Interplay Between Strain and Thickness on the Effective Carrier Lifetime of Buffer-Mediated Epitaxial Germanium Probed by the Photoconductance Decay Technique

We report contactless effective minority carrier lifetime of epitaxially grown unstrained and in-plane <110> biaxially tensile-strained (001) germanium (ε-Ge) epilayers measured using microwave-reflectance photoconductance decay measurements. Strained Ge epilayers were grown using In x Ga 1– x As linearly graded buffers on (001) GaAs substrates. Using homogeneous excitation of unstrained Ge epilayers, thickness-dependent separation of minority carrier lifetime components under low injection conditions yielded a bulk lifetime of 114 ± 2 ns and low surface recombination velocity of 21.3 ± 0.04 cm/s. More notably, an effective minority carrier lifetime of >100 ns obtained from sub-50 nm 1.6% tensile-strained Ge epilayers showed no degradation relative to the unstrained counterpart. Detailed material characterization using X-ray diffractometry revealed successful strain transfer of 0.61 and 0.89% to the Ge epilayers via In x Ga 1– x As metamorphic buffers and confirms pseudomorphic growth. Lattice coherence observed at the ε-Ge epilayer and In x Ga 1– x As buffer heterointerfaces via transmission electron microscopy substantiates the prime material quality achieved. The relatively high carrier lifetimes achieved are an indicator of excellent material quality and provide a path forward to realize low-threshold Ge laser sources.