Residual strain and microstructure evolution in 316L stainless steel fabricated by hybrid additive/subtractive manufacturing

The extreme thermal gradients in additive manufacturing (AM) result in residual strains. Subsequent machining operations can relieve the AM strains but can introduce additional strains. AM and machining on the same platform, also called interleaving, during hybrid manufacturing has been shown to improve productivity. However, the impacts of these operations on the resulting strains are not well understood. In this investigation, neutron diffraction was used to measure residual strains in hybrid manufactured 316L stainless steel where blown-powder laser directed energy deposition (DED), and machining operations were interleaved in 1-inch intervals. We observe that the dominant texture developed during AM, resulting from different spot sizes and deposition parameters, significantly affects residual strain evolution. A dominant <011> texture along the build direction does not show any strain localization during interleaved deposition and machining whereas a dominant <001> texture shows strong tensile strain localization consistent with the pauses for machining at the end of AM step. Using coolant during machining can further alter the residual strain evolution. Our work shows that a combination of AM parameters and machining strategy can be used to influence the nature and magnitude of residual strains in components fabricated using convergent manufacturing technologies.