The effect of varying powder feedstock chemistry and printing atmosphere on the microstructure of additively manufactured nickel-based ODS alloys: Role on stabilization of cellular structures vs. oxide dispersion formation

Nickel-based alloys have a wide variety of structural applications due to their high corrosion resistance and mechanical strength which depend on solid solution strengthening, or the formation of oxides and/or intermetallic precipitation for their properties. In this study, the microstructure of six Ni–Cr–Y–Ti–Al powder batches designed for the production of oxide dispersion strengthened nickel were compared. These batches varied in chemistry and atomization technique used which included Gas Atomization Reactive Synthesis (GARS). The batches of powder were then consolidated via Additive Manufacturing (AM) Powder Bed Fusion using Laser Beam (PBF-LB) and characterized via transmission electron microscopy to elucidate the influence of powder feedstock (i.e. synthesis methodology and chemistry) on the PBF-LB microstructure. The study investigates (i) how the amount of yttrium and titanium additions in the powder feedstock and the addition of oxygen during the processing (through GARS) affect the microstructure of the powder itself and the AM printed microstructure, and (ii) how the control of oxygen addition in the printing atmosphere during the PBF-LB printing process itself is another important parameter for achieving the formation of the wanted oxide dispersion versus the stabilization of the cellular structure (often observed in AM processed alloys). Microstructural characterization of both powder particles and additively manufactured nickel alloys in this study provide important insights into the movement of yttrium within the material upon solidification, particularly along cell boundaries, and how yttrium behaves depending on alloy chemistry. When a threshold of yttrium content is reached within the system, yttrium consistently reacts to form an intermetallic along cell boundaries instead of forming oxide nanoparticles.