Strain localization–driven deformation and damage evolution during low-cycle fatigue of flux-cored arc welded 460 MPa-class H-section steel
Source abstract
Abstract
In this study, the microstructural characteristics and low-cycle fatigue (LCF) behavior of a 460 MPa-grade offshore H-section steel and its flux-cored arc welded (FCAW) joint were systematically investigated. The base metal consisted of a ferrite–pearlite microstructure with fine Nb–Ti–V MC-type precipitates, whereas the welded joint exhibited acicular ferrite–dominated weld metal and bainitic transformation products across the heat-affected zone. Hardness and tensile testing confirmed a typical overmatching condition, and all tensile and fatigue fractures occurred within the base metal, indicating sound weld integrity. Under strain-controlled LCF loading, the as-rolled steel showed typical cyclic softening followed by a clear saturation stage. In contrast, the welded joint exhibited continuous cyclic softening without saturation, accompanied by a slight reduction in fatigue life. Kernel average misorientation (KAM) analysis revealed relatively homogeneous strain distribution in the as-rolled steel, whereas the welded joint exhibited pronounced strain localization within the BM. This localization appeared as inclined deformation bands aligned with high-Schmid-factor slip systems, as confirmed by EBSD-based crystallographic analysis. Transmission electron microscope (TEM) observations further demonstrated that the welded joint developed planar slip-band structures with dislocation pile-up, exhibiting superficial resemblance to early-stage persistent slip band (PSB) formation. These PSB-like features serve as preferential sites for crack initiation and account for the absence of a saturation stage and the reduced fatigue life in the welded joint. Overall, this study provides mechanistic insight into strain partitioning, crystallographically governed deformation localization in the adjacent base metal, and fatigue damage evolution in FCAW joint of H-section steel under room-temperature LCF conditions.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Microstructure and Mechanical Properties of Steels · Fatigue and fracture mechanics · Welding Techniques and Residual Stresses
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (59)
Show source-provided references
1. Oil and gas operations under extreme conditions in the cold north
2. Levelised cost of energy, A challenge for offshore wind10.1016/j.renene.2020.06.030 ↗
3. Billingham · 2003
4. Production of high-strength and high-toughness steel for offshore structures
5. Microstructure and mechanical properties in hot-rolled extra high-yield-strength steel plates for offshore structure and shipbuilding10.1007/s11661-010-0458-1 ↗
6. Investigation on tempering of granular bainite in an offshore platform steel10.1016/j.msea.2014.12.074 ↗
7. Microstructure and impact toughness of offshore steel
8. Low-temperature toughness properties of 500 MPa offshore steels and their simulated coarse-grained heat-affected zones10.1016/j.msea.2019.138719 ↗
9. Effect of microstructural heterogeneities on variability in low-temperature impact toughness in multi-pass weld metal of 420 MPa offshore engineering steel10.1007/s40194-023-01521-7 ↗
10. Cryogenic fracture toughness of 9Ni steel enhanced through grain refinement10.1007/BF02659812 ↗
11. Microstructural characteristics and impact toughness in YS690MPa steel weld metal for offshore structures10.1080/13621718.2016.1204774 ↗
12. New generation structural steel plate metallurgy for meeting offshore and arctic application challenges
13. Hardening mechanisms and impact toughening of a high-strength steel containing low Ni and Cu additions10.1016/j.actamat.2019.04.041 ↗
14. The effects of prior austenite grain refinement on strength and toughness of high-strength low-alloy steel10.3390/met12010028 ↗
15. Strengthening-toughening mechanism of cost-saving marine steel plate with 1000 MPa yield strength10.1016/j.msea.2021.142280 ↗
16. The effect of nickel on the microstructure, mechanical properties and corrosion properties of niobium–vanadium microalloyed powder metallurgy steels10.3390/ma13184021 ↗
17. Nickel alloying in carbon steel: fundamentals and applications10.3390/alloys2010001 ↗
18. Precipitation of MC phase and precipitation strengthening in hot rolled Nb–Mo and Nb–Ti steels10.1007/s10853-007-2000-4 ↗
19. Evaluating strengthening and impact toughness mechanisms for ferritic and bainitic microstructures in Nb, Nb-Mo and Ti-Mo microalloyed steels10.3390/met7020065 ↗
