Process characteristics of V-shaped coupling dual GTA-based additive manufacturing
Source abstract
Abstract
The deposition efficiency of gas tungsten arc (GTA) additive manufacturing is quite low despite its superior quality in comparison with other arc-based manufacturing processes. Therefore, V-shaped coupling dual GTA-based additive manufacturing (VCG-AM) process was proposed in this study to solve the problem. Thin-wall part with sound formation was acquired by VCG-AM, with the deposition efficiency reaching more than twice of conventional single GTA-based additive manufacturing (SG-AM) process. The microstructure of mainly polygonal ferrite and pearlite was obtained via both processes, and the grain size of VCG-AM was slightly larger than that of SG-AM, related with the higher heat input. The pearlite assembled near the grain boundary of the polygonal ferrite, and a larger volume fraction of pearlite formed in the VCG-AM sample due to the lower cooling rate. The average microhardness of the VCG-AM sample was a little lower than that of the SG-AM sample, while the impact absorbing energy and ultimate tensile strength was close. Both VCG-AM and SG-AM part demonstrates ductile fracture based on the tensile fracture analysis.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Additive Manufacturing Materials and Processes · Additive Manufacturing and 3D Printing Technologies · Welding Techniques and Residual Stresses
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (27)
Show source-provided references
1. Technology development for producing Inconel 625 in aerospace application using wire arc additive manufacturing process10.1007/s11665-021-05781-6 ↗
2. Location-dependent microstructure and properties for plasma arc additively manufactured duplex stainless steel ER2209 wire10.1007/s11665-021-06005-7 ↗
3. Multi-layer deposition mechanism in ultra high-frequency pulsed wire arc additive manufacturing (WAAM) of NiTi shape memory alloys
4. Influence of heat input on the evolution of δ-ferrite grain morphology of SS308L fabricated using WAAM-CMT10.1016/j.matchar.2022.112363 ↗
5. Influence of deposition strategy and heat treatment on mechanical properties and microstructure of 2319 aluminium WAAM components10.1016/j.matdes.2022.110974 ↗
6. Microstructural, mechanical and energy demand characterization of alternative WAAM techniques for Al-alloy parts production10.1016/j.cirpj.2020.08.001 ↗
7. Bending fatigue properties of structural steel fabricated through wire arc additive manufacturing (WAAM)
8. Microstructural characterisation of thick-walled wire arc additively manufactured stainless steel10.1016/j.jmatprotec.2021.117373 ↗
9. A multi-tier layer-wise thermal management study for long-scale wire-arc additive manufacturing10.1016/j.jmatprotec.2022.117651 ↗
10. Experimental investigations on mechanical properties of multi-layered structure fabricated by GMAW-based WAAM of SS316L10.1016/j.jmrt.2022.08.074 ↗
11. The forming profile model for cold metal transfer and plasma wire-arc deposition of nickel-based alloy10.1007/s11665-021-05485-x ↗
12. Mechanical properties and microstructural characteristics of wire arc additive manufactured 308L stainless steel cylindrical components made by gas metal arc and cold metal transfer arc welding processes
13. Investigating the generation process of molten droplets and arc plasma in the confined space during compulsively constricted WAAM10.1016/j.jmatprotec.2019.116355 ↗
14. A comparative study of GMAW-and DE-GMAW-based additive manufacturing techniques: thermal behavior of the deposition process for thin-walled parts10.1007/s00170-016-9898-0 ↗
15. Fabrication of iron-rich Fe–Al intermetallics using the wire-arc additive manufacturing process
16. Microstructure and mechanical properties of wire+arc additively manufactured Al-Mg-Si aluminum alloy10.1016/j.matlet.2018.09.048 ↗
17. The double-wire feed and plasma arc additive manufacturing process for deposition in Cr-Ni stainless steel10.1016/j.jmatprotec.2018.04.040 ↗
18. Effects of in-process LN2 cooling on the microstructure and mechanical properties of type 316L stainless steel produced by wire arc directed energy deposition10.1016/j.matlet.2020.128707 ↗
19. The effects of forced interpass cooling on the material properties of wire arc additively manufactured Ti6Al4V alloy10.1016/j.jmatprotec.2018.03.024 ↗
20. On microstructure and mechanical properties of a low-carbon low-alloy steel block fabricated by wire arc additive manufacturing10.1007/s11665-021-05568-9 ↗
21. Characterization of robotized CMT-WAAM carbon steel10.1016/j.jcsr.2022.107624 ↗
22. High deposition wire arc additive manufacturing of mild steel: strategies and heat input effect on microstructure and mechanical properties10.1016/j.jmapro.2020.08.060 ↗
23. Mechanical testing and microstructural analysis of wire arc additively manufactured steels10.1016/j.matdes.2022.110544 ↗
24. Microstructural evolution and mechanical properties of a low-carbon low-alloy steel produced by wire arc additive manufacturing10.1007/s00170-019-04393-8 ↗
25. Effect of solidification defects and HAZ softening on the anisotropic mechanical properties of a wire arc additive-manufactured low-carbon low-alloy steel part[J]
26. A comparative study of the microstructure and properties of 800 MPa microalloyed C-Mn steel welded joints by laser and gas metal arc welding10.1016/j.msea.2016.05.079 ↗
27. Effect of multi-walled structure on microstructure and mechanical properties of 1.25 Cr-1.0 Mo steel fabricated by GMAW-based WAAM using metal-cored wire10.1016/j.jmrt.2022.10.158 ↗