Fatigue and fracture characteristic of hypoeutectoid pearlitic R7T steel used in railway applications
Source abstract
Abstract
This study comprehensively investigates the mechanical properties, fatigue behavior, and fracture toughness of hypoeutectoid pearlitic R7T steel employed in railway wheel manufacturing. Utilizing a combination of rotating bending fatigue tests and compact tension (CT) specimens, the fatigue life, crack growth rate, and fracture toughness of the material were systematically evaluated. Experiments were conducted under cyclic loading conditions in both radial and tangential orientations to simulate in-service conditions. Microstructural examination using scanning electron microscopy (SEM) revealed the role of inclusions, dimpled rupture, and cleavage features in failure mechanisms. Hardness measurements across different wheel rim regions indicated minimal anisotropy. The findings provide critical insights into the structural performance and failure resistance of R7T steel under cyclic loading conditions, offering valuable implications for the design and maintenance of wheel steel.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Fatigue and fracture mechanics · Material Properties and Failure Mechanisms · Mechanical Failure Analysis and Simulation
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (41)
Show source-provided references
1. Simulation of railroad crack growth life under the influence of combination of mechanical contact and thermal loads
2. Simulation of crack propagation of fatigue in Iran rail road wheels and effect of residual stresses
3. Life estimation in the railway wheels under the influence of residual stress field
4. Masoudi Nejad · 2013
5. Reza · 2017
6. Rolling contact fatigue analysis of rails under the influence of residual stresses induced by manufacturing
7. Using three-dimensional finite element analysis for simulation of residual stresses in railway wheels10.1016/j.engfailanal.2014.07.018 ↗
8. Effects of residual stress and shape of web plate on the fatigue life of railway wheels10.1016/j.engfailanal.2009.04.013 ↗
9. Fatigue crack growth of a railway wheel steel and fatigue life prediction under spectrum loading conditions
10. Fatigue fracture and fatigue life assessment of railway wheel using non‐linear model for fatigue crack growth
11. Investigation on fatigue parameters in railway wheels using a critical plane model
12. Mechanical properties and fatigue behaviour of railway wheel steels as influenced by mechanical and thermal loadings10.1016/j.wear.2016.04.009 ↗
13. Multiaxial fatigue of a railway wheel steel under non-proportional loading10.1016/j.ijfatigue.2005.07.045 ↗
14. Fracture behaviour and cleavage initiation in hypoeutectoid pearlitic steel10.1007/s10704-007-9173-3 ↗
15. Experimental investigation on the fatigue and fracture toughness properties of hypereutectoid rail steel10.1016/j.engfracmech.2024.110657 ↗
16. Prediction of fatigue crack propagation and fractography of rail steel10.1016/j.tafmec.2019.03.016 ↗
17. Fatigue crack growth and microstructural analysis of rail steel specimens under periodic overloads
18. Effect of periodic overloads and spectrum loading on fatigue life and microstructure in a grade 900A rail steel
19. Effect of chemical composition and microstructure on the fatigue crack growth resistance of pearlitic steels for railroad application10.1016/j.ijfatigue.2018.10.016 ↗
20. Fatigue and fracture behavior of pearlitic grade 900a steel used in railway applications10.1016/j.tafmec.2015.12.017 ↗
21. Analysis of fatigue crack growth under mixed-mode loading conditions for a pearlitic grade 900A steel used in railway applications
22. Tread evolution of bainitic heavy-haul freight wheels due to progressive heat accumulations from cyclic drag braking10.1016/j.engfailanal.2025.109344 ↗
23. Research on the damage mechanism of the rolling contact fatigue of a wheel–rail contact system under the influences of surface defects10.1016/j.engfailanal.2024.108631 ↗
24. Investigations of fatigue crack propagation in ER8 railway wheel steel with varying microstructures10.1016/j.msea.2022.142980 ↗
25. Microstructure evolution of railway pearlitic wheel steels under rolling-sliding contact loading10.1016/j.triboint.2020.106685 ↗
26. The influence of microstructure on the rolling contact fatigue of steel for high-speed-train wheel10.1016/j.wear.2015.10.002 ↗
27. Fatigue crack growth of a railway wheel10.1016/j.engfailanal.2017.07.036 ↗
28. Corrosion induced fatigue failure of railway wheels10.1016/j.engfailanal.2015.06.009 ↗
29. Multiaxial fatigue reliability analysis of railroad wheels10.1016/j.ress.2006.12.021 ↗
30. The competitive role of wear and RCF: full scale experimental assessment of artificial and natural defects in railway wheel treads10.1016/j.wear.2016.06.020 ↗
31. Modeling the competitive relationship between wear and rolling contact fatigue of railway wheel steel
32. Cyclic deformation behaviour of railway wheel steels in the very high cycle fatigue (VHCF) regime10.1016/j.ijfatigue.2010.07.010 ↗
33. Tension-shear multiaxial fatigue damage behavior of high-speed railway wheel rim steel10.1016/j.ijfatigue.2019.105416 ↗
34. Microstructural analysis and fatigue fracture behavior of rail steel10.1080/15376494.2018.1472339 ↗
35. Fatigue crack growth analysis in CTS specimens made of railway wheel steel under mixed-mode loading conditions
36. 2016
37. 2015
38. Prediction of the S–N curves of high-strength steels in the very high cycle fatigue regime10.1016/j.ijfatigue.2010.02.006 ↗
39. 2002
40. Review of fracture toughness (G, K, J, CTOD, CTOA) testing and standardization10.1016/j.engfracmech.2012.02.001 ↗
41. 2024