20. Microstructure characteristics and impact fracture mechanisms of Nb and V–Ti micro-alloyed offshore platform steels10.1016/j.vacuum.2021.110709 ↗
21. On the strengthening effects affecting tensile and low cycle fatigue properties of low-alloyed seismic/fire-resistant structural steels10.1007/s12540-020-00870-y ↗
22. Mutual strengthening by fine MX precipitation and solute segregation on dislocations during complex low-cycle fatigue to simulate the seismic/fire situation in bainitic H-section steel10.1016/j.ijfatigue.2025.109112 ↗
23. Materials problems in offshore platforms
24. Gupta · 1986
25. Steel plates and fatigue solution for offshore wind turbines in the fukushima floating offshore wind farm demonstration project
26. Review of corrosion fatigue in offshore structures: present status and challenges in the offshore wind sector10.1016/j.rser.2016.02.017 ↗
27. Development of fatigue design standards for marine structures10.1115/1.4041993 ↗
28. Review of fatigue assessment approaches for welded marine joints and structures10.3390/met12061010 ↗
29. Improving the fatigue life of large offshore foundations10.1016/j.marstruc.2022.103314 ↗
30. Fatigue crack initiation and propagation in a low-carbon steel of two different grain size10.1111/j.1460-2695.1992.tb00055.x ↗
31. Effect of grain size on low cycle fatigue in low carbon steel10.1299/jsme1958.24.1692 ↗
32. Fatigue crack propagation behaviour in ultra-fine grained low carbon steel10.1016/j.ijfatigue.2004.07.004 ↗
33. Effect of grain size on the threshold stress intensity factor in fatigue of a ferritic steel10.1016/0036-9748(76)90142-3 ↗
34. The effects of stress ratio and grain size on near-threshold fatigue crack propagation in low-carbon steel10.1016/0013-7944(81)90062-X ↗
35. Theoretical modelling of the effects of grain size on the threshold for fatigue crack growth10.1016/0956-7151(91)90222-M ↗
36. Influence of carbide and inclusion contents on the fatigue properties of high speed steels and tool steels10.1016/S0142-1123(00)00087-6 ↗
37. Influence of phase coarsening on fatigue crack growth in precipitate strengthened alloys10.1016/j.engfracmech.2018.11.029 ↗
38. Steel selection for offshore structures10.2118/4332-PA ↗
39. Microstructure and local brittle zone phenomena in high-strength low-alloy steel welds10.1007/BF03350956 ↗
40. Microstructures relevant to brittle fracture initiation at the heat-affected zone of weldment of a low carbon steel10.1007/BF02652351 ↗
41. Corrosion fatigue crack propagation in a heat affected zone of high-performance steel in an underwater sea environment10.1016/j.engfailanal.2010.08.019 ↗
42. Comparative study on corrosion fatigue behaviour of high strength low alloy steel and simulated HAZ microstructures in a simulated marine atmosphere10.1016/j.ijfatigue.2020.105666 ↗
43. Effect of alloying elements addition on coarsening behavior of pearlitic cementite particles after severe cold rolling and annealing10.1016/j.msea.2007.12.005 ↗
44. Effect of inclusion size on the nucleation of acicular ferrite in welds10.2355/isijinternational.40.1260 ↗
45. Effect of austenite grain size on transformation behavior, microstructure and mechanical properties of 0.1C–5Mn martensitic steel10.2355/isijinternational.53.2218 ↗
46. Effect of austenite grain size and accelerated cooling start temperature on the transformation behaviors of multi-phase steel10.1007/s11431-012-4980-9 ↗
47. Effect of prior austenite grain size on the morphology of nano-bainitic steels10.1007/s11661-018-4492-8 ↗
48. Low energy dislocation structures produced by cyclic deformation10.1016/0025-5416(86)90281-8 ↗
49. Quasi in-situ observations of microstructure evolution during low cycle fatigue in carbide-free bainitic steel10.1016/j.ijfatigue.2022.107464 ↗
50. A comparative study on the mechanical behavior of S355J2 steel repair-welded joints10.1016/j.jcsr.2023.107878 ↗
51. The resistance of metals to cyclic deformation
52. Suresh · 1998
53. Dieter · 1961
54. In situ SEM study of tensile deformation of a near-β titanium alloy10.1016/j.msea.2017.10.028 ↗
55. Microstructure and cyclic deformation behaviour of plain carbon and low-alloyed steels10.1016/0142-1123(90)90092-S ↗
56. Influence of microstructure on low-cycle and extremely-low-cycle fatigue resistance of low-carbon steels10.1007/s12540-020-00819-1 ↗
57. Role of persistent slip bands and persistent slip markings in fatigue crack initiation in polycrystals10.3390/cryst13020220 ↗
58. Fatigue in metals and alloys
59. The heterogeneity of persistent slip band nucleation and evolution in metals at the micrometer scale10.1126/science.abb2690 ↗