015388912729 ↗
32. Czerwinski F (2020) Cerium in aluminum alloys. J Mater Sci 55:24–72. https://doi.org/10.1007/s10853-019-03892-z10.1007/s10853-019-03892-z ↗
33. Nguyen RT, Imholte DD, Rios OR, Weiss D, Sims Z, Stromme E, McCall SK (2019) Anticipating impacts of introducing aluminum–cerium alloys into the United States automotive market. Resour Conserv Recycl 144:340–34910.1016/j.resconrec.2019.02.009 ↗
34. Manca D, Churyumov AY, Pozdniakov A, Prosviryakov A, Ryabov D, Krokhin AY, Korolev V, Daubarayte D (2019) Microstructure and properties of novel heat resistant Al–Ce–Cu alloy for additive manufacturing. Metals Mater Int 25(3):633–64010.1007/s12540-018-00211-0 ↗
35. Buschow K, Van Vucht J (1967) Systematic arrangement of the binary rare-earth-aluminium systems. Philips Res Rep 22:233–245
36. Gill S, Kurz W (1995) Rapidly solidified Al–Cu alloys—II. Calculation of the microstructure selection map. Acta Metall Mater 43(1):139–151
37. Trivedi R, Magnin P, Kurz W (1987) Theory of eutectic growth under rapid solidification conditions. Acta Metall 35(4):971–98010.1016/0001-6160(87)90176-3 ↗
38. Mohammadpour P, Plotkowski A, Phillion AB (2020) Revisiting solidification microstructure selection maps in the frame of additive manufacturing. Addit Manuf 31:100936
39. Liu S, Zhu H, Peng G, Yin J, Zeng X (2018) Microstructure prediction of selective laser melting AlSi10Mg using finite element analysis. Mater Des 142:319–32810.1016/j.matdes.2018.01.022 ↗
40. Jackson K, Hunt J (1988) Lamellar and rod eutectic growth, dynamics of curved fronts. Elsevier, Amsterdam, pp 363–37610.1016/B978-0-08-092523-3.50040-X ↗
41. Waterloo G, Jones H (1996) Microstructure and thermal stability of melt-spun Al–Nd and Al–Ce alloy ribbons. J Mater Sci 31(9):2301–2310. https://doi.org/10.1007/BF0115293810.1007/BF01152938 ↗
42. Hadadzadeh A, Amirkhiz BS, Li J, Mohammadi M (2018) Columnar to equiaxed transition during direct metal laser sintering of AlSi10Mg alloy: effect of building direction. Addit Manuf 23:121–131
43. Seidman DN, Marquis EA, Dunand DC (2002) Precipitation strengthening at ambient and elevated temperatures of heat-treatable Al(Sc) alloys. Acta Mater 50(16):4021–403510.1016/S1359-6454(02)00201-X ↗
44. Myhr O, Grong Ø, Andersen S (2001) Modelling of the age hardening behaviour of Al–Mg–Si alloys. Acta Mater 49(1):65–7510.1016/S1359-6454(00)00301-3 ↗
45. Xia K, Wu X (2005) Back pressure equal channel angular consolidation of pure Al particles. Scr Mater 53(11):1225–122910.1016/j.scriptamat.2005.08.012 ↗
46. Ng DS, Dunand DC (2020) Aging-and creep-resistance of a cast hypoeutectic Al–6.9 Ce–9.3 Mg (wt%) alloy. Mater Sci Eng A 786:13939810.1016/j.msea.2020.139398 ↗
47. Mukherjee T, Zuback J, De A, DebRoy T (2016) Printability of alloys for additive manufacturing. Sci Rep 6(1):1–810.1038/s41598-016-0001-8 ↗
48. Kou S (2015) A criterion for cracking during solidification. Acta Mater 88:366–37410.1016/j.actamat.2015.01.034 ↗
49. Hyer H, Zhou L, Benson G, McWilliams B, Cho K, Sohn Y (2020) Additive manufacturing of dense WE43 Mg alloy by laser powder bed fusion. Addit Manuf 33:101123